Pyrolytic hybrid enamel
View Patent ↗A fired hybrid enamel coating is provided. The hybrid enamel coating is formed by firing an enamel composition on a substrate. The enamel composition includes at least a first glass frit, which is sintered to form the hybrid enamel coating. The hybrid enamel coating can be cleaned using aqualytic or pyrolytic cleaning methods, and does not discolor or lose gloss when subject to typical pyrolytic cleaning methods. The hybrid enamel coating does not require the application of highly caustic cleaners to remove the baked-on soils.
1. A composition for forming an enamel cover coat, the composition comprising at least a first glass frit comprising by weight:
from about 6.3% to about 7.4% Na 2 O;
from about 6.3% to about 7.4% K 2 O;
from about 9.9% to about 11.9% SiO 2 ;
from about 25.7% to about 29.7% P 2 O 5 ;
from about 12.7% to about 14.7% ZrO 2 ;
from about 16.8% to about 20.8% Al 2 O 3 ;
from about 0.6% to about 4.0% TiO 2 ;
from about 0.1% to about 2.0% Li 2 O;
from about 0.1% to about 2.0% BaO;
from about 0.1% to about 5.0% Co 2 O 3 ;
from about 0.1% to about 1.0% Cr 2 O 3 ;
from about 10.3% to about 14.3% B 2 O 3 ; and
from about 0.1% to about 3.0% F.
2. The composition according to claim 1 , further comprising a cobalt containing material selected from the group consisting of cobalt oxide, cobalt containing pigment, and a combination thereof.
3. A composition for forming an enamel cover coat, the composition comprising at least a first glass frit comprising by weight:
from about 5.2% to about 9.7% Na 2 O;
from about 1.5% to about 7.0% K 2 O;
from about 21.0% to about 23.7% SiO 2 ;
from about 16.9% to about 24.1% P 2 O 5 ;
from about 0% to about 6.8% ZrO 2 ;
from about 11.9% to about 20.7% Al 2 O 3 ;
from about 0% to about 2.1% TiO 2 ;
from about 0.3% to about 2.1% Li 2 O;
from about 2.1% to about 7.5% BaO;
from about 0% to about 1.8% CaO;
from about 0% to about 6.0% SrO;
from about 0.4% to about 2.0% F;
from about 5.6% to about 16.7% B 2 O 3 ;
from about 0% to about 0.2% MgO;
from about 0% to about 2.1% SnO;
from about 1.1% to about 1.6% Co 3 O 4 ;
from about 0.1% to about 1.3% Fe 2 O 3 ;
from about 0% to about 0.9% CuO;
from about 0.2% to about 1.9% MnO;
from about 0% to about 1.3% CeO 2 ;
from about 0% to about 1.0% Sb 2 O 3 ;
from about 0% to about 0.2% MoO 3 ; and
from about 0% to about 2.8% NO 2 .
4. A substrate having thereon a fired hybrid enamel cover coat, the cover coat comprising prior to firing, at least a first glass frit comprising by weight:
from about 6.3% to about 7.4% Na 2 O;
from about 6.3% to about 7.4% K 2 O;
from about 9.9% to about 11.9% SiO 2 ;
from about 25.7% to about 29.7% P 2 O 5 ;
from about 12.7% to about 14.7% ZrO 2 ;
from about 16.8% to about 20.8% Al 2 O 3 ;
from about 0.6% to about 4.0% TiO 2 ;
from about 0.1% to about 2.0% Li 2 O;
from about 0.1% to about 2.0% BaO;
from about 0.1% to about 5.0% Co 2 O 3 ;
from about 0.1% to about 1.0% Cr 2 O 3 ;
from about 10.3% to about 14.3% B 2 O 3 ; and
from about 0.1% to about 3.0% F.
5. The substrate according to claim 4 , further comprising a cobalt containing material selected from the group consisting of cobalt oxide, cobalt containing pigment, and a combination thereof.
6. A substrate having thereon a fired hybrid enamel cover coat, the cover coat comprising prior to firing, at least the composition according to claim 3 .
7. The substrate of claim 6 , wherein the substrate comprises an interior surface of an oven.
8. The substrate of claim 6 , wherein the cover coat further includes prior to firing, a second glass frit blended with the first glass frit.
9. A method of forming a hybrid enamel cover coat on a substrate from which baked-on food can be removed with aqualysis or pyrolysis and without requiring highly alkaline cleaners, the method comprising:
providing a pre-fired enamel composition including at least the composition according to claim 1 ,
depositing the enamel composition on a substrate, and
firing the enamel composition thereby sintering the at least first glass frit and thereby forming a hybrid enamel cover coat on the substrate.
10. A method of forming a hybrid enamel cover coat on a substrate from which baked-on food can be removed with aqualysis or pyrolysis and without requiring highly alkaline cleaners, the method comprising:
providing a pre-fired enamel composition including at least the composition according to claim 3 ,
depositing the enamel composition on a substrate, and
firing the enamel composition thereby sintering the pre-fired enamel composition and thereby forming a hybrid enamel cover coat on the substrate.
11. The method of claim 10 , further comprising providing a ground coat composition, depositing the ground coat composition on the substrate, and firing the ground coat composition to thereby form a ground coat enamel on the substrate.
12. A household appliance including a surface that is at least partially coated with the enamel cover coat formed by firing the composition of claim 1 .
13. A household appliance including the substrate of claim 6 .