Multi-layered aluminium brazing sheet material
Brazing sheet material having an aluminium core alloy layer, a first brazing clad layer on one face of the core layer and an inter-layer between the core layer and the first clad layer material. The core layer of aluminium alloy including, up to 0.6% Si, up to 0.45% Fe, 0.6% to 1.25% Cu, 0.6% to 1.4% Mn, 0.08% to 0.4% Mg, up to 0.2% Cr, up to 0.25% Zr, up to 0.25% Ti, up to 0.3% Zn, balance aluminium. The first clad layer is made from 4xxx-series aluminium alloy having 6% to 14% Si and up to 2% Mg, balance aluminium. The inter-layer is made from 3xxx-series aluminium alloy including, up to 0.4% Si, up to 0.5% Fe, up to 0.8% Cu, 0.4% to 1.1% Mn, up to 0.04% Mg, up to 0.2% Cr, up to 0.25% Zr, up to 0.25% Ti, up to 0.3% Zn, balance aluminium.
1. A multi-layered brazing sheet material having
an aluminium core alloy layer provided with
a first brazing clad layer material on one face of said aluminium core layer and an inter-layer inter-positioned between the aluminium core alloy layer and the first brazing clad layer material,
wherein the core layer is made from an aluminium alloy comprising, in wt. %, up to 0.6% Si, up to 0.45% Fe, 0.6% to 1.25% Cu, 0.6% to 1.4% Mn, 0.08% to 0.4% Mg, up to 0.2% Cr, up to 0.25% Zr, up to 0.25% Ti, up to 0.3% Zn, balance aluminium and impurities,
wherein the first brazing clad layer is made from an 4xxx-series aluminium alloy having 6% to 14% Si and up to 2% Mg, balance aluminium and impurities, and
wherein the inter-layer is made from an 3xxx-series aluminium alloy comprising, in wt. %, up to 0.4% Si, up to 0.5% Fe, 0.40% to 0.75% Cu, 0.4% to 1.1% Mn, up to 0.04% Mg, up to 0.2% Cr, up to 0.25% Zr, up to 0.25% Ti, up to 0.3% Zn, balance aluminium and impurities, and wherein the core layer has been homogenized.
2. The multi-layered brazing sheet material according to claim 1 , wherein the Cu-content in the core alloy is higher than in the inter-layer positioned between the core alloy and the first brazing clad layer.
3. The multi-layered brazing sheet material according to claim 1 , wherein the core layer is made from an aluminium alloy consisting of, in wt. %, up to 0.25% Si, up to 0.35% Fe, 0.7% to 1.1% Cu, 0.7% to 1.2% Mn, 0.1% to 0.4% Mg, up to 0.2% Cr, 0.04% to 0.25% Zr, 0.03% to 0.2% Ti, up to 0.15% Zn, balance aluminium and impurities.
4. The multi-layered brazing sheet material according to claim 1 , wherein the core layer is made from an aluminium alloy consisting of, in wt. %, up to 0.1% Si, up to 0.25% Fe, 0.75% to 1.05% Cu, 0.75% to 1.1% Mn, 0.15% to 0.35% Mg, up to 0.1% Cr, 0.04% to 0.15% Zr, 0.05% to 0.2% Ti, up to 0.1% Zn, balance aluminium and impurities.
5. The multi-layered brazing sheet material according to claim 1 , wherein 3xxx-series aluminium inter-layer alloy is made from an aluminium alloy consisting of, in wt. %: up to 0.3% Si, up to 0.5% Fe, 0.40% to 0.75% Cu, 0.6% to 1.1% Mn, up to 0.04% Mg, up to 0.2% Cr, up to 0.25% Zr, up to 0.25% Ti, up to 0.3% Zn, balance aluminium and impurities.
6. The multi-layered brazing sheet material according to claim 5 , wherein 3xxx-series aluminium inter-layer alloy is made from an aluminium alloy having up to 0.15% Zn.
7. The multi-layered brazing sheet material according to claim 1 , wherein the brazing sheet material has a post-braze yield strength of at least 65 MPa.
8. The multi-layered brazing sheet material according to claim 1 , and wherein the inter-layer has a thickness of 4% to 20% of the total thick-ness of the multi-layered brazing sheet product.
9. The multi-layered brazing sheet material according to claim 1 , wherein the multi-layered brazing sheet product has a total thickness in the range of 0.1 to 0.8 mm.
10. The multi-layered brazing sheet material according to claim 1 , wherein the inter-liner layer has been homogenised.
11. The multi-layered brazing sheet material according to claim 1 , wherein the 3xxx-series inter-liner layer is non-homogenised.
12. A multi-layered brazed tube made from the multi-layered brazing sheet material according to claim 1 .
13. A heat exchanger comprising a brazed tube made from the multi-layered brazing sheet material according to claim 1 .
14. A charge-air-cooler, incorporating a brazed tube made from the multi-layered brazing sheet material according to claim 1 .
15. The multi-layered brazing sheet material according to claim 1 , wherein 3xxx-series aluminium inter-layer alloy is made from an aluminium alloy consisting of, in wt. %: up to 0.3% Si, up to 0.5% Fe, 0.40% to 0.70% Cu, 0.6% to 1.1% Mn, up to 0.04% Mg, up to 0.2% Cr, up to 0.25% Zr, up to 0.25% Ti, up to 0.3% Zn, balance aluminium and impurities.
16. The multi-layered brazing sheet material according to claim 5 , wherein 3xxx-series aluminium inter-layer alloy is made from an aluminium alloy having up to 0.1% Zn.
17. The multi-layered brazing sheet material according to claim 1 , wherein the brazing sheet material has a post-braze yield strength of at least 70 MPa.
18. An air-to-water charge-air-cooler, incorporating a brazed tube made from the multi-layered brazing sheet material according to claim 1 .