A surface treatment solution for a plated steel sheet to be hot-pressed comprising a ZnO aqueous dispersion (A) and a water dispersible organic resin (B), wherein the ZnO aqueous dispersion (A) comprises water and ZnO particle size having 50 to 300 nm particles, the water dispersible organic resin (B) has a 5 to 45 mgKOH/g acid value and 5 to 300 nm emulsion particle size, and a mass ratio (W A /W B ) of a mass of ZnO particles in the ZnO aqueous dispersion (W A ) to a mass of solid content of the water dispersible organic resin (W B ) is 30/70 to 95/5.
1. A surface treatment solution for a plated steel sheet to be hot-pressed comprising a ZnO aqueous dispersion (A) and a water dispersible organic resin (B), wherein
the ZnO aqueous dispersion (A) comprises water and ZnO particles having an average particle size of 10 to 300 nm,
the ZnO aqueous dispersion (A) comprises one or both of an anionic dispersant and nonionic dispersant,
the water dispersible organic resin (B) has a 5 to 300 nm emulsion average particle size, and
a mass ratio (W A /W B ) of a mass (W A ) of ZnO particles in the ZnO aqueous dispersion to a mass (W B ) of solid content in the water dispersible organic resin is 30/70 to 95/5,
wherein the ZnO particles have an aspect ratio (long axis/short axis) of 1 to 2.8.
2. The surface treatment solution for a plated steel sheet to be hot-pressed according to claim 1 , wherein the water dispersible organic resin (B) is one or more types of resin selected from a group consisting of a water dispersible polyurethane resin, a water dispersible epoxy resin, a water dispersible acryl resin, and a water dispersible polyester resin.
3. The surface treatment solution for a plated steel sheet to be hot-pressed according to claim 2 , wherein the water dispersible organic resin (B) has a number average molecular weight of 10000 or more.
4. The surface treatment solution for a plated steel sheet to be hot-pressed according to claim 2 , wherein the water dispersible organic resin (B) is one or more types of resin having a 5 to 45 mg KOH/g acid value and selected from a group consisting of a water dispersible polyurethane resin, a water dispersible acryl resin, and a water dispersible polyester resin.
5. The surface treatment solution for a plated steel sheet to be hot-pressed according to claim 2 , comprising at least one type of additive (C) selected from compounds comprising elements selected from the group consisting of B, Mg, Si, Ca, Ti, V, Zr, W, and Ce.
6. The surface treatment solution for a plated steel sheet to be hot-pressed according to 1, wherein the water dispersible organic resin (B) has a number average molecular weight of 10000 or more.
7. The surface treatment solution for a plated steel sheet to be hot-pressed according to claim 6 , wherein the water dispersible organic resin (B) is one or more types of resin having a 5 to 45 mg KOH/g acid value and selected from a group consisting of a water dispersible polyurethane resin, a water dispersible acryl resin, and a water dispersible polyester resin.
8. The surface treatment solution for a plated steel sheet to be hot-pressed according to claim 6 , comprising at least one type of additive (C) selected from compounds comprising elements selected from the group consisting of B, Mg, Si, Ca, Ti, V, Zr, W, and Ce.
9. The surface treatment solution for a plated steel sheet to be hot-pressed according to claim 1 , wherein the water dispersible organic resin ( 13 ) is one or more types of resin having a 5 to 45 mg KOH/g acid value and selected from a group consisting of a water dispersible polyurethane resin, a water dispersible acryl resin, and a water dispersible polyester resin.
10. The surface treatment solution for a plated eel sheet to be hot-pressed according to claim 9 , comprising at least one type of additive (C) selected from compounds comprising elements selected from the group consisting of B, Mg, Si, Ca, Ti, V, Zr, W, and Ce.
11. The surface treatment solution for a plated steel sheet to be hot-pressed according to claim 1 , comprising at least one type of additive (C) selected from compounds comprising elements selected from the group consisting of B, Mg, Si, Ca, Ti, V, Zr, W, and Ce.
12. The surface treatment solution for a plated steel sheet to be hot-pressed according to claim 11 , wherein a mass ratio (W C /W A ) of a mass (W C ) of the additive (C) to a mass (W A ) of the ZnO particles in the ZnO aqueous dispersion is 0.05 to 0.6.