Pouch and film for a pouch
A film for use in the formation of a flexible package that has a first layer and a second layer that are laminated together to form a two layer laminate. The first layer is a base comprising polyethylene terephthalate, with at least one of the outer surface and the inner surface having a barrier layer disposed thereon. The second layer is a coextrusion having a core layer comprising an ethylene vinyl alcohol with an outer upper layer of a linear low density polyethylene and an outer lower layer of linear low density polyethylene.
1. A film for use in the formation of a flexible package comprising:
a first layer and a second layer, the first layer having an outer surface and an inner surface, and the second layer having an outer surface and an inner surface, the inner surface of the first layer laminated to the outer surface of the second layer to form a two layer laminate,
the first layer further comprising a base comprising polyethylene terephthalate, with at least one of the outer surface and the inner surface having a barrier layer disposed thereon; and
the second layer comprising a coextrusion having a core layer comprising an ethylene vinyl alcohol with an outer upper layer comprising linear low density polyethylene and an outer lower layer comprising linear low density polyethylene.
2. The film of claim 1 wherein the second layer further includes an upper tie layer between the upper outer layer and the core layer and a lower tie layer between the lower outer layer and the core layer, the upper tie layer and the lower tie layer each comprising a maleic anhydride modified linear low density polyethylene.
3. The film of claim 2 wherein the barrier layer comprises one of the group selected from: Aluminum Oxides (AlO x ), Silicone Oxides (SiO x ), polyvinyl alcohol (PVOH), polyvinylidene chloride (PVdC) and combinations of the foregoing.
4. The film of claim 3 wherein the first layer has a thickness of approximately 12 μm.
5. The film of claim 4 wherein the upper outer layer has a thickness of approximately 33 μm and the lower outer layer has a thickness of approximately 33 μm.
6. The film of claim 5 wherein the ethylene vinyl alcohol comprises 29 mol % ethylene.
7. The film of claim 6 wherein the core layer has a thickness of approximately 8 μm.
8. The film of claim 7 wherein the second layer has a thickness of approximately 89 μm.
9. The film of claim 8 wherein the upper outer layer and the lower outer layer are substantially identical.
10. The film of claim 1 wherein the film is substantially transparent.
11. A film for use in the formation of a flexible package comprising:
a first layer and a second layer, the first layer having an outer surface and an inner surface, and the second layer having an outer surface and an inner surface, the inner surface of the first layer laminated to the outer surface of the second layer to form a two layer laminate,
the first layer further comprising a base comprising polyethylene terephthalate, with at least one of the outer surface and the inner surface having a barrier layer disposed thereon, the first layer having a thickness of approximately 12 μm;
the second layer comprising a coextrusion having a thickness of approximately 89 μm, and having a core layer comprising a 29 mol % ethylene ethylene vinyl alcohol with an outer upper layer comprising linear low density polyethylene and an outer lower layer comprising linear low density polyethylene, with an upper tie layer between the upper outer layer and the core layer, and a lower tie layer between the lower outer layer and the core layer, the core layer having a thickness of approximately 8 μm, with each of the upper outer layer and the lower outer layer having a thickness of approximately 33 μm.
12. The film of claim 11 wherein the barrier layer comprises an Aluminum Oxide (AlO x ).
13. The film of claim 11 wherein the barrier layer comprises one of the group consisting of: Silicon Oxides (SiO x ), polyvinyl alcohol (PVOH), polyvinylidene chloride (PVdC) and combinations of the foregoing.
14. The film of claim 12 wherein the upper and lower tie layers comprise a maleic anhydride modified linear low density polyethylene.
15. The film of claim 14 wherein the first layer and the second layer are laminated with an adhesive.
16. The film of claim 11 wherein the oxygen transmission measured in cc/100 in 2 /day at 100% O 2 in a 50/50% relative humidity at 23° C. is less than 0.010.
17. The film of claim 11 wherein the oxygen transmission measured in cc/100 in 2 /day at 100% O 2 in a 50/50% relative humidity at 23° C. of the film after submersion in water at 95° C. for 10 minutes is less than 0.010.
18. A pouch comprising:
a front panel and a back panel sealed together with a seal to define a cavity, with a spout coupled to at least one of the front panel and the back panel, the spout having an opening providing communication into the cavity, wherein,
at least one of the front panel and the back panel are formed, at least partially from a film comprising:
a first layer and a second layer, the first layer having an outer surface and an inner surface, and the second layer having an outer surface and an inner surface, the inner surface of the first layer laminated to the outer surface of the second layer to form a two layer laminate,
the first layer further comprising a base comprising polyethylene terephthalate, with at least one of the outer surface and the inner surface having a barrier layer disposed thereon; and
the second layer comprising a coextrusion having a core layer comprising an ethylene vinyl alcohol with an outer upper layer comprising linear low density polyethylene and an outer lower layer comprising linear low density polyethylene.
19. The pouch of claim 18 further comprising a base gusset panel.