Process for producing multimodal polyethylene in-situ blends including ultra-high molecular weight fractions
The present application relates to a process for producing a multimodal polyethylene composition comprising the steps of polymerizing a polyethylene fraction (A-1) having a weight average molecular weight Mw of equal to or more than 500 kg/mol to equal to or less than 10,000 kg/mol and a density of equal to or more than 915 kg/m 3 to equal to or less than 960 kg/m 3 in one reaction step and polymerizing a polyethylene fraction (A-2) having a lower weight average molecular weight Mw as polyethylene fraction (A-1) and a density of equal to or more than 910 kg/m 3 to equal to or less than 975 kg/m 3 in a second reaction step of a sequential multistage process wherein one of said polyethylene fractions is polymerized in the presence of the other of said polyethylene fractions to form a first polyethylene resin (A) having a weight average molecular weight Mw of equal to or more than 150 kg/mol to equal to or less than 1,500 kg/mol, and a density of equal to or more than 910 kg/m 3 to equal to or less than 975 kg/m 3 , wherein the weight average molecular weight Mw of the first polyethylene resin (A) is lower than the weight average molecular weight Mw of the polyethylene fraction (A-1), blending the first polyethylene resin (A) with a second polyethylene resin (B) having a weight average molecular weight Mw of equal to or more than 50 kg/mol to less than 500 kg/mol, and a density of equal to or more than 910 kg/m 3 to equal to or less than 970 kg/m 3 to form said multimodal polyethylene composition, wherein the multimodal polyethylene composition a melt flow rate MFR 5 (190° C., 5 kg) of 0.01 to 10 g/10 min and a density of equal to or more than 910 kg/m 3 to equal to or less than 970 kg/m 3 a polyethylene composition obtainable by said process and the polyethylene resin of said first polymerization step.
1. A process for producing a multimodal polyethylene composition comprising the following steps:
i) polymerizing a polyethylene fraction (A-1) having a weight average molecular weight Mw of equal to or more than 500 kg/mol to equal to or less than 10,000 kg/mol and a density of equal to or more than 915 kg/m 3 to equal to or less than 960 kg/m 3 in a first reaction step and then polymerizing a polyethylene fraction (A-2) having a lower Mw as polyethylene fraction (A-1) and a density of equal to or more than 910 kg/m 3 to equal to or less than 975 kg/m 3 in a second reaction step of a sequential multistage process wherein one of said polyethylene fractions is polymerized in the presence of the other of said polyethylene fractions to form a first polyethylene resin (A) having a weight average molecular weight Mw of equal to or more than 150 kg/mol to equal to or less than 1,500 kg/mol, and a density of equal to or more than 910 kg/m 3 to equal to or less than 975 kg/m 3 , wherein the weight average molecular weight Mw of the first polyethylene resin (A) is lower than the weight average molecular weight Mw of the polyethylene fraction (A-1);
ii) blending the first polyethylene resin (A) with a second polyethylene resin (B) having a weight average molecular weight Mw of equal to or more than 50 kg/mol to less than 500 kg/mol, and a density of equal to or more than 910 kg/m 3 to equal to or less than 970 kg/m 3 to form said multimodal polyethylene composition,
wherein the multimodal polyethylene composition has a melt flow rate MFR 5 (190° C., 5 kg) of 0.01 to 10 g/10 min and a density of equal to or more than 910 kg/m 3 to equal to or less than 970 kg/m 3 and the weight ratio of said first polyethylene resin (A) to said second polyethylene resin (B) in the polyethylene composition is 2:98 to 40:60; and
wherein the blending step ii) is performed by mechanical blending.
2. The process according to claim 1 , wherein said first polyethylene resin (A) is pelletized prior to blending with said second polyethylene resin (B) to form the polyethylene composition.
3. The process according to claim 1 , wherein said first polyethylene resin (A) is blended in powder form with said second polyethylene resin (B) to form the polyethylene composition.
4. The process according to claim 1 , wherein said polyethylene fraction (A-2) is polymerized in the presence of said polyethylene fraction (A-1).
5. The process according to claim 1 , wherein the polyethylene composition is formed by melt blending of said first polyethylene resin (A) and said second polyethylene resin (B).
6. The process according to claim 1 , wherein the amount of said polyethylene fraction (A-1) is 0.5 to 36 wt % of the total amount of the polyethylene composition.