Hot-dip zinc-based plated steel sheet
[Object] To provide a hot-dip zinc-based plated steel sheet excellent in coating film adhesiveness after hot pressing more conveniently. [Solution] A hot-dip zinc-based plated steel sheet according to the present invention includes: a hot-dip zinc-based plated steel sheet that is a base metal; and a surface treatment layer formed on at least one surface of the hot-dip zinc-based plated steel sheet, in which the surface treatment layer contains one or more oxides selected from zirconia, lanthanum oxide, cerium oxide, and neodymium oxide each having a particle size of more than or equal to 5 nm and less than or equal to 500 nm, in a range of more than or equal to 0.2 g/m 2 and less than or equal to 2 g/m 2 per one surface.
1. A hot-dip zinc-based plated steel sheet comprising:
a hot-dip zinc-based plated steel sheet that is a base metal; and
a surface treatment layer formed on at least one surface of the hot-dip zinc-based plated steel sheet, wherein
the surface treatment layer contains one or more oxides selected from zirconia, lanthanum oxide, cerium oxide, and neodymium oxide each having a particle size of more than or equal to 5 nm and less than or equal to 500 nm, in a range of more than or equal to 0.2 g/m 2 and less than or equal to 2 g/m 2 per one surface, and contains 20 mass % or more of resin, and
the surface treatment layer further contains one or more vanadium-containing compounds and/or one or more copper-containing compounds in the following range as a content per one surface,
the one or more vanadium-containing compounds: more than 0.0 g/m 2 and less than or equal to 0.01 g/m 2 on a V basis,
the one or more copper-containing compounds: more than 0.0 g/m 2 and less than or equal to 0.02 g/m 2 on a Cu basis.
2. The hot-dip zinc-based plated steel sheet according to claim 1 , wherein
the surface treatment layer further contains one or more phosphorus-containing compounds, one or more aluminum-containing compounds, one or more silicon-containing compounds, and/or one or more chromium-containing compounds in the following range as a content per one surface,
the one or more phosphorus-containing compounds: more than 0.0 g/m 2 and less than or equal to 0.01 g/m 2 on a P basis,
the one or more aluminum-containing compounds: more than 0.0 g/m 2 and less than or equal to 0.005 g/m 2 on an Al basis,
the one or more silicon-containing compounds: more than 0.0 g/m 2 and less than or equal to 0.005 g/m 2 on a Si basis, and
the one or more chromium-containing compounds: more than 0.0 g/m 2 and less than or equal to 0.01 g/m 2 on a Cr basis.
3. The hot-dip zinc-based plated steel sheet according to claim 1 , wherein
the particle size of each of the one or more oxides selected from zirconia, lanthanum oxide, cerium oxide, and neodymium oxide is more than or equal to 10 nm and less than or equal to 200 nm.
4. The hot-dip zinc-based plated steel sheet according to claim 1 , wherein
the content of the one or more oxides selected from zirconia, lanthanum oxide, cerium oxide, and neodymium oxide is more than or equal to 0.4 g/m 2 and less than or equal to 1.5 g/m 2 per one surface.
5. The hot-dip zinc-based plated steel sheet according to claim 1 , wherein
the one or more oxides include zirconia or lanthanum oxide.
6. The hot-dip zinc-based plated steel sheet according to claim 1 , wherein
the surface treatment layer further contains one or more oxides selected from titanium oxide, nickel oxide, and tin(IV) oxide each having a particle size of more than or equal to 2 nm and less than or equal to 100 nm, in a range of more than or equal to 0.2 g/m 2 and less than or equal to 2 g/m 2 per one surface.
7. The hot-dip zinc-based plated steel sheet according to claim 6 , wherein
the particle size of each of the one or more oxides selected from titanium oxide, nickel oxide, and tin(IV) oxide is more than or equal to 5 nm and less than or equal to 50 nm.
8. The hot-dip zinc-based plated steel sheet according to claim 6 , wherein
the content of the one or more oxides selected from titanium oxide, nickel oxide, and tin(IV) oxide is more than or equal to 0.4 g/m 2 and less than or equal to 1.5 g/m 2 per one surface.
9. The hot-dip zinc-based plated steel sheet according to claim 6 , wherein
the one or more oxides include titanium oxide.
10. The hot-dip zinc-based plated steel sheet according to claim 1 , wherein
the surface treatment layer further contains magnesium oxide, calcium oxide, or zinc oxide in a range of more than or equal to 0.2 g/m 2 and less than or equal to 5.0 g/m 2 per one surface.
11. The hot-dip zinc-based plated steel sheet according to claim 10 , wherein
the particle size of the magnesium oxide, the calcium oxide, or the zinc oxide is more than or equal to 5 nm and less than or equal to 100 nm.
12. The hot-dip zinc-based plated steel sheet according to claim 10 , wherein
the content of the magnesium oxide, the calcium oxide, or the zinc oxide is more than or equal to 0.4 g/m 2 and less than or equal to 2.5 g/m 2 per one surface.
13. The hot-dip zinc-based plated steel sheet according to claim 1 , wherein
the hot-dip zinc-based plated steel sheet is a hot-dip zinc-based plated steel sheet for hot pressing.