Adhesives and related methods

1. A cure in place liquid comprising:

5-50 wt % of a bodying component comprising a pre-polymerized acrylic backbone base polymer having a molecular weight (Mw) of 5,000 to 1,000,000;

50-95 wt % of at least one structural diluent;

0.01-10 wt % of a curative; and

0-10 wt % stabilizer/process aid.

2. The cure in place liquid of claim 1 wherein the curative is selected from the group consisting of thermal catalysts, base catalysts, photoinitiators, radical initiators, and UV radical photoinitiators.

3. The cure in place liquid of claim 1 wherein the curative is a thermal catalyst.

4. The cure in place liquid of claim 1 wherein the curative is activatable by at least one of radiation, heat, moisture, pressure, ultrasound, exposure to chemical agents, and combinations thereof.

5. The cure in place liquid of claim 1 wherein the acrylic backbone base polymer has a Mw of 15,000 to 250,000.

6. The cure in place liquid of claim 5 wherein the acrylic backbone base polymer has a Mw of 15,000 to 100,000.

7. The cure in place liquid of claim 1 wherein the acrylic backbone base polymer has a Mw of 25,000 to 1,000,000.

8. The cure in place liquid of claim 1 wherein the structural diluent is selected from the group consisting of 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate (S-21), Bis[(3,4-epoxycyclohexyl)methyl]adipate (S-28), difunctional bisphenol A/epichlorohydrin derived liquid epoxy resin (Epon 828), Bisphenol A epoxy resin having a weight per epoxide of 235-263 g/eq as measured by ASTM D1652 (Epon 834), beta-(3,4-epoxycyclohexyl)ethyltrimethoxysilane (A-186), gamma-glycidoxypropyltrimethoxysilane (A-187), glycidyl ester of neodecanoic acid (EP-10), isocyanate-functional urethane acrylate (Desmolux D100), isocyanate-bearing urethane acrylate (Desmolux D200), aliphatic polyisocyanate (low-viscosity hexamethylene diisocyanate (HDI) biuret) (Desmodur N3200), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) biuret) (Desmodur N100), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) trimer) (Desmodur N3300), poly(propylene oxide) (PPO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, trimethylolpropane oxetane (TMPO), poly(ethylene oxide) (PEO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, ethyl hexyl oxetane (2EH oxetane), difunctional oxetane, trimethylolpropane triacrylate (TMPTA) of the following formula (5), tripropyleneglycol diacrylate (TPGDA) of the following formula (6), ethoxylated bisphenol A diacrylate of the following formula (7) in which n+m=3, ethoxylated trimethylolpropane triacrylate of the following formula (8), bisphenol A diglycidyl ether diacrylate of the following formula (9), 1,2-cyclic ethers, 1,3-cyclic ethers, 1,4-cyclic ethers, anhydrides, lactones, lactams, cyclic ethers, siloxanes, oxazolines, oxalidines, and bismaleimides;

9. The cure in place liquid of claim 1 wherein the structural diluent is selected from the group consisting of 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate (S-21), Bis[(3,4-epoxycyclohexyl)methyl]adipate (S-28), difunctional bisphenol A/epichlorohydrin derived liquid epoxy resin (Epon 828), Bisphenol A epoxy resin having a weight per epoxide of 235-263 g/eq as measured by ASTM D1652 (Epon 834), beta-(3,4-epoxycyclohexyl)ethyltrimethoxysilane (A-186), gamma-glycidoxypropyltrimethoxysilane (A-187), glycidyl ester of neodecanoic acid (EP-10), isocyanate-functional urethane acrylate (Desmolux D100), isocyanate-bearing urethane acrylate (Desmolux D200), aliphatic polyisocyanate (low-viscosity hexamethylene diisocyanate (HDI) biuret) (Desmodur N3200), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) biuret) (Desmodur N100), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) trimer) (Desmodur N3300), poly(propylene oxide) (PPO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, trimethylolpropane oxetane (TMPO), poly(ethylene oxide) (PEO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, ethyl hexyl oxetane (2EH oxetane), difunctional oxetane, ethoxylated bisphenol A diacrylate of the following formula (7) in which n+m=3, ethoxylated trimethylolpropane triacrylate of the following formula (8), bisphenol A diglycidyl ether diacrylate of the following formula (9), 1,2-cyclic ethers, 1,3-cyclic ethers, 1,4-cyclic ethers, anhydrides, lactones, lactams, cyclic ethers, siloxanes, oxazolines, oxalidines, and bismaleimides;

10. The cure in place liquid of claim 1 wherein the structural diluent is selected from the group consisting of 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate (S-21), Bis[(3,4-epoxycyclohexyl)methyl]adipate (S-28), difunctional bisphenol A/epichlorohydrin derived liquid epoxy resin (Epon 828), Bisphenol A epoxy resin having a weight per epoxide of 235-263 g/eq as measured by ASTM D1652 (Epon 834), beta-(3,4-epoxycyclohexyl)ethyltrimethoxysilane (A-186), gamma-glycidoxypropyltrimethoxysilane (A-187), glycidyl ester of neodecanoic acid (EP-10), isocyanate-functional urethane acrylate (Desmolux D100), isocyanate-bearing urethane acrylate (Desmolux D200), aliphatic polyisocyanate (low-viscosity hexamethylene diisocyanate (HDI) biuret) (Desmodur N3200), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) biuret) (Desmodur N100), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) trimer) (Desmodur N3300), poly(propylene oxide) (PPO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, trimethylolpropane oxetane (TMPO), poly(ethylene oxide) (PEO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, ethyl hexyl oxetane (2EH oxetane), difunctional oxetane, ethoxylated bisphenol A diacrylate of the following formula (7) in which n+m=3, ethoxylated trimethylolpropane triacrylate of the following formula (8), bisphenol A diglycidyl ether diacrylate of the following formula (9), 1,2-cyclic ethers, 1,3-cyclic ethers, 1,4-cyclic ethers, butyrolactone, valerolactone, caprolactone, methy-butyrolactone, butyrolactam, valerolactam, caprolactam, cyclic ethers, siloxanes, oxazolines, oxalidines, bismaleimides,

and lactones of the following formulas (10)-(12)

wherein n is 4 or 5, h, i, k, and m are independently 1 or 2 and each R is independently chosen from H or hydrocarbyl containing up to 12 carbon atoms.

11. The adhesive of claim 1 wherein the acrylic backbone base polymer includes an acrylic block polymer.

12. The adhesive of claim 11 wherein the acrylic block polymer includes two reactive functional end segments and one non-reactive middle segment.

13. The adhesive of claim 12 wherein the non reactive segment is non reactive with the reactive functional group of the reactive segments.

14. The adhesive of claim 12 wherein the reactive segments include one or more monomers of the non-reactive segment.

15. The adhesive of claim 11 wherein the acrylic block polymer includes one reactive functional end segment and one non-reactive middle segment.

16. The adhesive of claim 15 wherein the non-reactive segment is non-reactive with the reactive functional group of the reactive segment.

17. The adhesive of claim 15 wherein the reactive segment includes one or more monomers of the non-reactive segment.

18. A cure in place liquid comprising:

5-50 wt % of a bodying component comprising a pre-polymerized acrylic backbone base polymer having a molecular weight (Mw) of 5,000 to 1,000,000;

50-95 wt % of at least one structural diluent;

0.01-10 wt % of a curative; and

0-10 wt % stabilizer/process aid,

wherein the structural diluent is selected from the group consisting of 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate (S-21), Bis[(3,4-epoxycyclohexyl)methyl]adipate (S-28), difunctional bisphenol A/epichlorohydrin derived liquid epoxy resin (Epon 828), Bisphenol A epoxy resin having a weight per epoxide of 235-263 g/eq as measured by ASTM D1652 (Epon 834), beta-(3,4-epoxycyclohexyl)ethyltrimethoxysilane (A-186), gamma-glycidoxypropyltrimethoxysilane (A-187), glycidyl ester of neodecanoic acid (EP-10), isocyanate-functional urethane acrylate (Desmolux D100), isocyanate-bearing urethane acrylate (Desmolux D200), aliphatic polyisocyanate (low-viscosity hexamethylene diisocyanate (HDI) biuret) (Desmodur N3200), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) biuret) (Desmodur N100), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) trimer) (Desmodur N3300), poly(propylene oxide) (PPO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, trimethylolpropane oxetane (TMPO), poly(ethylene oxide) (PEO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, ethyl hexyl oxetane (2EH oxetane), difunctional oxetane, tripropyleneglycol diacrylate (TPGDA) of the following formula (6), ethoxylated bisphenol A diacrylate of the following formula (7) in which n+m=3, ethoxylated trimethylolpropane triacrylate of the following formula (8), bisphenol A diglycidyl ether diacrylate of the following formula (9), 1,2-cyclic ethers, 1,3-cyclic ethers, 1,4-cyclic ethers, anhydrides, lactones, lactams, cyclic ethers, siloxanes, oxazolines, oxalidines, and bismaleimides;

19. A cure in place liquid consisting of:

5-50 wt % of a bodying component comprising a pre-polymerized acrylic backbone base polymer having a molecular weight (Mw) of 5,000 to 1,000,000;

50-95 wt % of at least one structural diluent;

0.01-10 wt % of a curative; and

0-10 wt % stabilizer/process aid,

wherein the structural diluent is selected from the group consisting of 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate (S-21), Bis[(3,4-epoxycyclohexyl)methyl]adipate (S-28), difunctional bisphenol A/epichlorohydrin derived liquid epoxy resin (Epon 828), Bisphenol A epoxy resin having a weight per epoxide of 235-263 g/eq as measured by ASTM D1652 (Epon 834), beta-(3,4-epoxycyclohexyl)ethyltrimethoxysilane (A-186), gamma-glycidoxypropyltrimethoxysilane (A-187), glycidyl ester of neodecanoic acid (EP-10), isocyanate-functional urethane acrylate (Desmolux D100), isocyanate-bearing urethane acrylate (Desmolux D200), aliphatic polyisocyanate (low-viscosity hexamethylene diisocyanate (HDI) biuret) (Desmodur N3200), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) biuret) (Desmodur N100), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) trimer) (Desmodur N3300), poly(propylene oxide) (PPO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, trimethylolpropane oxetane (TMPO), poly(ethylene oxide) (PEO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, ethyl hexyl oxetane (2EH oxetane), difunctional oxetane, tripropyleneglycol diacrylate (TPGDA) of the following formula (6), ethoxylated bisphenol A diacrylate of the following formula (7) in which n+m=3, ethoxylated trimethylolpropane triacrylate of the following formula (8), bisphenol A diglycidyl ether diacrylate of the following formula (9), 1,2-cyclic ethers, 1,3-cyclic ethers, 1,4-cyclic ethers, anhydrides, lactones, lactams, cyclic ethers, siloxanes, oxazolines, oxalidines, and bismaleimides;