Polypropylene film structure
The present invention is a structure comprising a biaxially oriented film having a layer comprising a homopolymer of propylene which layer is in contact with oil, characterised in that the homopolymer of propylene has a content of isotactic pentads of from 95% to 98% and a content of ash of not more than 30 ppm.
1. A structure comprising a biaxially oriented film having a layer comprising:
a homopolymer of propylene which layer is in contact with oil, characterised in that the homopolymer of propylene has a content of isotactic pentads of from 95% to 98% and a content of ash of not more than 30 ppm; and
stabilisers, wherein the stabilisers are selected from the group consisting of 1,3,5-Trimethyl-2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzypenzene in an amount of from 600 to 1700 ppm, butylhydroxytoluene in an amount of from 200 to 900 ppm, both based on the amount of the homopolymer of propylene, and the mixtures thereof; and
wherein the biaxially oriented film does not contain pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate).
2. The structure according to claim 1 wherein the biaxially oriented film has a total content of additives selected from the group consisting of stabilisers, acid scavengers and nucleating agents in the range of from 600 to 5000 ppm.
3. The structure according to claim 2 , wherein the oil comprises at least 20% by weight of aromatic hydrocarbons.
4. The structure according to claim 3 wherein the oil comprises cyclic aromatic hydrocarbons.
5. The structure according to claim 4 wherein the oil comprises at least 50% by weight of cyclic aromatic hydrocarbons.
6. The structure according to claim 4 , wherein the cyclic aromatic hydrocarbons are toluene derivatives.
7. A method for making a capacitor comprising: providing a biaxially oriented film that includes a homopolymer of propylene having a content of isotactic pentads of from 95% to 98% and a content of ash of not more than 30 ppm; and stabilizers, wherein the stabilizers are selected from the group consisting of 1,3,5-Trimethyl-2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzypenzene in an amount of from 600 to 1700 ppm, butylhydroxytoluene in an amount of from 200 to 900 ppm, both based on the amount of the homopolymer of propylene, and the mixtures thereof; and wherein the biaxially oriented film does not contain pentaerythritol tetrakis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate); and
contacting a layer of the film with oil.
8. The method of claim 7 , comprising the steps of flat winding the film and an aluminum foil to obtain a wound structure, and impregnating the wound structure with oil.
9. The method claim 7 , wherein the film has a total content of additives selected from the group consisting of stabilisers, acid scavengers and nucleating agents in the range of from 600 to 5000 ppm.
10. The method of claim 9 , wherein the oil comprises at least 20% by weight aromatic hydrocarbons.
11. The method of claim 10 , wherein the oil comprises cyclic aromatic hydrocarbons.
12. The method of claim 1 , wherein the oil comprises at least 50% by weight of cyclic aromatic hydrocarbons.
13. The method of claim 11 , wherein the cyclic aromatic hydrocarbons are toluene derivatives.