UV curable coating compositions for improved abrasion resistance
An ophthalmic article and methods of manufacturing the ophthalmic article are described herein. The ophthalmic article can include a first coating and a second coating. The first coating can include an abrasion resistant coating that includes flexible materials. The abrasion resistant coating can be radiation cured. The second coating can include a sputter-applied anti-reflective (AR) coating. Such an ophthalmic article can have a Bayer value of at or between 1.25 and 2.6, between 1.25 and 2.0 or 1.25 and 1.75; and a hand steel wool value of 3 or less.
1. An ophthalmic article comprising:
a first coating comprising an abrasion resistant coating comprising at least one flexible material having a glass transition temperature ranging from −150° C. to 25° C., wherein the abrasion resistant coating is radiation-cured; and
a second coating comprising a sputter-applied anti-reflective (AR) coating,
wherein the ophthalmic article has a Bayer value of at or between 1.25 and 2.6 and a hand steel wool value of 3 or less.
2. The ophthalmic article of claim 1 , wherein the second coating is adhered directly to the first coating.
3. The ophthalmic article of claim 1 , wherein the at least one flexible material comprises at least one of an aliphatic epoxy, a difunctional acrylate, a vinyl silane, a vinyl ether, a urethane, or a polyester.
4. The ophthalmic article of claim 1 , wherein the first coating further comprises at least one rigid material, wherein the rigid material comprises at least one of an epoxy alkoxysilane, a mono-organoalkoxysilane, a tetraorganoxysilane, or a polyorganoxysiloxane.
5. The ophthalmic article of 4 , wherein the first coating comprises flexible material in a greater weight amount than a weight amount of rigid material.
6. The ophthalmic article of claim 1 , wherein the first coating further comprises highly cross-linkable materials, wherein the highly cross-linkable materials comprise at least one of SiO 2 , pentaerythritol tri- and tetra acrylate, pentaerythritol triacrylate, ethoxylated pentaerythritol tetraacrylate, dipentaerythritol pentaacrylate, or dipentaerthritolhexaacrylate.
7. The ophthalmic article of claim 1 , wherein the first coating is a single layer.
8. The ophthalmic article of claim 1 , wherein the anti-reflective coating comprises at least four layers.
9. A method of manufacturing an ophthalmic article comprising:
applying a first coating to an ophthalmic article, wherein the first coating comprises a radiation-curable abrasion resistant coating comprising at least one flexible material having a glass transition temperature ranging from −150° C. to 25° C.;
radiation-curing the first coating; and
sputter-applying a second coating onto the first coating, the second coating comprising an anti-reflective coating;
wherein the article, after application of the second coating, has a Bayer value of at or between 1.25 and 2.6 and a hand steel wool value of 3 or less.
10. The method of claim 9 , wherein the second coating is adhered directly to the first coating.
11. The method of claim 9 , wherein the at least one flexible material comprises at least one of an aliphatic epoxy, a difunctional acrylate, a vinyl silane, a vinyl ether, a urethane, a polyester, or any combination thereof.
12. The method of claim 9 , wherein the first coating further comprises at least one rigid material, wherein the rigid material comprises at least one of an epoxy alkoxysilane, a mono-organoalkoxysilane, a tetraorganoxysilane, or a polyorganoxysiloxane, and wherein a weight amount of flexible material is greater than a weight amount of rigid material.
13. The method of claim 9 , wherein the first coating is a single layer.
14. The method of claim 9 , wherein the anti-reflective coating comprises at least four layers.
15. An ophthalmic article manufactured by the method of claim 9 .
16. The ophthalmic article of claim 1 , wherein the first coating further comprises at least one rigid material.
17. The ophthalmic article of claim 1 , wherein the first coating further comprises at least one rigid material having a glass transition temperature ranging from 25° C. to 250° C.
18. The method of claim 9 , wherein the first coating further comprises at least one rigid material.
19. The method of claim 9 , wherein the first coating further comprises at least one rigid material having a glass transition temperature ranging from 25° C. to 250° C.