Tissue-engineered constructs
The present invention provides constructs including a tubular biodegradable polyglycolic acid scaffold, wherein the scaffold may be coated with extracellular matrix proteins and substantially acellular. The constructs can be utilized as an arteriovenous graft, a coronary graft, a peripheral artery bypass conduit, or a urinary conduit. The present invention also provides methods of producing such constructs.
1. A tubular scaffold comprising tubular biodegradable non-woven polyglycolic acid wherein the density of the polyglycolic acid is 45 mg/cc to 75 mg/cc and said density is uniform across the entire tubular scaffold, wherein the thickness of the polyglycolic acid is 0.8 to 1.2 mm and wherein the scaffold comprises polyglycolic acid fibers and the thickness of the fibers within the polyglycolic acid is 5 to 20 μm, and wherein the scaffold is substantially free of heavy metal contaminants, wherein the tubular scaffold is an ex vivo cell culture tubular scaffold.
2. The scaffold of claim 1 , wherein the length of the scaffold is 1 cm to 100 cm.
3. The scaffold of claim 1 , wherein the length of the scaffold is 10 cm to 40 cm.
4. The scaffold of claim 1 , wherein the inner diameter of the scaffold is 3 mm to 6 mm.
5. The scaffold of claim 1 , wherein the scaffold comprises trace amounts of heavy metal contaminants selected from the group consisting of: aluminum, barium, calcium, iodine, lanthanum, magnesium, nickel, potassium and zinc.
6. The scaffold of claim 1 , wherein the scaffold comprises non-biodegradable supports at each end.
7. A composition comprising
(a) a tubular scaffold comprising biodegradable non-woven polyglycolic acid, wherein the density of the polyglycolic acid is 45 mg/cc to 75 mg/cc and said density is uniform across the entire tubular scaffold, wherein the thickness of the polyglycolic acid is 0.8 to 1.2 mm and wherein the scaffold comprises polyglycolic acid fibers and the thickness of the fibers within the polyglycolic acid is 5 to 20 μm, wherein the tubular scaffold is an ex vivo cell culture tubular scaffold, and wherein the scaffold is substantially free of heavy metal contaminants;
(b) human cells seeded on the scaffold, and
(c) cell culture medium.
8. The composition of claim 7 wherein the cell culture medium comprises human serum.
9. The composition of claim 7 wherein the human cells comprise smooth muscle cells.
10. The composition of claim 7 wherein the human cells seeded on the scaffold are passaged less than 10 times when seeded.
11. The composition of claim 7 , wherein the length of the scaffold is 1 cm to 100 cm.
12. The composition of claim 7 , wherein the length of the scaffold is 10 cm to 40 cm.
13. The composition of claim 7 , wherein the inner diameter of the scaffold is 3 mm to 6 mm.
14. The composition of claim 7 , wherein the scaffold comprises non-biodegradable supports at each end.