Inorganic fiber with improved shrinkage and strength
View Patent ↗An inorganic fiber containing silica and magnesia as the major fiber components and which further includes intended addition of lithium oxide to improve the thermal stability of the fiber. The inorganic fiber exhibits good thermal performance at 1260° C. and greater, low linear shrinkage, retains mechanical integrity after exposure to the use temperature, and exhibits low biopersistence in physiological fluids. Also provided are thermal insulation product forms prepared from a plurality of the inorganic fibers, methods of preparing the inorganic fiber and of thermally insulating articles using thermal insulation prepared from a plurality of the inorganic fibers.
1. An inorganic fiber consisting essentially of the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, greater than 0 to about 2% alumina and greater than 0 to about 0.45 weight percent lithium oxide, wherein said inorganic fiber has compression recovery of at least about 10% after exposure to a temperature of 1400° C. for 24 hours, exhibits a shrinkage of 5% or less at 1260° C. for 24 hours and a shrinkage of 10% or less at 1400° C. for 24 hours.
2. The inorganic fiber of claim 1 , consisting essentially of the fiberization product of about 65 to about 86 weight percent silica, about 14 to about 35 weight percent magnesia, and greater than 0 to about 0.35 weight percent lithium oxide.
3. The inorganic fiber of claim 1 , consisting essentially of the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide.
4. The inorganic fiber of claim 3 , consisting essentially of the fiberization product of about 70 to about 80 weight percent silica, about 20 to about 30 weight percent magnesia, and greater than 0 to about 0.35 weight percent lithium oxide.
5. The inorganic fiber of claim 1 , consisting essentially of the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, and greater than 0 to about 0.45 weight percent lithium oxide.
6. The inorganic fiber of claim 5 , consisting essentially of the fiberization product of about 75 to about 80 weight percent silica, about 20 to about 25 weight percent magnesia, and greater than 0 to about 0.35 weight percent lithium oxide.
7. The inorganic fiber of claim 1 , consisting essentially of the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide.
8. The inorganic fiber of claim 7 , consisting essentially of the fiberization product of about 76 to about 80 weight percent silica, about 20 to about 24 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide.
9. The inorganic fiber of claim 1 , consisting essentially of the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide.
10. The inorganic fiber of claim 9 , consisting essentially of the fiberization product of about 77 to about 80 weight percent silica, about 20 to about 23 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide.
11. The inorganic fiber of claim 1 , consisting essentially of the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, greater than 0 to about 0.45 weight percent lithium oxide.
12. The inorganic fiber of claim 11 , consisting essentially of the fiberization product of about 78 to about 80 weight percent silica, about 20 to about 22 weight percent magnesia, greater than 0 to about 0.35 weight percent lithium oxide.
13. An inorganic fiber containing article comprising at least one of bulk fiber, blankets, blocks, boards, caulking compositions, cement compositions, coatings, felts, mats, moldable compositions, modules, papers, pumpable compositions, putty compositions, sheets, tamping mixtures, vacuum cast shapes, vacuum cast forms, or woven textiles, braids, cloths, fabrics, ropes, tapes, sleeving, wicking, said fiber containing article comprising the fiberization product of claim 1 .