Tire rubber composition and pneumatic tire
Provided are a tire rubber composition capable of producing a pneumatic tire having excellent rigidity and wear resistance and a pneumatic tire using the same. The tire rubber composition includes 100 parts by mass of a diene rubber (A) and from 1 to 50 parts by mass of elastic microparticles (B), wherein the elastic microparticles (B) have a form of microparticles obtained by crosslinking a crosslinkable oligomer or polymer (b1) in water or an organic solvent, or in the diene rubber (A), and have an average particle size of from 0.001 to 100 μm, the JIS A hardness of a cured product obtained by crosslinking the crosslinkable oligomer or polymer (b1) without use of water, the organic solvent or the diene rubber (A) is greater than 45, and the elongation of the cured product is 200% or greater.
1. A tire rubber composition comprising 100 parts by mass of a diene rubber (A) and from 1 to 50 parts by mass of elastic microparticles (B), wherein
the elastic microparticles (B) have a form of microparticles obtained by crosslinking a crosslinkable oligomer or polymer (b1) in water or an organic solvent or in the diene rubber (A), and have an average particle size of from 0.001 to 100 μm,
the JIS A hardness of a cured product obtained by crosslinking the crosslinkable oligomer or polymer (b1) without use of water, the organic solvent or the diene rubber (A) is greater than 45, and the elongation of the cured product is 200% or greater,
the crosslinkable oligomer or polymer (b1) is a polyether-based, polyester-based, polyolefin-based, polycarbonate-based, aliphatic, saturated hydrocarbon-based, acrylic, plant-derived or siloxane-based polymer or copolymer,
the crosslinkable oligomer or polymer (b1) has at least one crosslinkable functional group selected from the group consisting of a hydroxyl group, a hydrolyzable silyl group, a silanol group, an isocyanate group, a (meth)acryloyl group, an allyl group, a carboxy group, an acid anhydride group, and an epoxy group, and
the elastic microparticles (B) have at least one selected from the group consisting of a mercapto group and a sulfide bond on the surface of the elastic microparticles (B).
2. The tire rubber composition according to claim 1 , wherein the microparticles (B) have a composite structure composed of a component compatible with the diene rubber (A) and a component incompatible with the diene rubber (A).
3. The tire rubber composition according to claim 2 , further comprising a carbon black and/or a white filler (C) in an amount of from 1 to 100 parts by mass per 100 parts by mass of the diene rubber (A).
4. The tire rubber composition according to claim 2 , wherein the elastic microparticles (B) are microparticles obtained by crosslinking the crosslinkable oligomer or polymer (b1) in a dispersion including water or the organic solvent as a dispersion medium, removing the dispersion medium, and forming a powder.
5. The tire rubber composition according to claim 2 , wherein the elastic microparticles (B) are microparticles obtained by crosslinking the crosslinkable oligomer or polymer (b1) in the diene rubber (A).
6. The tire rubber composition according to claim 1 , further comprising a carbon black and/or a white filler (C) in an amount of from 1 to 100 parts by mass per 100 parts by mass of the diene rubber (A).
7. The tire rubber composition according to claim 6 , wherein the elastic microparticles (B) are microparticles obtained by crosslinking the crosslinkable oligomer or polymer (b1) in a dispersion including water or the organic solvent as a dispersion medium, removing the dispersion medium, and forming a powder.
8. The tire rubber composition according to claim 6 , wherein the elastic microparticles (B) are microparticles obtained by crosslinking the crosslinkable oligomer or polymer (b1) in the diene rubber (A).
9. The tire rubber composition according to claim 1 , wherein the elastic microparticles (B) are microparticles obtained by crosslinking the crosslinkable oligomer or polymer (b1) in a dispersion including water or the organic solvent as a dispersion medium, removing the dispersion medium, and forming a powder.
10. The tire rubber composition according to claim 9 , wherein the elastic microparticles (B) are microparticles obtained by crosslinking the crosslinkable oligomer or polymer (b1) in the diene rubber (A).
11. The tire rubber composition according to claim 1 , wherein the elastic microparticles (B) are microparticles obtained by crosslinking the crosslinkable oligomer or polymer (b1) in the diene rubber (A).
12. A pneumatic tire comprising a tire tread formed using the tire rubber composition described in claim 1 .
13. A pneumatic tire comprising a tire tread formed using the tire rubber composition described in claim 2 .
14. A pneumatic tire comprising a tire tread formed using the tire rubber composition described in claim 6 .