Polyolefin microporous membrane, production method therefor, and battery separator
A polyolefin microporous membrane is disclosed. The membrane includes a polyolefin resin having an MFR value of not greater than 2.0 g/10 min, and a crystal nucleating agent. The polyolefin microporous membrane has an air permeation resistance scaled to a thickness of 20 μm of from 100 to 500 sec/100 cc, a porosity of from 20% to 60%, and a mean flow pore size of not greater than 100 nm.
1. A polyolefin microporous membrane, comprising:
a polyolefin resin having an MFR value of not greater than 2.0 g/10 min; and
a crystal nucleating agent,
wherein the polyolefin microporous membrane has an air permeation resistance scaled to a thickness of 20 μm of from 100 to 500 sec/100 cc, a porosity of from 20% to 60%, and a mean flow pore size of not greater than 100 nm,
wherein a half-crystallization period t 1/2 of the polyolefin microporous membrane is not greater than 2.0 minutes during an isothermal crystallization at 123° C.
2. The polyolefin microporous membrane according to claim 1 , wherein the polyolefin resin comprises not less than 90 mass % of a polyethylene resin.
3. The polyolefin microporous membrane according to claim 1 , wherein the mean flow pore size is not greater than 50 nm.
4. The polyolefin microporous membrane according to claim 1 , having a dielectric breakdown voltage of not less than 163 V/μm.
5. The polyolefin microporous membrane according to claim 1 , having a dielectric breakdown voltage of not less than 175 V/μm.
6. A battery separator, comprising:
a polyolefin microporous membrane, comprising:
a polyolefin resin having an MFR value of not greater than 2.0 g/10 min; and
a crystal nucleating agent,
wherein the polyolefin microporous membrane has an air permeation resistance scaled to a thickness of 20 μm of from 100 to 500 sec/100 cc, a porosity of from 20% to 60%, and a mean flow pore size of not greater than 100 nm,
wherein a half-crystallization period t 1/2 of the polyolefin microporous membrane is not greater than 2.0 minutes during an isothermal crystallization at 123° C.
7. A rechargeable battery, comprising:
a battery separator, comprising:
a polyolefin microporous membrane, comprising:
a polyolefin resin having an MFR value of not greater than 2.0 g/10 min; and
a crystal nucleating agent,
wherein the polyolefin microporous membrane has an air permeation resistance scaled to a thickness of 20 μm of from 100 to 500 sec/100 cc, a porosity of from 20% to 60%, and a mean flow pore size of not greater than 100 nm,
wherein a half-crystallization period t 1/2 of the polyolefin microporous membrane is not greater than 2.0 minutes during an isothermal crystallization at 123° C.
8. A method of producing a polyolefin microporous membrane, the polyolefin microporous membrane having an air permeation resistance scaled to 20 μm of from 100 to 500 sec/100 cc, a porosity of from 20% to 60%, and a mean flow pore size of not greater than 100 nm, the method comprising:
melt-kneading a polyolefin resin, a crystal nucleating agent, and a membrane formation solvent to form a polyolefin resin composition;
extruding and cooling the polyolefin resin composition to form a gel sheet;
performing a first stretching step of stretching the gel sheet;
removing the membrane formation solvent from the gel sheet after stretching; and
drying the gel sheet after removing the membrane formation solvent.
9. The method according to claim 8 , wherein the polyolefin resin has an MFR value of not greater than 2.0 g/10 min.