3-Dimensional high-strength fiber composite component and method for producing same
A 3-dimensional high-strength fiber composite component having isotropic fiber distribution, comprising 25 to 70 wt % of high-strength, high-modulus fibers, up to 5 wt % of binding fibers, and 25 to 70 wt % of thermosetting or thermoplastic matrix. The invention further relates to a method for producing same, comprising the following steps: preparing the fibers by opening the fibers by releasing the fibers from fiber bundles, bales, or textile structures; sucking and/or blowing the opened fibers onto a three-dimensional, air-permeable tool half having the contour of this side of the component in an interactively controlled manner; pre-solidifying the obtained fiber molding in the flock box; transferring the fiber molding onto a pressing tool in the form of the contour of the air-permeable tool half of the component; bringing into contact with at least one liquid plastic; and solidifying the fiber molding by pressing in order to form a component.
1. A method for producing a three-dimensional high-strength fiber composite component with an isotropic fiber distribution with a charge-dependent material distribution made of stiff high-modulus fibers and a plastic matrix, comprising the following steps in the given order:
(a) opening carbon fibers by releasing the same from fiber bundles, bales or textile structures;
(b) mixing of the carbon fibers after the opening with at least one binding fiber, wherein the mass proportion of the binding fibers in the entire fiber mass after the mixing is between about 0 and about 5% by weight;
(c) sucking and/or blowing of the opened released fibers onto a three-dimensional air-permeable half mold with a contour of this side of the three-dimensional high-strength fiber composite component;
(d) activating the binding fibers by heated air for preliminarily solidifying a fiber preform;
(e) transferring the fiber preform to a pressing mold in the form of the contour of the air-permeable half mold of the three-dimensional high-strength fiber composite component;
(f) contacting the fiber preform with at least one liquid plastic material; and
(g) solidifying the fiber preform by pressing the preform into the three-dimensional high-strength fiber composite component.
2. The method according to claim 1 , characterized in that the fibers are arranged on the surface of said three-dimensional air-permeable mold during the sucking and/or blowing in such a way that the coverage of the fibers has a uniform weight per unit area over the entire surface.
3. The method according to claim 1 , characterized in that the fibers are arranged on the surface of said three-dimensional air-permeable mold during the sucking and/or blowing in such a way that the coverage of the fibers has locally different weights per unit area.
4. The method according to claim 1 , characterized in that the transfer of said fiber preform to a pressing mold is effected by means of a transport tray, in which the fiber preform is retained by a vacuum.
5. The method according to claims 1 , characterized in that uniaxial fiber bundles and/or fabrics are applied to one or both surfaces of the fiber preform.
6. The method according to claim 1 , characterized in that one-component fibers of thermoplastic PUR, copolyamide or copolyester is employed as said binding fibers.
7. The method according to claim 1 , characterized in that bicomponent fibers with shell materials of thermoplastic PUR, copolyamide or copolyester are employed as said binding fibers.
8. The method according to claim 1 , characterized in that resins that are liquid in the application state and made of epoxy resin, polyurethane resin, polyester resin or casting polyamide are employed as matrix materials.
9. The method according to claim 8 , characterized in that said resin is sprayed on one or both sides of said fiber preform.
10. The method according to claim 8 , characterized in that said resin is injected through nozzles on the mold side into the pressed fiber preform in the closed mold.