A solid surface comprises (i) a crosslinked acrylic or unsaturated polyester resin present in an amount no greater than 52 volume fraction percent, and (ii) no greater than 48 volume fraction percent of inorganic filler particles distributed evenly throughout the solid surface wherein (a) 95-99 volume fraction percent of the filler particles has a major dimension in the range of from 0.5 to no greater than 10 microns, (b) the D50 of the filler particles is from 0.5-2.5 microns, and (c) the D90 of the filler particles is equal to or less than 10 microns.
1. A solid surface comprising
(i) a crosslinked acrylic or unsaturated polyester resin present in an amount of from 45 to 80 volume fraction percent, and
(ii) from 25 to 55 volume fraction percent of filler particles consisting of alumina trihydrate or alumina or silica or talc or quartz, the particles being distributed evenly throughout the solid surface wherein
(a) 95-99 volume fraction percent of the filler particles has a major dimension in the range of from 0.5 to no greater than 10 microns,
(b) the D50 of the filler particles is from 0.5-2.5 microns, and
(c) the D90 of the filler particles is equal to or less than 10 microns.
2. The surface of claim 1 wherein the organic polymer component includes a coupling agent comonomer that will copolymerize with the resin and bond to the filler surface.
3. The surface of claim 1 further comprising decorative components selected from pigments and visible particulates, or a combination thereof.
4. The surface of claim 1 wherein the filler particles are alumina trihydrate.
5. The surface of claim 1 wherein the crosslinked acrylic resin includes a thermoset acrylic resin.
6. The surface of claim 1 wherein the crosslinked acrylic resin includes methyl methacrylate homopolymers or copolymers of methyl methacrylate.