SPONGE-FORMABLE SILICONE RUBBER COMPOSITION AND SILICONE RUBBER SPONGE
A sponge-formable silicone rubber composition comprises: (A) a polyorganosiloxane having at least two silicon-bonded alkenyl groups per molecule, (B) a polyorganosiloxane having at least two silicon-bonded hydrogen atoms per molecule, (C) water, (D) cellulose nanofibers, (E) an emulsifier, and (F) a hydrosilylation reaction catalyst. The sponge-formable silicone rubber composition can form a silicone rubber sponge having uniform and fine bubbles and that does not readily contaminate a mold.
1 . A sponge-formable silicone rubber composition comprising:
(A) 100 parts by mass of a polyorganosiloxane having at least two silicon-bonded alkenyl groups per molecule;
(B) a polyorganosiloxane having at least two silicon-bonded hydrogen atoms per molecule, in an amount such that an amount of silicon-bonded hydrogen atoms in component (B) is from 0.4 to 20 moles per 1 mole of alkenyl groups in component (A);
(C) from 20 to 500 parts by mass of water;
(D) cellulose nanofibers, in an amount of from 0.01 to 15 parts by mass per 100 parts by mass of component (C);
(E) from 0.1 to 15 parts by mass of an emulsifier; and
(F) a hydrosilylation reaction catalyst, in an amount to accelerate a hydrosilylation reaction of the composition.
2 . The sponge-formable silicone rubber composition according to claim 1 , wherein component (D) is cellulose nanofibers having a number-average fiber diameter of 2 to 150 nm.
3 . The sponge-formable silicone rubber composition according to claim 1 , further comprising (G) a hydrosilylation reaction inhibitor, in an amount of 0.001 to 5 parts by mass per 100 parts by mass of component (A).
4 . The sponge-formable silicone rubber composition according to claim 1 , further comprising (H) a reinforcing silica fine powder, in an amount of not greater than 30 parts by mass per 100 parts by mass of component (A).
5 . A silicone rubber sponge obtained by crosslinking the sponge-formable silicone rubber composition according to claim 1 by a hydrosilylation reaction and then removing water from the obtained silicone rubber, or removing water while crosslinking the composition by a hydrosilylation reaction.
6 . The silicone rubber sponge according to claim 5 , wherein the sponge is a silicone rubber sponge for a fixing member for an image forming device.
7 . The sponge-formable silicone rubber composition according to claim 2 , further comprising (G) a hydrosilylation reaction inhibitor, in an amount of 0.001 to 5 parts by mass per 100 parts by mass of component (A).
8 . The sponge-formable silicone rubber composition according to claim 7 , further comprising (H) a reinforcing silica fine powder, in an amount of not greater than 30 parts by mass per 100 parts by mass of component (A).
9 . The sponge-formable silicone rubber composition according to claim 2 , further comprising (H) a reinforcing silica fine powder, in an amount of not greater than 30 parts by mass per 100 parts by mass of component (A).
10 . The sponge-formable silicone rubber composition according to claim 3 , further comprising (H) a reinforcing silica fine powder, in an amount of not greater than 30 parts by mass per 100 parts by mass of component (A).