Support carbon material and catalyst for solid polymer type fuel cell use
A support carbon material able to support a catalyst metal in a highly dispersed state and resistant to the flooding phenomenon and with little voltage drop even at the time of large current power generation under high humidity conditions and a catalyst using the same, specifically, a support carbon material for solid polymer type fuel cell use comprised of a porous carbon material which has a pore volume and a pore area found by the BJH analysis method from a nitrogen adsorption isotherm in an adsorption process of a radius 2 nm to 50 nm pore volume V A of 1 ml/g to 5 ml/g and a radius 2 nm to 50 nm pore area S 2-50 of 300 m 2 /g to 1500 m 2 /g and a ratio (V 5-25 /V A ) of radius 5 nm to 25 nm pore volume V 5-25 (ml/g) to said pore volume V A (ml/g) of 0.4 to 0.7 and a ratio (V 2-5 /V A ) of radius 2 nm to 5 nm pore volume V 2-5 (ml/g) to the same of 0.2 to 0.5 and a catalyst using the same.
1. A support carbon material for solid polymer type fuel cell use comprised of a porous carbon material which has a pore volume and a pore area found by the BJH analysis method from a nitrogen adsorption isotherm in an adsorption process satisfying the following conditions:
a radius 2 nm to 50 nm pore volume V A of 1 ml/g to 5 ml/g and a radius 2 nm to 50 nm pore area S 2-50 of 300 m 2 /g to 1500 m 2 /g and
a ratio (V 5-25 /V A ) of radius 5 nm to 25 nm pore volume V 5-25 (ml/g) to said pore volume V A (ml/g) of 0.4 to 0.7 and a ratio (V 2-5 /V A ) of radius 2 nm to 5 nm pore volume V 2-5 (ml/g) to the same of 0.2 to 0.5.
2. The support carbon material for solid polymer type fuel cell use according to claim 1 wherein said pore volume V 5-25 is 0.7 ml/g to 2 ml/g.
3. The support carbon material for solid polymer type fuel cell use according to claim 1 or 2 wherein an average particle radius is 0.1 μm to 5 μm.
4. A catalyst for solid polymer type fuel cell use comprising
a support carbon material for solid polymer type fuel cell use according to any one of claim 1 at which catalyst metal particulates comprised of Pt or a Pt alloy having Pt as its main component are supported.
5. A catalyst for solid polymer type fuel cell use comprising
a support carbon material for solid polymer type fuel cell use according to claim 2 at which catalyst metal particulates comprised of Pt or a Pt alloy having Pt as its main component are supported.
6. A catalyst for solid polymer type fuel cell use comprising
a support carbon material for solid polymer type fuel cell use according to claim 3 at which catalyst metal particulates comprised of Pt or a Pt alloy having Pt as its main component are supported.