Multi-ply bath tissue with temporary wet strength resin and/or a particular lignin content
A multi-ply bath tissue includes cellulosic microfibers and wood pulp fibers. The bath tissue has sufficient temporary wet strength resin to provide an initial Finch Cup cross-machine direction (CD) wet tensile of from about 2.5 to about 20 g/3 in. per pound of basis weight, decaying to less than 65% of the initial value in less than 15 minutes after immersion of the tissue in water, and a caliper of at least 5 mils per 8 sheets per pound of basis weight. At least one of the plies includes a plurality of fiber-enriched hollow domed regions having a relatively high basis weight, a plurality of connecting regions having a relatively lower basis weight forming a network interconnecting the fiber-enriched hollow domed regions of the sheet, and a plurality of transition regions transitioning from the connecting regions into the fiber-enriched hollow domed regions.
1. A multi-ply bath tissue comprising:
(A) a percentage by weight of cellulosic microfibers; and
(B) a percentage by weight of wood pulp fibers, the multi-ply bath tissue having:
(a) sufficient temporary wet strength resin to provide an initial Finch Cup cross-machine direction (CD) wet tensile of from about 2.5 to about 20 g/3 in. per pound of basis weight, the initial Finch Cup CD wet tensile decaying to less than 65% of the initial value in less than 15 minutes after immersion of the tissue in water; and
(b) a caliper of at least 5 mils per 8 sheets per pound of basis weight, wherein at least one of the plies comprises:
(i) a plurality of fiber-enriched hollow domed regions having a relatively high basis weight;
(ii) a plurality of connecting regions having a relatively lower basis weight forming a network interconnecting the fiber-enriched hollow domed regions of the sheet; and
(iii) a plurality of transition regions transitioning from the connecting regions into the fiber-enriched hollow domed regions.
2. The multi-ply bath tissue of claim 1 , having an opacity of at least about 2.5 MacBeth Opacity Units per pound of basis weight.
3. The multi-ply bath tissue of claim 1 , comprising from about 5% to about 25% cellulosic microfiber and from about 75% to about 85% wood pulp fibers.
4. The multi-ply bath tissue of claim 1 , comprising two substantially unembossed plies and one embossed ply.
5. The multi-ply bath tissue of claim 1 , comprising one substantially unembossed ply and two embossed plies.
6. The multi-ply bath tissue of claim 1 , comprising overall from at least about 5% up to about 50% of cellulosic microfiber (CMF) by weight and from about 50% to about 95% of wood pulp fibers, the multi-ply bath tissue comprising three plies, at least one of the plies comprising at least one stratum comprising from about 15% to about 50% of cellulosic microfiber, the multi-ply bath tissue having an eight sheet caliper of at least about 5.25 mils per lb of basis weight for a 3000 sq foot ream, a breaking modulus of between 2.5 and 3.5 g/% stretch per pound of basis weight, a CD wet tensile of between 3.5 and 18 g/3 in. per pound of basis weight, and a geometric mean (GM) dry tensile (GMT) of between 30 and 60 g/3 in. per pound of basis weight.
7. The multi-ply bath tissue of claim 6 , wherein (i) the ply comprising the plurality of fiber-enriched hollow domed regions, the plurality of connecting regions, and the plurality of transition regions is a ply other than an interior ply, and (ii) the at least one of the plies comprising the at least one stratum comprising from about 15% to about 50% of cellulosic microfiber is disposed such that the stratum defines an exterior surface of the multi-ply bath tissue.
8. The multi-ply bath tissue of claim 6 , wherein at least two of the three plies comprise a plurality of fiber-enriched hollow domed regions having a relatively high basis weight, a plurality of connecting regions of a relatively lower basis weight forming a network interconnecting the fiber-enriched hollow domed regions of a sheet of the bath tissue, and a plurality of transition regions with upwardly and inwardly inflected consolidated fibrous regions transitioning from the connecting regions into the fiber-enriched hollow domed regions.
9. The multi-ply bath tissue of claim 6 , wherein each of the three plies comprises a plurality of fiber-enriched hollow domed regions having a relatively high basis weight, a plurality of connecting regions of a relatively lower basis weight forming a network interconnecting the fiber-enriched hollow domed regions of the sheet, and a plurality of transition regions with upwardly and inwardly inflected consolidated fibrous regions transitioning from the connecting regions into the fiber-enriched hollow domed regions.
10. The multi-ply bath tissue of claim 1 , wherein the fiber-enriched hollow domed regions in the plurality of fiber-enriched hollow domed regions are provided in an interpenetrating staggered array.
11. The multi-ply bath tissue of claim 1 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 35 mm 2 .
12. The multi-ply bath tissue of claim 1 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 30 mm 2 .
13. The multi-ply bath tissue of claim 1 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 25 mm 2 .
14. The multi-ply bath tissue of claim 1 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 20 mm 2 .
15. The multi-ply bath tissue of claim 1 , wherein, when tested according to the Dry Lint Test, the ΔL* value is less than 6.0.
16. The multi-ply bath tissue of claim 1 , wherein, when tested according to the Dry Lint Test, the ΔL* value is less than 5.0.
17. The multi-ply bath tissue of claim 1 , wherein, when tested according to the Dry Lint Test, the ΔL* value is less than 4.5.
18. The multi-ply bath tissue of claim 1 , wherein, when tested according to the Dry Lint Test, the ΔL* value is less than 4.25.
19. The multi-ply bath tissue of claim 1 , wherein the plies are joined to each other by knurling.
20. The multi-ply bath tissue of claim 1 , wherein the plies are embossed with a pattern having primarily points to the inside and are joined by glue-lamination.
21. The multi-ply bath tissue of claim 1 , comprising three plies of tissue, wherein two plies are embossed, one ply is unembossed, and the plies are joined by knurling, in which knurled regions are arranged in a meandering path.
22. The multi-ply bath tissue of claim 1 , comprising three plies of tissue, wherein two plies are unembossed, one ply is embossed, and the plies are joined by knurling, in which knurled regions are arranged in a meandering path.
23. The multi-ply bath tissue of claim 1 , comprising three plies of tissue, wherein two plies are embossed, one ply is unembossed, and the plies are joined by knurling, wherein knurled regions are arranged in a meandering path and an outermost stratum of a lower ply has substantially the same composition as that of an outermost stratum of an upper ply.
24. The multi-ply bath tissue of claim 1 , having a geometric mean (GM) dry tensile of from about 17 to about 80 g/3 in. per pound basis weight.
25. The multi-ply bath tissue of claim 1 , having a CD dry tensile of between about 30 to about 60 g/3 in. per pound of basis weight.
26. A multi-ply bath tissue comprising:
(A) a percentage by weight of cellulosic microfibers; and
(B) a percentage by weight of wood pulp fibers,
the multi-ply bath tissue having sufficient temporary wet strength resin to provide an initial Finch Cup cross-machine (CD) wet tensile of from about 2.5 to about 20 g/3 in. per pound of basis weight, the initial Finch Cup CD wet tensile decaying to less than 75% of the initial value in less than 1 hour after immersion of the tissue in water,
wherein at least one of the plies, other than an interior ply, comprises:
(i) a plurality of fiber-enriched hollow domed regions having a relatively high basis weight;
(ii) a plurality of connecting regions having a relatively lower basis weight forming a network interconnecting the fiber-enriched hollow domed regions of the sheet; and
(iii) a plurality of transition regions transitioning from the connecting regions into the fiber-enriched hollow domed regions.
27. The multi-ply bath tissue of claim 26 , having a geometric mean (GM) dry tensile of from about 17 to 80 g/3 in. per pound of basis weight.
28. The multi-ply bath tissue of claim 26 , having a geometric mean (GM) breaking modulus of between 1.5 to 6.5 g/% stretch per pound of basis weight.
29. The multi-ply bath tissue of claim 26 , having a CD dry tensile of between about 2 to about 30 g/3 in. per pound of basis weight.
30. The multi-ply bath tissue of claim 26 , having an opacity of at least about 2.0 MacBeth Opacity Units per pound of basis weight.
31. A multi-ply bath tissue comprising:
(A) a percentage by weight of cellulosic microfibers; and
(B) a percentage by weight of wood pulp fibers,
wherein a percentage by weight of the tissue comprises eucalyptus fibers having a lignin content of at least about 20%, and
wherein the multi-ply bath tissue has sufficient temporary wet strength resin to provide an initial Finch Cup cross-machine direction (CD) wet tensile of from about 2.5 to about 20 g/3 in. per pound of basis weight, the initial Finch Cup CD wet tensile decaying to less than 65% of the initial value in less than one half hour after immersion of the tissue in water.
32. The multi-ply bath tissue of claim 31 , having a caliper of at least 4 mils per 8 sheets per pound of basis weight.
33. The multi-ply bath tissue of claim 31 , having a geometric mean (GM) dry tensile of from about 35 to 80 g/3 in. per pound of basis weight.
34. The multi-ply bath tissue of claim 31 , having a CD dry tensile of between about 2 to about 30 g/3 in. per pound of basis weight.
35. The multi-ply bath tissue of claim 31 , having a caliper of at least 4.5 mils per 8 sheets per pound of basis weight.
36. The multi-ply bath tissue of claim 31 , having a caliper of at least 5 mils per 8 sheets per pound of basis weight.
37. The multi-ply bath tissue of claim 31 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 35 mm 2 .
38. The multi-ply bath tissue of claim 31 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 30 mm 2 .
39. The multi-ply bath tissue of claim 31 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 25 mm 2 .
40. The multi-ply bath tissue of claim 31 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 20 mm 2 .
41. The multi-ply bath tissue of claim 31 , having an opacity of at least about 2.5 MacBeth Opacity Units per pound of basis weight.
42. The multi-ply bath tissue of claim 31 , comprising from about 3% to about 10% cellulosic microfiber and from about 75% to about 85% wood pulp fibers.
43. The multi-ply bath tissue of claim 31 , comprising two substantially unembossed plies and one embossed ply.
44. The multi-ply bath tissue of claim 31 , comprising one substantially unembossed ply and two embossed plies.
45. The multi-ply bath tissue of claim 31 , comprising at least three plies, at least first and second plies of which comprise from about 3% to about 25% of cellulosic microfiber, up to about 50% alkaline peroxide mechanical pulp (APMP) eucalyptus and from about 75% to about 97% of wood pulp fibers.
46. The multi-ply bath tissue of claim 45 having:
(a) an overall basis weight of between 22 and 36 lbs per 3000 sq ft ream;
(b) an eight sheet caliper of at least about 5.25 mils per lb of basis weight for a 3000 sq foot ream;
(c) a breaking modulus of between 2.5 and 3.5 g/% stretch per pound of basis weight;
(d) a CD wet tensile of between 3 and 18 g/3 in. per pound of basis weight; and
(e) a geometric mean tensile (GMT) of between 40 and 70 g/3 in. per pound of basis weight.
47. The multi-ply bath tissue of claim 46 , wherein the percentage of eucalyptus APMP in the third ply is:
(i) greater than at least about 20%;
(ii) greater than the percentage of eucalyptus APMP in the first ply; and
(iii) exceeds the percentage of eucalyptus APMP in the first ply by an amount that is at least 20% of the weight of eucalyptus APMP in the first ply, if any.
48. The multi-ply bath tissue of claim 45 , wherein at least one of the plies comprises a web having a plurality of fiber-enriched hollow domed regions having a relatively high basis weight, a plurality of connecting regions having a relatively lower basis weight forming a network interconnecting the fiber-enriched hollow domed regions of the sheet, and a plurality of transition regions with upwardly and inwardly inflected consolidated fibrous regions transitioning from the connecting regions into the fiber-enriched hollow domed regions.
49. The multi-ply bath tissue of claim 48 , wherein the ply comprising the plurality of fiber-enriched hollow domed regions, the plurality of connecting regions, and the plurality of transition regions is a ply other than an interior ply.
50. The multi-ply bath tissue of claim 48 , wherein the fiber-enriched hollow domed regions in the plurality of fiber-enriched hollow domed regions are provided in an interpenetrating staggered array.
51. The multi-ply bath tissue of claim 45 , wherein at least two of the three plies comprise a plurality of fiber-enriched hollow domed regions having a relatively high basis weight, a plurality of connecting regions having a relatively lower basis weight forming a network interconnecting the fiber-enriched hollow domed regions of the sheet, and a plurality of transition regions with upwardly and inwardly inflected consolidated fibrous regions transitioning from the connecting regions into the fiber-enriched hollow domed regions.
52. The multi-ply bath tissue of claim 45 , wherein each of the three plies comprises a plurality of fiber-enriched hollow domed regions having a relatively high basis weight, a plurality of connecting regions having a relatively lower basis weight forming a network interconnecting the fiber-enriched hollow domed regions of the sheet, and a plurality of transition regions with upwardly and inwardly inflected consolidated fibrous regions transitioning from the connecting regions into the fiber-enriched hollow domed regions.
53. The multi-ply bath tissue of claim 45 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 35 mm 2 .
54. The multi-ply bath tissue of claim 45 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 30 mm 2 .
55. The multi-ply bath tissue of claim 45 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 25 mm 2 .
56. The multi-ply bath tissue of claim 45 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 20 mm 2 .
57. The multi-ply bath tissue of claim 45 , wherein, when tested according to the Dry Lint Test, the ΔL* value is less than 6.0.
58. The multi-ply bath tissue of claim 45 , wherein, when tested according to the Dry Lint Test, the ΔL* value is less than 5.5.
59. The multi-ply bath tissue of claim 45 , wherein, when tested according to the Dry Lint Test, the ΔL* value is less than 5.0.
60. The multi-ply bath tissue of claim 45 , wherein the plies are joined to each other by knurling.
61. The multi-ply bath tissue of claim 45 , wherein the plies are embossed in a pattern having primarily points to the inside and are joined by glue-lamination.
62. The multi-ply bath tissue of claim 45 , comprising three plies of tissue, wherein two plies are embossed, one ply is unembossed, and the plies are joined by knurling, wherein knurled regions are arranged in a meandering path.
63. The multi-ply bath tissue of claim 45 , comprising three plies of tissue, wherein two plies are unembossed, one ply is embossed, and the plies are joined by knurling, wherein knurled regions are arranged in a meandering path.
64. The multi-ply bath tissue of claim 46 , comprising two plies of tissue, wherein one ply is embossed, one ply is unembossed, and the plies are joined by knurling, wherein knurled regions are arranged in a meandering path.
65. A multi-ply bath tissue comprising:
(A) a percentage by weight of cellulosic microfibers; and
(B) a percentage by weight of wood pulp fibers,
wherein a percentage by weight of the tissue comprises eucalyptus fibers having a lignin content of at least about 20%, an ISO brightness of at least about 84, a Canadian Standard Freeness (CSF) of at least about 400 ml, a bulk of between 2.2 and 4.2 cc/g, and a breaking length of between about 1.2 and 4.7 km, and
wherein the multi-ply bath tissue has sufficient temporary wet strength resin to provide an initial Finch Cup cross-machine direction (CD) wet tensile of from about 2.5 g/3 in. to about 20 g/3 in. per pound of basis weight, the initial Finch Cup CD wet tensile decaying to less than 65% of the initial value in less than one hour after immersion in water.
66. The multi-ply bath tissue of claim 65 , wherein at least one of the plies, other than an interior ply, comprises:
(a) a plurality of fiber-enriched hollow domed regions having a relatively high basis weight;
(b) a plurality of connecting regions having a relatively lower basis weight forming a network interconnecting the fiber-enriched hollow domed regions of the sheet; and
(c) a plurality of transition regions transitioning from the connecting regions into the fiber-enriched hollow domed regions.
67. The multi-ply bath tissue of claim 65 , wherein at least 50% of the eucalyptus fibers having a lignin content of at least about 20% are never dried fibers.
68. The multi-ply bath tissue of claim 65 , having a geometric mean (GM) dry tensile of from about 25 to 80 g/3 in. per pound of basis weight.
69. The multi-ply bath tissue of claim 65 , having a breaking modulus of between 2.5 and 3.5 g/% stretch per pound of basis weight.
70. The multi-ply bath tissue of claim 65 , having a cross-machine direction (CD) dry tensile of between about 30 to about 60 g/3 in. per pound of basis weight.
71. The multi-ply bath tissue of claim 65 , having an opacity of at least about 2.5 MacBeth Opacity Units per pound of basis weight.
72. A multi-ply bath tissue product comprising:
(A) an upper stratified ply comprising two strata, an outer stratum and an inner stratum,
(a) the outer stratum comprising a blend of at least about 30% to about 70% kraft fiber and at least 30% to about 70% by weight of eucalyptus kraft; and
(b) the inner stratum comprising at least about 50% fibers having a lignin content of at least about 20% by weight;
(B) an interior ply comprising:
(a) a percentage by weight of fibers having a lignin content of at least about 20% by weight; and
(b) a percentage by weight of bleached softwood kraft fibers; and
(C) a lower stratified ply comprising two strata, a first stratum and a second stratum,
(a) the first stratum comprising from at least about 30% to about 70% kraft fiber and from about 30% to about 70% by weight of eucalyptus kraft; and
(b) the second stratum comprising at least about 50% fibers having a lignin content of at least about 20% by weight,
wherein at least one of the plies comprises:
(i) a plurality of fiber-enriched hollow domed regions having a relatively high basis weight;
(ii) a plurality of connecting regions having a relatively lower basis weight forming a network interconnecting the fiber-enriched hollow domed regions of the sheet; and
(iii) a plurality of transition regions transitioning from the connecting regions into the fiber-enriched hollow domed regions.
73. The multi-ply bath tissue product of claim 72 , wherein at least 50% of the fibers have a lignin content of at least about 20% are never dried fibers.
74. The multi-ply bath tissue product of claim 73 , wherein the outer stratum of the upper stratified ply comprises at least about 8% by weight of individualized regenerated cellulosic microfiber.
75. The multi-ply bath tissue product of claim 73 , wherein the outer stratum of the upper stratified ply comprises at least about 8% by weight of individualized regenerated cellulosic microfiber having a number average diameter of at most about 2 microns.
76. The multi-ply bath tissue product of claim 72 , wherein the interior ply and the upper stratified ply have been joined by being embossed together.
77. The multi-ply bath tissue product of claim 76 , wherein the fibrous composition of the upper stratified ply is substantially the same as the fibrous composition of the lower stratified ply.
78. The multi-ply bath tissue product of claim 76 , wherein the depth of emboss of the lower stratified ply is less than 50% of the depth of emboss of the upper stratified ply.
79. The multi-ply bath tissue product of claim 76 , wherein the depth of emboss of the lower stratified ply is less than 80% of the depth of emboss of the upper stratified ply.
80. The multi-ply bath tissue product of claim 72 , wherein the outer stratum of the upper stratified ply comprises at least about 8% by weight of individualized regenerated cellulosic microfiber having a number average diameter of at most about 2 microns.
81. The multi-ply bath tissue product of claim 76 , wherein the lower stratified ply is generally unembossed.
82. The multi-ply bath tissue product of claim 81 , wherein the outer stratum of the upper stratified ply comprises at least about 5% by weight of individualized regenerated cellulosic microfiber having a number average diameter of at most about 1 micron.
83. The multi-ply bath tissue product of claim 72 , wherein the fibrous composition of the upper stratified ply is substantially the same as the fibrous composition of the lower stratified ply.
84. The multi-ply bath tissue product of claim 72 , wherein the outer stratum of the upper stratified ply further comprises at least about 5% by weight of individualized regenerated cellulosic microfiber having a diameter of no more than about 5 microns and passing a screen of about 14 mesh.
85. The multi-ply bath tissue product of claim 72 , wherein the outer stratum of the upper stratified ply further comprises at least about 5% by weight of individualized regenerated cellulosic microfiber having a number average diameter of no more than about 4 microns and a number average length of between about 50 microns and 2000 microns.
86. The multi-ply bath tissue product of claim 72 , wherein the outer stratum of the upper stratified ply further comprises at least about 10% by weight of individualized regenerated cellulosic microfiber having a number average diameter of at most about 4 microns and a number average length of between about 50 microns and 2000 microns.
87. The multi-ply bath tissue product of claim 72 , wherein the outer stratum of the upper stratified ply further comprises at least about 10% by weight of individualized regenerated cellulosic microfiber having a number average diameter of at most about 2 microns and a number average length of between about 50 microns and 2000 microns.
88. The multi-ply bath tissue product of claim 72 , wherein the outer stratum of each of the upper stratified ply and the lower stratified ply further comprises at least about 5% by weight of individualized regenerated cellulosic microfiber having a number average diameter of at most about 4 microns and a number average length of between about 50 microns and 2000 microns.
89. The multi-ply bath tissue product of claim 72 , wherein each of the inner stratum of the upper stratified ply and the second stratum of the lower stratified ply comprises at least about 70% eucalyptus fibers having a lignin content of at least about 20% by weight.
90. The multi-ply bath tissue product of claim 72 , wherein each of the inner stratum of the upper stratified ply and the second stratum of the lower stratified ply comprises debonder.
91. The multi-ply bath tissue product of claim 72 , wherein the interior ply is creped, exhibiting a percent crepe at least 3% greater than that of the upper stratified and lower stratified plies.
92. A multi-ply bath tissue product comprising:
(A) an upper stratified ply comprising two strata, an outer stratum and an inner stratum,
(a) the outer stratum comprising a blend of at least about 30% to about 70% kraft fiber and at least 30% to about 70% by weight of eucalyptus kraft and at least about 5% by weight of individualized regenerated cellulosic microfibers having a number average diameter of at most about 4 microns and a number average length of between about 50 microns and 2000 microns; and
(b) the inner stratum comprising at least about 70% fibers having a lignin content of at least about 20% by weight;
(B) an interior ply comprising:
(a) a percentage by weight of fibers having a lignin content of at least about 20% by weight; and
(b) a percentage by weight of bleached kraft fiber; and
(C) a lower stratified ply comprising at least two strata, including a first stratum and a second stratum,
(a) the first stratum comprising from at least about 30% to about 70% kraft fiber and from about 30% to about 70% by weight of eucalyptus kraft; and
(b) the second stratum comprising at least about 70% fibers having a lignin content of at least about 20% by weight.
93. The multi-ply bath tissue product of claim 92 , wherein at least one of the plies, other than the interior ply, comprises:
(i) a plurality of fiber-enriched hollow domed regions having a relatively high basis weight;
(ii) a plurality of connecting regions having a relatively lower basis weight forming a network interconnecting the fiber-enriched hollow domed regions of the sheet; and
(iii) a plurality of transition regions with transitioning from the connecting regions into the fiber-enriched hollow domed regions.
94. The multi-ply bath tissue product of claim 92 , wherein the upper stratified ply and the lower stratified ply have substantially identical fibrous compositions.
95. The multi-ply bath tissue product of claim 92 , exhibiting an ISO brightness of at least:
0.82×(% VCP)+0.795×(% RF)98+0.84×(% APMP+CFM),
where % VCP is the percentage of virgin chemical pulp in a sheet in an outer ply, % RF, the percentage of recycle fiber in the outer ply, and % APMP+CMF is the percentage of alkaline peroxide mechanical pulp (APMP) eucalyptus and regenerated cellulosic microfiber in the outer ply.
96. The multi-ply bath tissue product of claim 92 , wherein a major portion of the fibers in the interior ply is never dried fibers having a lignin content of at least about 23%, and exhibits an ISO brightness of at least about 82.
97. The multi-ply bath tissue product of claim 92 , wherein the weight percentage of chemically pulped softwood fiber in the three-ply bath tissue product is limited to at most 30% of the weight of the multi-ply bath tissue product.
98. The multi-ply bath tissue product of claim 92 , wherein a major portion of the fibers in the interior ply has a lignin content of at least about 23%, and exhibits an ISO brightness of at least about 82.
99. A multi-ply bath tissue comprising:
(A) a percentage by weight of cellulosic microfibers; and
(B) a percentage by weight of wood pulp fibers,
the multi-ply bath tissue having:
(a) sufficient temporary wet strength resin to provide an initial Finch Cup cross-machine direction (CD) wet tensile of from about 2.5 to about 20 g/3 in. per pound of basis weight, the initial Finch Cup CD wet tensile decaying to less than 65% of the initial value in less than 15 minutes after immersion of the tissue in water; and
(b) a caliper of at least 5 mils per 8 sheets per pound of basis weight.
100. The multi-ply bath tissue of claim 99 , wherein at least one of the plies comprises:
(i) a plurality of fiber-enriched hollow domed regions having a relatively high basis weight;
(ii) a plurality of connecting regions having a relatively lower basis weight forming a network interconnecting the fiber-enriched hollow domed regions of the sheet; and
(iii) a plurality of transition regions transitioning from the connecting regions into the fiber-enriched hollow domed regions.
101. The multi-ply bath tissue of claim 99 , having an opacity of at least about 2.5 MacBeth Opacity Units per pound of basis weight.
102. The multi-ply bath tissue of claim 99 , comprising from about 5% to about 25% of cellulosic microfiber and from about 75% to about 85% of wood pulp fibers.
103. The multi-ply bath tissue of claim 99 , having a basis weight of from about 20 to about 40 lbs per 3000 sq foot ream.
104. The multi-ply bath tissue of claim 99 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 35 mm 2 .
105. The multi-ply bath tissue of claim 99 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 30 mm 2 .
106. The multi-ply bath tissue of claim 99 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 25 mm 2 .
107. The multi-ply bath tissue of claim 99 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 20 mm 2 .
108. The multi-ply bath tissue of claim 99 , wherein, when tested according to the Dry Lint Test, the ΔL* value is less than 6.0.
109. The multi-ply bath tissue of claim 99 , wherein, when tested according to the Dry Lint Test, the ΔL* value is less than 5.0.
110. The multi-ply bath tissue of claim 99 , wherein, when tested according to the Dry Lint Test, the ΔL* value is less than 4.5.
111. The multi-ply bath tissue of claim 99 , wherein, when tested according to the Dry Lint Test, the ΔL* value is less than 4.25.
112. The multi-ply bath tissue of claim 99 , wherein the plies are joined to each other by knurling.
113. The multi-ply bath tissue of claim 99 , wherein the plies are embossed with a pattern having primarily points to the inside and are joined by glue-lamination.
114. The multi-ply bath tissue of claim 99 , having a geometric mean (GM) dry tensile of from about 17 to 80 g/3 in. per pound of basis weight.
115. The multi-ply bath tissue of claim 99 , having a CD dry tensile of between about 30 to about 60 g/3 in. per pound of basis weight.
116. A bath tissue comprising:
(A) a percentage by weight of cellulosic microfibers; and
(B) a percentage by weight of wood pulp fibers,
the bath tissue having sufficient temporary wet strength resin to provide an initial Finch Cup cross-machine direction (CD) wet tensile of from about 2.5 to about 20 g/3 in. per pound of basis weight, the initial Finch Cup CD wet tensile decaying to less than 65% of the initial value in less than 15 minutes after immersion in water,
wherein the bath tissue includes at least one ply comprising:
(i) a plurality of fiber-enriched hollow domed regions having a relatively high basis weight;
(ii) a plurality of connecting regions having a relatively lower basis weight forming a network interconnecting the fiber-enriched hollow domed regions of the sheet; and
(iii) a plurality of transition regions with upwardly and inwardly inflected consolidated fibrous regions transitioning from the connecting regions into the fiber-enriched hollow domed regions.
117. The bath tissue of claim 116 , having an opacity of at least about 2.5 MacBeth Opacity Units per pound of basis weight.
118. The bath tissue of claim 116 , comprising from about 5% to about 25% cellulosic microfiber and from about 75% to about 85% wood pulp fibers.
119. The bath tissue of claim 116 , having a basis weight of from about 22 to about 32 lbs per 3000 sq foot ream.
120. The bath tissue of claim 116 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 35 mm 2 .
121. The bath tissue of claim 116 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 30 mm 2 .
122. The bath tissue of claim 116 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 25 mm 2 .
123. The bath tissue of claim 116 , wherein, when tested according to the Wet Abrasion Lint Test, the Wet Abraded Lint Area is less than 20 mm 2 .
124. The bath tissue of claim 116 , wherein, when tested according to the Dry Lint Test, the ΔL* value is less than 6.0.
125. The bath tissue of claim 116 , wherein, when tested according to the Dry Lint Test, the ΔL* value is less than 5.0.
126. The bath tissue of claim 116 , wherein, when tested according to the Dry Lint Test, the ΔL* value is less than 4.5.
127. The bath tissue of claim 116 , wherein, when tested according to the Dry Lint Test, the ΔL* value is less than 4.25.
128. The bath tissue of claim 116 , having a geometric mean (GM) dry tensile of from about 17 to 80 g/3 in. per pound of basis weight.
129. The bath tissue of claim 116 , having a CD dry tensile of between about 30 to about 60 g/3 in. per pound of basis weight.
130. The bath tissue of claim 116 , having a caliper of at least 5 mils per 8 sheets per pound of basis weight.