Production of polyamide powders by ester aminolysis
A method for producing a polycondensate powder dispersion, characterised in that it includes at least one step of polycondensation: i) of at least one diester and at least one diamine, and/or ii) at least one amino ester, while stirring, in a solvent that can solubilise both the diamine and the diester and/or the amino ester but not the polyamide that forms during the polycondensation, at a temperature between 30° C. and the boiling temperature of the solvent, in order to produce a powder precipitate dispersed in the solvent.
1. A process for producing a polycondensate powder dispersion, wherein the process comprises polycondensation:
i) of at least one diester and at least one diamine,
and/or
ii) of at least one amino ester,
with stirring, in a solvent that can dissolve both the diamine and the diester and/or the amino ester, but not a polyamide which forms during the polycondensation, at a temperature included in the range of from 50° C. to 120° C. such that a polycondensate powder precipitate dispersed in the solvent is obtained,
wherein the process further comprises a step of separation of the solvent and recovering a polycondensate powder, wherein the polycondensate powder comprises particles of free powder which have a spheroidal shape, a D50 measured according to ISO standard 13320-1:1999 included in the range of from 1 to 200 μm, and which comprise traces of ester chain ends,
wherein said at least one diester is of formula:
R 1 —(CH 2 ) m —R 2 , wherein m represents an integer ranging from 0 to 36, and R 1 and R 2 represent identical or different ester functions of general formula COOR 3 , wherein R 3 represents a saturated or unsaturated, linear or branched alkyl chain of from 1 to 5 carbon atoms and/or R 1 —(C 6 H 4 ) n —R 2 , wherein n represents an integer ranging from 1 to 2, and R 1 and R 2 represent identical or different ester functions of general formula COOR 3 , wherein R 3 represents a saturated or unsaturated, linear or branched alkyl chain of from 1 to 5 carbon atoms;
wherein said at least one diamine is chosen from aliphatic diamines having from 6 to 12 carbon atoms;
wherein said at least one amino ester corresponds to the general formula R 5 —(CH 2 ) p —R 6 , wherein p represents an integer ranging from 0 to 36, R 5 represents a primary or secondary amine function, and R 6 represents an ester function of general formula COOR 7 , wherein R 7 represents an alkyl chain of from 1 to 5 carbon atoms;
wherein the solvent is chosen from linear alkanes, cycloaliphatic alkanes, halogenated solvents and mixtures thereof.
2. The process as claimed in claim 1 , wherein said polycondensation is carried out in the presence of a polycondensation catalyst, the content of which is included in the range of from 0.01 mol % to 50 mol %, relative to the number of moles of all of the reagents, wherein the polycondensation catalyst is chosen from sodium hydride, potassium hydride, sodium, sodium stearate, ortho-phosphoric acid, stearic acid, ethanol, phenol, sodium methoxide, sodium ethoxide, and mixtures thereof.
3. The process as claimed in claim 1 , wherein the polycondensation comprises a simultaneous precipitation in the form of polycondensate powders.
4. The process as claimed in claim 1 , wherein the stirring is at a speed included in the range of from 1 to 2000 rpm.
5. The process as claimed in claim 1 , wherein the process comprises at least one step of polycondensation of at least one diester and at least one diamines.
6. The process as claimed in claim 1 , wherein the process comprises at least one step of polycondensation of at least one amino ester.
7. The process as claimed in claim 1 , wherein the particles of free powder comprise 10 to 4000 meq/kg of ester chain ends, relative to the weight of polycondensate.
8. The process as claimed in claim 1 , wherein the process comprises at least one step of polycondensation at a temperature in the range of 50° C. to 120° C.