Hydrogen-dispensing hose
Provided is a hydrogen-dispensing hose. At least two reinforcing layers are coaxially layered between an inner surface layer of a thermoplastic resin having a dry hydrogen gas permeability coefficient at 90° C. of 1×10 −8 cc·cm/cm 2 ·sec.·cmHg or less and an outer surface layer of a thermoplastic resin. A wire braided layer formed by braiding metal wires is used as the outermost reinforcing layer. Fiber braided layers formed by braiding high-strength fibers such as polyparaphenylene benzobisoxazole fibers are used as the other reinforcing layers.
1. A hydrogen-dispensing hose, comprising:
A coaxially layered inner surface layer and outer surface layer; and
at least two reinforcing layers coaxially layered between the coaxially layered inner layer and outer surface layer, the inner surface layer being formed from a thermoplastic resin having a dry hydrogen gas permeability coefficient at 90° C. of 1×10 −8 cc·cm/cm 2 ·sec.·cmHg or less, and the outer surface layer being formed from a thermoplastic resin;
the outermost reinforcing layer out of the reinforcing layers being a wire braided layer formed by braiding metal wires; and
the other reinforcing layer being a fiber braided layer formed by braiding high-strength fibers;
wherein the fiber braided layer is composed of at least three layers, a diameter of high-strength fibers constituting the fiber braided layer is 0.25 mm to 0.30 mm, a braid angle of an innermost fiber braided layer is 43° to 55°, a braid angle of a second innermost fiber braided layer is 45° to 55°, and a braid angle of a third innermost fiber braided layer is 50° to 60°.
2. The hydrogen-dispensing hose according to claim 1 , wherein the thickness of the inner surface layer is 0.5 mm to 1.5 mm, and the inner diameter thereof is 5 mm to 9 mm.
3. The hydrogen-dispensing hose according to claim 1 , wherein the diameter of the metal wire is 0.25 mm to 0.4 mm, the braid angle thereof is 45° to 55°, and the braid density of the wire braided layer is 70% or greater.
4. The hydrogen-dispensing hose according to claim 1 , wherein the diameter of the metal wire is 0.25 mm to 0.4 mm, the braid angle thereof is greater than 55° up to 60°, and the braid density of the wire braided layer is 70% or greater.
5. The hydrogen-dispensing hose according to claim 1 , wherein the high-strength fibers are polyparaphenylene benzobisoxazole fibers.
6. The hydrogen-dispensing hose according to claim 1 , wherein the hose is configured for use with an internal pressure acting on the hose of from 45 MPa to 87.5 MPa and with a temperature of hydrogen flowing through the hose of from −40° C. to −20° C.