Nitrile rubber glove with stretch modifier
An improved nitrile rubber formulation and process for making elastomeric nitrile rubber articles from the nitrile rubber formulation are disclosed. In particular, the nitrile rubber formulation can produce nitrile rubber based articles which exhibit force-strain characteristics that are comparable to those of natural rubber latex articles, while maintaining the tensile strength properties of nitrile rubber. The process includes adding a stretch modifier during the compounding of the nitrile rubber formulation. The invention also includes an elastomeric nitrile rubber product made by the process, such as examination glove, surgical glove, etc.
1. An elastomeric article comprising a compounded nitrile rubber formulation, the compounded nitrile rubber formulation comprising a nitrile rubber, an alkali agent, a metal oxide, a sulfur crosslinking agent, a vulcanization accelerator, and a stretch modifier, wherein the stretch modifier includes particles having a mean particle size ranging from about 0.5 micrometers to about 25 micrometers.
2. The elastomeric article of claim 1 , wherein the alkali agent is present in the compounded rubber nitrile formulation in an amount ranging from about 0.1 parts to about 0.99 parts based on 100 dry parts of the nitrile rubber.
3. The elastomeric article of claim 1 , wherein the metal oxide is present in the compounded rubber nitrile formulation in an amount ranging from about 0.01 parts to about 0.5 parts based on 100 dry parts of the nitrile rubber.
4. The elastomeric article of claim 1 , wherein the combined amount of the alkali agent and the metal oxide present in the compounded rubber nitrile formulation is less than or equal to 1, based on 100 dry parts of the nitrile rubber.
5. The elastomeric article of claim 1 , wherein the stretch modifier is a wax emulsion.
6. The elastomeric article of claim 5 , wherein the wax emulsion comprises a micronized wax.
7. The elastomeric article of claim 6 , wherein the micronized wax includes a polyethylene wax, an oxidized polyethylene wax, a modified polyethylene wax, a high density polyethylene wax, an oxidized high density polyethylene wax, a modified high density polyethylene wax, a polypropylene wax, a polyamide wax, a polytetrafluoroethylene wax, or a combination thereof.
8. The elastomeric article of claim 1 , wherein the stretch modifier is present in the compounded rubber nitrile formulation in an amount ranging from about 0.1 parts to about 10 parts, based on 100 dry parts of the nitrile rubber.
9. The elastomeric article of claim 1 , wherein the elastomeric article exhibits a tensile strength at break B ranging from about 20 MPa to about 50 MPa.
10. A method of making an elastomeric article, the method comprising: a) preparing a compounded nitrile rubber formulation comprising a nitrile rubber, an alkali agent, a metal oxide, a sulfur crosslinking agent, a vulcanization accelerator, and a stretch modifier, wherein the stretch modifier includes particles having a mean particle size ranging from about 0.5 micrometers to about 25 micrometers; b) dipping a mold into the compounded rubber nitrile formulation; and c) curing said compounded nitrile rubber formulation to form the elastomeric article.
11. The method of claim 10 , wherein the alkali agent is present in the compounded rubber nitrile formulation in an amount ranging from about 0.1 arts to about 0.99 arts based on 100 dry parts of the nitrile rubber.
12. The method of claim 10 , wherein the metal oxide is present in the compounded rubber nitrile formulation in an amount ranging from about 0.01 parts to about 0.5 parts based on 100 dry parts of the nitrile rubber.
13. The method of claim 10 , wherein the combined amount of the alkali agent and the metal oxide present in the compounded rubber nitrile formulation is less than or equal to 1, based on 100 dry parts of the nitrile rubber.
14. The method of claim 10 , wherein the stretch modifier is a wax emulsion.
15. The method of claim 14 , wherein the wax emulsion comprises a micronized wax.
16. The method of claim 15 , wherein the micronized wax includes a polyethylene wax, an oxidized polyethylene wax, a modified polyethylene wax, a high density polyethylene wax, an oxidized high density polyethylene wax, a modified high density polyethylene wax, a polypropylene wax, a polyamide wax, a polytetrafluoroethylene wax, or a combination thereof.
17. The method of claim 10 , wherein the stretch modifier is present in the compounded rubber nitrile formulation in an amount ranging from about 0.1 parts to about 10 parts, based on 100 dry parts of the nitrile rubber.
18. The method of claim 10 , wherein the nitrile rubber formulation is adjusted to a pH ranging from about 9 to about 11.