Non-oriented electrical steel sheet
A non-oriented electrical steel sheet containing: in mass%, C: 0.005% or less; Si: 0.1% to 2.0%; Mn: 0.05% to 0.6%; P: 0.100% or less; and Al: 0.5% or less, in which 10 pieces/μm 3 or less in number density of non-magnetic precipitate AlN having an average diameter of 10 nm to 200 nm are contained, and an average magnetic flux density B50 in a rolling direction and in a direction perpendicular to rolling is 1.75 T or more. This non-oriented electrical steel sheet can be manufactured by two methods of a method of performing hot rolling annealing at a temperature of 750° C. to an Ac 1 transformation point and a method of setting a coil winding temperature to 780° C. or higher and performing self annealing.
1. A non-oriented electrical steel sheet, comprising:
in mass %,
C: 0.005% or less;
Si: 0.1% to 0.7%;
Mn: 0.05% to 0.6%;
P: 0.08% or less;
Al: 0.03% to 0.5%; and
a balance comprising Fe and inevitable impurities,
wherein:
10 pieces/μm 3 or less in number density of non-magnetic precipitate AIN having an average diameter of 10 nm to 200 nm are contained, a structure is made of ferrite grains containing no non-recrystallized structure, and an average grain diameter of the ferrite grains is 30μm to 92μm, and
an average magnetic flux density B50 in a rolling direction and in a direction perpendicular to rolling is 1.75 T or more.
2. The non-oriented electrical steel sheet according to claim 1 , further comprising:
in mass %, 0.05% to 0.2% of at least one of Sn and Sb.
3. The non-oriented electrical steel sheet according to claim 1 , further comprising:
in mass %, 0.0005% to 0.0030% of B.
4. The non-oriented electrical steel sheet according to claim 2 , further comprising:
in mass %, 0.0005% to 0.0030% of B.