Gold-based catalyst for the oxidative esterification of aldehydes to obtain carboxylic esters
View Patent ↗Catalysts for oxidative esterification can be used, for example, for converting (meth)acrolein to methyl (meth)acrylate. The catalysts are especially notable for high mechanical and chemical stability even over very long time periods, including activity and/or selectivity relatively in continuous operation in media having even a small water content.
1. A catalyst, comprising:
a) 0.01 to 10 mol % of gold,
b) 40 to 94 mol % of silicon,
c) 3 to 40 mol % of aluminium, and
d) 2 to 40 mol % of at least one element selected from the group consisting of alkali metals, alkaline earth metals, lanthanoids having atomic numbers 57 to 71, Y, Sc, Ti, Zr, Cu, Mn, Pb and Bi,
wherein components b) to d) are present as oxides and the stated amounts of components a) to d) relate to 100 mol % of the composition of the catalyst without oxygen,
wherein the catalyst is in the form of particles and is capable of catalyzing oxidative esterification of aldehydes to carboxylic esters,
wherein the catalyst has a shell structure comprising a core and at least one shell, where at least 80% of the total amount of component a) is part of a shell, and
wherein the catalyst has a PZC value between 7 and 11.
2. The catalyst according to claim 1 , which, except for the oxygen, consists of components a) to d).
3. The catalyst according to claim 1 , wherein the catalyst comprises between 0.05 and 2 mol % of component a).
4. The catalyst according to claim 1 , wherein component a) is in the form of particles having a mean diameter between 2 and 10 nm.
5. The catalyst according to claim 1 , wherein the catalyst particles have an average diameter between 10 and 200 μm and a spherical shape.
6. The catalyst according to claim 1 , wherein the catalyst comprises between 2 and 30 mol % of Mg, Ce, La, Y, Zr, Mn, Pb and/or Bi as component d).
7. The catalyst according to claim 1 , wherein the catalyst has a core and two shells, wherein at least 80% of the total amount of component a) is within an inner shell of the two shells.
8. A process for producing catalyst particles, wherein admixing a basic mixed oxide support with a gold-containing solution to form a component a) having a pH between 0.5 and 5.0,
wherein the basic mixed oxide support has a PZC value between 8 and 12 and a mean diameter between 10 and 200 μm, consists of b) 40 to 94 mol % of silicon, c) 3 to 40 mol % of aluminium and d) 2 to 40 mol % of at least one element selected from alkali metals, alkaline earth metals, rare earth metals, Ti, Zr, Cu, Mn, Pb and Bi,
wherein components b) to d) are present as oxides and the stated amounts of components a) to d) relate to 100 mol % of the composition of the catalyst without oxygen.
9. The process according to claim 8 , wherein the gold-containing solution contains at least one additional compound including components b), c) and/or d) in ionic form.
10. A method of producing an alkyl (meth)acrylate, comprising:
reacting (meth)acrolein with oxygen and a monofunctional alcohol to give the alkyl (meth)acrylate;
wherein the reacting is in the presence of a catalyst according to claim 1 .
11. The method according to claim 10 , wherein methacrolein is reacted with oxygen and methanol to give MMA.
12. A method of producing a hydroxyalkyl (meth)acrylate or a di-, tri- or tetra(meth)acrylate, comprising:
reacting (meth)acrolein with oxygen and a di-, tri- or tetrafunctional alcohol to give the hydroxyalkyl (meth)acrylate or to give the di-, tri- or tetra(meth)acrylate;
wherein the reacting is in the presence of a catalyst according to claim 1 .
13. The method according to claim 10 , wherein the reacting is conducted continuously.
14. The method according to claim 13 , wherein the catalyst is present in suspension form in a stirred reactor during the reacting.
15. The method according to claim 12 , wherein the reacting is conducted continuously.
16. The method according to claim 15 , wherein the catalyst is present in suspension form in a stirred reactor during the reacting.
17. The catalyst according to claim 3 , wherein component a) is in the form of particles having a mean diameter between 2 and 10 nm.
18. The catalyst according to claim 3 , wherein the catalyst particles have an average diameter between 10 and 200 μm and a spherical shape.
19. The catalyst according to claim 3 , wherein the catalyst comprises between 2 and 30 mol % of Mg, Ce, La, Y, Zr Mn, Pb and/or Bi as component d).
20. The catalyst according to claim 3 , wherein the catalyst has a core and two shells, wherein at least 80% of the total amount of component a) is within an inner shell of the two shells.