Drug-eluting medical implants
Disclosed are medical implants for placement within a lumen of a patient. The implants comprise a polymer and drug-coated metal structure having a tubular configuration and designed to deliver the drug to target tissue at tailored linear drug elution rate.
1. A coated stent comprising (a) a tubular metallic substrate, (b) a first coating at least partially covering said substrate, said first coating comprising a first biodegradable polymer or blend of biodegradable polymers, and paclitaxel, wherein the total amount of paclitaxel in the stent is in the range of from 10 ug/10 mm length of stent to 80 ug/10 mm length of stent, and (c) a second coating at least partially covering said first coating, said second coating comprising a second biodegradable polymer or blend of biodegradable polymers, said second coating not containing a therapeutic agent,
wherein said first biodegradable polymer or blend of biodegradable polymers is the same or different from the second biodegradable polymer or blend of biodegradable polymers; and
wherein the first coating thickness is from 1 to 15 microns and the second coating thickness is from 1 to 35 microns.
2. The coated stent of claim 1 , wherein the first coating is configured to release a quantity of paclitaxel equal to 12.5 ng/mm 2 of stent surface area per day or less, during a period of from one to four days of submersion in a pH 7.4 phosphate-buffered saline buffer solution containing 2 wt % sodium dodecyl sulfate at 37° C. under action of a rotary shaker, when the buffer solution is removed completely weekly for paclitaxel quantification and replaced with fresh buffer solution.
3. A coated stent comprising (a) a tubular metallic substrate, (b) a first coating at least partially covering said substrate, said coating comprising a blend of poly(L-lactide-co-c-caprolactone) (PLCL), poly(L-lactide) (PLA), and paclitaxel and (c) a second coating at least partially covering said first coating, said second coating comprising PLCL and PLA, wherein the first coating comprises 10 to 99 wt percent of PLCL, 1 to 90 wt percent of PLA and paclitaxel and wherein said second coating does not contain a therapeutic agent, wherein the total amount of paclitaxel in the stent is in the range of from 10 ug/10 mm length of stent to 80 ug/10 mm length of stent.
4. The coated stent of claim 3 , wherein the first coating is configured to release paclitaxel such that the quantity of paclitaxel released, based on a total amount of paclitaxel in the coated stent, ranges from 2% to 4% each week from 6 weeks to 20 weeks of submersion in a pH 7.4 phosphate-buffered saline buffer solution containing 2 wt % sodium dodecyl sulfate at 37° C. under action of a rotary shaker, when the buffer solution is removed weekly for paclitaxel quantification and replaced with fresh buffer solution.
5. The coated stent of claim 3 , wherein said tubular body comprises at least one strand, the at least one strand forming a plurality of intersections at which portions of the at least one strand overlap with each other.
6. The coated stent of claim 5 , wherein the helical metallic strands comprise nitinol.
7. The coated stent of claim 3 , wherein the PLCL has a molar percentage of lactide ranging from 60% to 80% and a molar percentage of caprolactone ranging from 20% to 40%.
8. The coated stent of claim 3 , wherein the weight ratio of PLCL to PLA in each of the first coating and the second coating ranges from 15:85 to 35:65.
9. The coated stent of claim 3 , wherein the weight ratio of PLCL to PLA in each of the first coating and the second coating ranges from 40:60 to 60:40.
10. The coated stent of claim 3 , wherein the weight ratio of PLCL to PLA in each of the first coating and the second coating ranges from 45:55 to 55:45.