Engineering minerals for use as polycarbonate fillers, and methods of using the same to reinforce polycarbonates
View Patent ↗A reinforced resin composition may include a polycarbonate, a functionalizing agent, and an inorganic filler that has been functionalized with the functionalizing agent, the functionalized inorganic filler being present in an amount ranging from 1 to 25 percent by weight of the resin composition. The reinforced resin may exhibit a melt flow index of 25 or less, when measured at a load of 1.2 kg, after allowing the resin to remain at a temperature of 300° C. for 10 minutes. A method of reducing thermal degradation of a reinforced polycarbonate material may include introducing into said polycarbonate material at least one inorganic filler functionalized with a functionalizing agent, such that the reinforced resin exhibits a melt flow index of 25 or less, when measured at a load of 1.2 kg, after allowing the resin to remain at a temperature of 300° C. for 10 minutes.
1. A reinforced resin composition comprising:
a polycarbonate in an amount ranging from 75 to 99 percent by weight of the resin composition;
a functionalizing agent; and
an inorganic filler functionalized with the functionalizing agent, the functionalized inorganic filler being present in an amount ranging from 1 to 25 percent by weight of the resin composition;
wherein the reinforced resin exhibits a melt flow index of 25 or less, when measured at a load of 1.2 kg, after allowing the resin to remain at a temperature of 300° C. for 10 minutes;
wherein a splay formation is reduced as compared to the splay formation relative to a reinforce resin composition including the inorganic filler when it has not been functionalized.
2. The reinforced resin composition of claim 1 , wherein the functionalizing agent comprises at least one organo-modified silane chosen from a methacrylate-silane (MEMO-silane), a vinyl silane, a phenyl silane, an epoxy silane, or combinations thereof.
3. The reinforced resin composition of claim 2 , wherein the functionalizing agent further comprises at least one of modified styrene acrylic polymer, monomeric carbodimide, or polymeric carbodimide.
4. The reinforced resin composition of claim 1 , wherein the functionalizing agent comprises at least one of modified styrene acrylic polymer, monomeric carbodimide, or polymeric carbodimide.
5. The reinforced resin composition of claim 1 , wherein the inorganic filler comprises talc, mica, kaolin, perlite, or combinations thereof.
6. The reinforced resin composition of claim 5 , wherein the inorganic filler comprises talc having a d 50 ranging from 0.5 to 5 μm, and comprises low BET macrocrystalline talc.
7. The reinforced resin composition of claim 1 , wherein the functionalized inorganic filler exhibits a melt flow index of 20 or less.
8. The reinforced resin composition of claim 1 , wherein the inorganic compound exhibits a surface area less than 12 m 2 /g.
9. The reinforced resin composition of claim 1 , further including at least one additional component chosen from plasticizers, impact modifiers, pigments, dyes, colorants, stabilizers, or processing aids.
10. The reinforced resin composition of claim 1 , wherein the inorganic filler functionalized with the functionalizing agent has a reduced moisture adsorption by at least 45%, when tested at 97% relative humidity and 23° C. for 120 hours, relative to the inorganic filler when it has not been functionalized.
11. A method of reducing thermal degradation of a reinforced polycarbonate material, said method comprising:
introducing into said polycarbonate material at least one inorganic filler that has been functionalized with a functionalizing agent to modify the surface activity of said inorganic filler, such that the reinforced resin exhibits a melt flow index of 25 or less, when measured at a load of 1.2 kg, after allowing the resin to remain at a temperature of 300° C. for 10 minutes.
12. The method of claim 11 , wherein the functionalizing agent comprises at least one organo-modified silane chosen from a methacrylate-silane (MEMO-silane), a vinyl silane, a phenyl silane, an epoxy silane, or combinations thereof.
13. The method of claim 12 , wherein the functionalizing agent further comprises at least one of modified styrene acrylic polymer, monomeric carbodimide, or polymeric carbodimide.
14. The method of claim 11 , wherein the functionalizing agent comprises at least one of modified styrene acrylic polymer, monomeric carbodimide, or polymeric carbodimide.
15. The method of claim 11 , wherein the inorganic filler comprises talc, mica, kaolin, perlite, or combinations thereof.
16. The method of claim 11 , wherein the inorganic filler comprises talc having a d 50 ranging from 0.5 to 5 μm, and comprises macrocrystalline talc having a surface area less than 12 m 2 /g.
17. The method of claim 11 , wherein the functionalized inorganic filler exhibits a melt flow index of 20 or less.
18. The method of claim 11 , further comprising at least one component chosen from plasticizers, impact modifiers, pigments, dyes, colorants, stabilizers, or processing aids.
19. The method of claim 11 , wherein the inorganic filler functionalized with the functionalizing agent has a reduced moisture adsorption by at least 45%, when tested at 97% relative humidity and 23° C. for 120 hours, relative to the inorganic filler when it has not been functionalized.
20. The method of claim 11 , wherein a splay formation is reduced as compared to the splay formation relative to a reinforced polycarbonate material including the inorganic filler when it has not been functionalized.