Powder compositions for laser sintering
Powder compositions for laser sintering. Nylon copolymer compositions are described which provide enhanced performance in processing and finished products when used in 3D laser sintering processes.
1. A polymer powder composition particularly adapted for use in laser sintering comprising a heat stabilizer and a nylon copolymer containing at least one aromatic component and at least one aliphatic component,
wherein the aliphatic component comprises nylon 612 present in an amount of about 75 mole % to about 95 mole %, and
wherein the at least one aromatic component comprises one or more phthalic acid present in an amount of about 5 mole % to about 25 mole %.
2. The polymer powder composition of claim 1 , wherein the polymer powder composition is obtained by grinding polymer pellets.
3. The polymer powder composition of claim 1 , wherein the nylon copolymer exhibits a difference between melting temperature and crystallization temperature of 52° C.
4. The polymer powder of composition claim 1 , wherein the aliphatic component is bio-based.
5. The polymer powder composition of claim 1 , wherein the heat stabilizer comprises copper halide and/or phosphorous antioxidant.
6. The polymer powder composition of claim 1 wherein the phthalic acid comprises isophthalic acid and/or terephthalic acid.
7. The polymer powder composition of claim 1 , wherein the aromatic component comprises isophthalic acid present in an amount of about 0.5 mole % to about 4.5 mole % and terephthalic acid present in an amount of about 9 mole % to about 22 mole %.
8. The polymer powder composition of claim 7 , wherein the nylon 612 is present in an amount of about 80 mole %, and the isophthalic acid is present in an amount of about 2 mole % and terephthalic acid present in an amount of about 18 mole %.
9. A method of making a 3D laser sintered part using the polymer powder composition of claim 1 .
10. A polymer powder composition particularly adapted for use in laser sintering comprising a heat stabilizer and a nylon copolymer containing at least one aromatic component and at least one aliphatic component,
wherein the aliphatic component comprises nylon 610 present in an amount of about 75 mole % to about 95 mole %, and
wherein the at least one aromatic component comprises one or more phthalic acid present in an amount of about 5 mole % to about 25 mole %.
11. The polymer powder composition of claim 10 , wherein the nylon copolymer exhibits a difference between melting temperature and crystallization temperature of 58° C.