Natural fiber composite and method of production
A reinforced polymer composite includes a polymer matrix, a strengthening agent, and a dispersing agent. The strengthening agent is a natural fiber having an aspect ratio between 6 and 12 and is included in the composite in amounts up to 30 wt %. The dispersing agent is coconut shell powder having an aspect ratio between 1 and 3 and is included in the composite in amounts up to 10 wt %.
1. A reinforced polymer composite, the reinforced polymer composite comprising:
a polymer matrix;
a strengthening agent, the strengthening agent including a natural fiber having a first aspect ratio;
a dispersing agent, the dispersing agent including a coconut shell powder wherein the coconut shell powder has a low aspect ratio as compared to the first aspect ratio of the natural fiber; and
a solid phase grafted MAPP in the amount up to 3.0 wt %,
wherein the strengthening agent is homogenously dispersed in the polymer matrix.
2. The polymer composite material of claim 1 , wherein the natural fiber is a bast fiber included in the reinforced polymer composite in an amount up to about 40.0 wt %.
3. The polymer composite material of claim 2 , wherein the bast fiber is included in the amount of about 25.0 wt %.
4. The polymer composite material of claim 2 , wherein the bast fiber is included in the amount of about 20.0 wt %.
5. The polymer composite material of claim 1 , wherein the coconut shell powder is included in the reinforced polymer composite in the amount up to 10.0 wt %.
6. The polymer composite material of claim 5 , wherein the coconut shell powder is included in the reinforced polymer composite in the amount of about 5.0 wt %.
7. The polymer composite material of claim 1 , wherein the low aspect ratio of the coconut shell powder is between 1 and 3.
8. The polymer composite material of claim 1 , wherein the first aspect ratio of the natural fiber is between 6 and 12.
9. The polymer composite material of claim 1 , further including a scrubbing agent in the amount up to 2.0 wt %.
10. An injection molded reinforced polymer composite part, the reinforced polymer composite comprising:
a polymer matrix;
a strengthening agent, the strengthening agent including a natural fiber having a first aspect ratio in the amount up to 40.0 wt %;
a dispersing agent, the dispersing agent including a coconut shell powder in the amount up to 10.0 wt %, and wherein the coconut shell powder exhibits a low aspect ratio compared to the first aspect ratio;
a scrubbing agent in the amount up to 2.0 wt %, and
a solid phase grafted MAPP in the amount up to 2.0 wt %; and
wherein the strengthening agent is homogenously dispersed in the polymer matrix.
11. The polymer composite material of claim 10 , wherein the natural fiber is a bast fiber included in the reinforced polymer composite in the amount of about 25.0 wt % and the coconut shell powder is included in the reinforced polymer composite in the amount of about 5.0 wt %.
12. The polymer composite material of claim 10 , wherein the natural fiber is a bast fiber included in the amount of about 20.0 wt % and the coconut shell powder is included in the reinforced polymer composite in the amount of about 10.0 wt %.
13. The polymer composite material of claim 10 , wherein the low aspect ratio of the coconut fiber is between 1 and 3.
14. The polymer composite material of claim 13 , wherein the first aspect ratio is between 6 and 12.
15. A method for manufacturing a reinforced polymer composite part, the method including the steps of:
providing and cleaning a natural fiber strengthening agent having an aspect ratio between 6 and 12;
providing, milling, and cleaning a dispersing agent having an aspect ratio between 1 and 3;
drying the cleaned natural fiber strengthening agent and milled and cleaned dispersing agent;
providing and combining a polymer resin with the natural fiber strengthening agent, the dispersing agent, and a solid phase grafted MAPP in the amount up to 3.0 wt % in an extruder; and
injecting the combined polymer resin, natural fiber, and dispersing agent mixture into a die to form the part.
16. The method of claim 15 , wherein the natural fiber strengthening agent is provided in the amount of about 25.0 wt % and the dispersing agent is provided in the amount of about 5.0 wt %.
17. The method of claim 15 , wherein the natural fiber strengthening agent is provided in the amount of about 20.0 wt % and the dispersing agent is provided in the amount of about 10.0 wt %.
18. The method of claim 15 , wherein the dispersing agent is a coconut shell powder, the coconut shell powder is provided in the amount between 5.0 wt % and 10.0 wt %, the natural fiber is a bast fiber, and the bast fiber is provided in the amount between 20.0 wt % and 25.0 wt %.
19. A reinforced polymer composite, the reinforced polymer composite comprising:
a polymer matrix;
a strengthening agent, the strengthening agent including a natural fiber having a first aspect ratio;
a dispersing agent, the dispersing agent including a coconut shell powder wherein the coconut shell powder has a low aspect ratio as compared to the first aspect ratio of the natural fiber; and
a scrubbing agent in the amount up to 2.0 wt. %,
wherein the strengthening agent is homogenously dispersed in the polymer matrix.
20. The reinforced polymer composite material of claim 19 , wherein the natural fiber is a bast fiber included in the reinforced polymer composite in an amount up to about 40.0 wt %.
21. The polymer composite material of claim 20 , wherein the bast fiber is included in the amount of about 25.0 wt %.
22. The polymer composite material of claim 20 , wherein the bast fiber is included in the amount of about 20.0 wt %.
23. The reinforced polymer composite material of claim 19 , wherein the coconut shell powder is included in the reinforced polymer composite in the amount up to 10.0 wt %.
24. The polymer composite material of claim 23 , wherein the coconut shell powder is included in the reinforced polymer composite in the amount of about 5.0 wt %.
25. The reinforced polymer composite material of claim 19 , wherein the low aspect ratio of the coconut shell powder is between 1 and 3.
26. The reinforced polymer composite material of claim 19 , wherein the first aspect ratio of the natural fiber is between 6 and 12.
27. A method for manufacturing a reinforced polymer composite part, the method including the steps of:
providing and cleaning a natural fiber strengthening agent having an aspect ratio between 6 and 12;
providing, milling, and cleaning a dispersing agent having an aspect ratio between 1 and 3;
drying the cleaned natural fiber strengthening agent and milled and cleaned dispersing agent;
providing and combining a polymer resin with the natural fiber strengthening agent, the dispersing agent, and a scrubbing agent in an extruder, wherein the scrubbing agent is provided in an amount up to 2.0 wt. %; and
injecting the combined polymer resin, natural fiber, and dispersing agent mixture into a die to form the part.
28. The method of claim 27 , wherein the natural fiber strengthening agent is provided in the amount of about 25.0 wt % and the dispersing agent is provided in the amount of about 5.0 wt %.
29. The method of claim 27 , wherein the natural fiber strengthening agent is provided in the amount of about 20.0 wt % and the dispersing agent is provided in the amount of about 10.0 wt %.
30. The method of claim 27 , wherein the dispersing agent is a coconut shell powder, the coconut shell powder is provided in the amount between 5.0 wt % and 10.0 wt %, the natural fiber is a bast fiber, and the bast fiber is provided in the amount between 20.0 wt % and 25.0 wt %.