Composite fiber for the reinforcement of concrete
Composite fibers and methods of manufacturing composite fibers for the reinforcement of concrete are provided. The composite fibers include fibers and a polymeric coating. The composite fibers have a length of about 10 mm to about 80 mm and an equivalent diameter from about 0.3 mm to about 2 mm. A method for reinforcing concrete using the composite fibers is further provided.
1. A method of reinforcing concrete, said method comprising:
preparing a viscous polymeric coating composition;
applying the viscous polymeric coating composition to a plurality of fibers to form a plurality of coated elements, each of said coated elements including one or more of said fibers;
exposing the coated elements to radiation which cures the viscous polymeric coating composition to form a plurality of composite fibers;
preparing a concrete; and
mixing the composite fibers in said concrete,
wherein said composite fibers are included in the concrete in an amount from 2 kg/m 3 to 75 kg/m 3 of said concrete.
2. The method of claim 1 , wherein said radiation is ultraviolet radiation.
3. The method of claim 1 , wherein said composite fibers have an equivalent diameter of 0.3 mm to 2 mm.
4. The method of claim 1 , wherein the viscous polymeric coating composition comprises at least one of a polyurethane, a polyester, and a vinylester.
5. The method of claim 1 , wherein the fibers comprise glass fiber.
6. The method of claim 1 , wherein the viscous polymeric coating composition is from 5 wt % to 50 wt % of the composite fiber.
7. The method of claim 1 , wherein the viscous polymeric coating composition is from 10 wt % to 30 wt % of the composite fiber.
8. The method of claim 1 , wherein said composite fibers are included in the concrete in an amount from 5 kg/m 3 to 25 kg/m 3 of said concrete.
9. The method of claim 1 , wherein said composite fibers have a length of 10 mm to 80 mm and an equivalent diameter from 0.3 mm to 2 mm.