Graphite oxide reinforced fiber in hosts such as concrete or asphalt
This can be a method of making a high strength composite reinforcing fiber using flat GO flakes coated on a conventional reinforcing fiber. This maintains some the flexibility of the fiber and aligns the flat graphene flakes along the surface of the fiber; this dramatically increases the strength of the fiber. It also allows bonding between overlapping flakes, in contrast to flakes being uniformly dispersed in a host material that is being reinforced and dramatically increases the strength of the host material.
1. A method of making a high strength composite reinforcing fiber comprising:
providing substantially flat graphene oxide (GO) flakes;
providing a reinforcing fiber;
providing a host material;
coating the GO flakes on the reinforcing fiber; and
wherein 95% of the substantially flat GO flakes have a surface area to thickness ratio of a minimum of 300 Angstroms and a thickness of less than 160 Angstroms, wherein the graphene flakes have no significant physical surface distortions and no significant epoxy functionalization and wherein surfaces of the GO flakes have the same hydrophobicity as the host material.
2. The method of claim 1 , wherein the substantially flat GO flakes have an oxidation level greater than 1.5% by mass.
3. The method of claim 1 , wherein the GO flakes have an oxidation level less than 1.5% by mass.
4. The method of claim 1 , wherein 95% of the GO flakes are from about 0.8 to 16 nanometers in thickness.
5. The method of claim 1 , wherein the maximum dimension of the GO flakes is between 220 Angstroms and 100 microns.
6. The method of claim 1 , wherein the GO flakes have primarily edge oxidation.
7. The method of claim 1 , further comprising the step of mechanochemical exfoliating graphite into graphene/graphite oxide flakes is done in a stirred media mill, and the stirred media mill is an attrition mill or ball mill.
8. A method of making a high strength structure: comprising:
providing substantially flat GO flakes;
providing a reinforcing fiber;
providing the structure's host material;
coating the GO flakes on the reinforcing fiber;
air drying the coated fiber;
incorporating the coated fiber into the structure's host material; and
forming the structure's host material with the incorporated coated fiber into a structure; and
wherein 95% of the substantially flat GO flakes have a surface area to thickness ratio of a minimum of 300 Angstroms and a thickness of less than 160 Angstroms, wherein the graphene flakes have no significant physical surface distortions and no significant epoxy functionalization, and wherein surfaces of the GO flakes have the same hydrophobicity as the host material.
9. The method of claim 8 , wherein the GO flakes have an oxidation level greater than 1.5% by mass, and further comprising combining the coated fiber with Ordinary Portland Cement and other dry powders.
10. The method of claim 8 , further comprising the step of mixing the coated fiber in the host material for at least 30 minutes in a sonic mixing system.
11. The method of claim 8 , further comprising the step of adding water to react the host material with one or more materials that form concrete to form a concrete composite when cured.
12. The method of claim 8 , wherein the GO flakes have with an oxidation level less than 1.5% by mass, and further comprising combining the coated fiber with sand and other dry powders.
13. The method of claim 8 , further comprising the steps of mixing the coated fiber and the host material for at least 30 minutes in a sonic mixing system, and adding Bitumen or other non-polar material to react the host material to form a composite when cured.
14. The method of claim 8 , wherein the GO flakes have mass greater than 0.00005% than the mass of the host material.
15. The method of claim 8 , wherein 95% of the GO flakes are from about 0.8 to 16 nanometers in thickness.
16. The method of claim 8 , wherein the maximum dimension of the GO flakes is between 220 Angstroms and 100 microns.
17. The method of claim 8 , wherein the GO flakes have primarily edge oxidation.
18. The method of claim 8 , further comprising the step of mechano-chemical exfoliating graphite into graphene/graphite oxide flakes in a stirred media mill, and the stirred media mill is an attrition mill or ball mill.