Ambient temperature decontamination of nuclear power plant component surfaces containing radionuclides in a metal oxide
A method for at least partially disrupting or removing radioactive deposits formed on a surface of a structure in a nuclear water reactor is disclosed. The method includes identifying the structure, taking the structure out of operational service, isolating the structure, contacting the surface of the structure with an aqueous solution, and adding an effective amount of an elemental metal in solid form to the aqueous solution. The effective amount includes an amount to at least partially disrupt or remove the radioactive deposits formed on the surface of the structure. The method is conducted at ambient temperature. The radioactive deposits include oxide-containing radionuclides deposited on the surface. The surface is a primary side structure in the nuclear water reactor.
1. A method for at least partially disrupting or removing radioactive deposits formed on a surface of a structure in a primary side of a nuclear water reactor, the method comprising:
identifying the structure;
taking the structure out of operational service;
isolating the structure from the remainder of the primary side;
contacting the surface of the structure with an aqueous solution while the structure is isolated from the remainder of the primary side;
adding an amount of an elemental metal in solid form to the aqueous solution, wherein the amount is effective to at least partially disrupt or remove the radioactive deposits formed on the surface of the structure; and
at least partially disrupting or removing the radioactive deposits formed on the surface utilizing the aqueous solution comprising the added elemental metal,
wherein the method is conducted at ambient temperature, and
wherein the radioactive deposits comprise oxide-containing radionuclides deposited on the surface.
2. The method of claim 1 , wherein the radioactive deposits include one or more materials selected from the group consisting of oxide scale and corrosion products.
3. The method of claim 1 , wherein the elemental metal is selected from the group consisting of metals with standard electrochemical potentials anodic to low alloy steel.
4. The method of claim 3 , wherein the electrochemical potential of the elemental metal is more active than the potential of low alloy steel in the galvanic series of metals and alloys.
5. The method of claim 1 , wherein the elemental metal is selected from the group consisting of zinc, aluminum, magnesium, beryllium, lithium, iron and mixtures thereof.
6. The method of claim 1 , wherein the elemental metal is zinc.
7. The method of claim 1 , wherein the elemental metal is in a form selected from the group consisting of slab, granular, powder, colloidal, and combinations thereof.
8. The method of claim 7 , wherein the elemental metal is in the colloidal form.
9. The method of claim 8 , wherein the colloidal form contains particles selected from the group consisting of micron-sized particles, nano-sized particles and combinations thereof.
10. The method of claim 1 , further comprising adding to the aqueous solution a material selected from the group consisting of sequestering agent, chelating agent and mixtures thereof.
11. The method of claim 10 , further comprising adding a dispersant to the aqueous solution.
12. The method of claim 1 , further comprising adding to the aqueous solution a material selected from the group consisting of an oxidizing agent, reducing agent and mixtures thereof.
13. The method of claim 1 , wherein the elemental metal is present in an amount from about 0.001 M to about 2 M based on volume of the aqueous solution.
14. The method of claim 1 , wherein the aqueous solution has a pH in a range from about 3.0 to about 13.
15. The method of claim 1 , wherein the nuclear water reactor is in a condition selected from the group consisting of layup and shutdown.
16. The method of claim 1 , wherein contacting comprises subjecting the surface of the structure to a technique selected from the group consisting of a recirculating flow of the aqueous solution and a static immersion of the aqueous solution.
17. The method of claim 1 , further comprising:
disassociating metal ions from the radioactive deposits;
precipitating the metal ions to form a precipitate; and
removing the precipitate by employing a process selected from the group consisting of filtration, ion exchange and reverse osmosis.
18. The method of claim 1 , further comprising at least one of purifying the disrupted and radioactive deposits, transferring said deposits to a containment sump, adding said deposits to a radioactive waste system and transporting said deposits to a location remote from the nuclear water reactor.
19. A method comprising,
taking a structure in a nuclear water reactor out of operational service;
contacting the surface of the structure with an aqueous solution comprising an elemental metal in an amount effective to at least partially disrupt or remove radioactive deposits formed on a surface of the structure, wherein the radioactive deposits comprise oxide-containing radionuclides deposited on the surface, wherein the elemental metal is in a form of slab, granular, powder, colloidal, or combinations thereof; and
at least partially disrupting or removing the radioactive deposits formed on the surface utilizing the aqueous solution,
wherein the method is conducted absent an external heat source applied to the structure.
20. A method for at least partially disrupting or removing radioactive deposits formed on a surface of a structure in a nuclear water reactor, the method comprising:
taking the structure out of operational service;
contacting the surface of the structure with an aqueous solution;
adding an amount of an elemental metal in solid form to the aqueous solution, wherein the amount is effective to at least partially disrupt or remove the radioactive deposits formed on the surface of the structure;
disassociating metal ions from the radioactive deposits;
precipitating the metal ions to form a precipitate; and
removing the precipitate by employing filtration, ion exchange, reverse osmosis, or a combination thereof;
wherein the method is conducted absent an external heat source applied to the structure.