Beta-phase indicator
A quick, non-destructive and inexpensive test is disclosed to determine whether a portion of a structure made of 5XXX Aluminum alloy is sensitized. Unlike the current sensitization tests, this test can be performed by non-skilled personnel without complicated procedures and equipment. Since the test is non-destructive, it does not require the removal material from the structure. This feature makes the test particularly attractive for in situ applications such as for use on existing structures like ships. The test requires the application of an indicating chemical to the surface of the material being tested. The indicating chemical has a pre-determined pH which may be either acidic or alkaline. The indicating chemical also contains an pH indicator of pre-determined value. After a short period of time has elapsed, the percentage of pH color change observed from the indicating chemical can be used to determine whether the sample is sensitized or not. It is also possible to obtain at least an approximation of the Degree of Sensitization of the structure using the test.
1. A method of determining whether or not a portion of a metallic structure comprising 5XXX Aluminum alloy is sensitized comprising the steps of:
cleaning the metallic structure portion to bare metal;
applying an indicating chemical combined with a pH indicator to the portion of the metallic structure comprising 5XXX Aluminum alloy;
allowing a pre-determined amount of time to pass;
and,
determining that said 5XXX Aluminum alloy is sensitized if a color change in the indicating chemical is observed within said pre-determined amount of time.
2. The method of claim 1 wherein the pH of the indicating chemical is less than or equal to 2.
3. The method of claim 1 wherein the pH of the indicating chemical is less than about 11 and greater than about 8.
4. The method of claim 1 wherein the pH of the indicating chemical is approximately 10.
5. The method of claim 1 wherein the metallic structure comprises a ship comprising 5XXX Aluminum alloy and the step of applying an indicating chemical to a portion of a metallic structure comprising 5XXX Aluminum alloy is performed in situ.
6. The method of claim 5 wherein the indicating chemical further comprises a thickening agent and wherein the step of applying an indicating chemical further comprises spraying the indicating chemical with said thickening agent therein upon a portion of the ship comprising 5XXX Aluminum alloy.
7. The method of claim 6 wherein the portion of the ship is a vertical bulkhead on a ship comprising 5XXX Aluminum alloy.
8. A method of determining the degree of sensitization of a portion of a metallic structure comprising 5XXX Aluminum alloy comprising the steps of:
cleaning the metallic structure portion to bare metal;
applying an indicating chemical combined with a pH indicator to the portion of the metallic structure comprising 5XXX Aluminum alloy:
allowing a pre-determined amount of time to pass;
further comprising plotting the color change in said indicating chemical against the amount of time necessary to obtain said color change and determining the degree of sensitization of the portion of the metallic structure comprising 5XXX Aluminum alloy from the plotting.
9. A method of determining the approximate degree of sensitization of a portion of a metallic structure comprising a particular 5XXX Aluminum alloy comprising the steps of:
cleaning said portion of said metallic structure to bare metal;
measuring the temperature of said portion of said metallic structure;
placing an indicating chemical with a pH indicator therein on said portion of said metallic structure;
allowing a certain amount of time to pass with said certain amount of time being selected based upon said measured temperature;
further comprising plotting the color change in said indicating chemical against the amount of time necessary to obtain said color change and determining the approximate degree of sensitization of the portion of the metallic structure comprising 5XXX Aluminum alloy from the plotting.