THERMOPLASTIC FLUORORESIN COMPOSITION AND METHOD FOR PRODUCING CROSS-LINKED BODY
Provided are a thermoplastic fluororesin composition including a thermoplastic fluororesin (A) having a Shore D hardness of less than or equal to 50, the Shore D hardness being measured at 23° C. in accordance with ASTM D2240, and a cross-linked structure forming agent (B) that is selected from the group consisting of a polyfunctional unsaturated compound (b-1), a polyamine compound (b-2), and a polyhydroxy compound (b-3) and that is capable of forming a cross-linked structure through a reaction with the thermoplastic fluororesin (A), the thermoplastic fluororesin composition not substantially containing a peroxide compound when containing the (b-1), not substantially containing an acid acceptor when containing the (b-2), and not substantially containing at least one of the acid acceptor and an onium compound when containing the (b-3); and a method for producing a cross-linked body including a step of cross-linking the thermoplastic fluororesin composition by an ionizing radiation.
1 . A thermoplastic fluororesin composition comprising:
a thermoplastic fluororesin (A) having a Shore D hardness of less than or equal to 50, the Shore D hardness being measured at 23° C. in accordance with ASTM D2240; and
a cross-linked structure forming agent (B) that is selected from the group consisting of a polyfunctional unsaturated compound (b-1), a polyamine compound (b-2), and a polyhydroxy compound (b-3) and that is capable of forming a cross-linked structure through a reaction with the thermoplastic fluororesin (A),
the thermoplastic fluororesin composition not substantially containing a peroxide compound when containing the polyfunctional unsaturated compound (b-1), not substantially containing an acid acceptor when containing the polyamine compound (b-2), and not substantially containing at least one of the acid acceptor and an onium compound when containing the polyhydroxy compound (b-3).
2 . The thermoplastic fluororesin composition according to claim 1 , further comprising a cross-linkable rubber component (C).
3 . The thermoplastic fluororesin composition according to claim 2 , wherein the cross-linkable rubber component (C) is a fluorine rubber.
4 . The thermoplastic fluororesin composition according to claim 2 , wherein a content of the cross-linkable rubber component (C) is less than or equal to 100 parts by weight per 100 parts by weight of the thermoplastic fluororesin (A).
5 . A method for producing a cross-linked body comprising the steps of:
providing the thermoplastic fluororesin composition according to claim 1 ; and
cross-linking the thermoplastic fluororesin composition by an ionizing radiation.
6 . The method according to claim 5 , further comprising a step of molding the thermoplastic fluororesin composition between the step of providing the thermoplastic fluororesin composition and the step of cross-linking the thermoplastic fluororesin composition.