Cellulose acetate particle aggregate, preparation method therefor and application thereof
A cellulose acetate particle aggregate, a preparation method therefor and an application thereof, which relate to the field of harm reduction additives in cigarettes. The cellulose acetate particle aggregate includes 49-99.5 wt % of cellulose acetate particles, 0-50 wt % of a second kind of particles, and 0.5-20 wt % of a binder. The preparation method involves selecting cellulose acetate particles and a second kind of particles in a certain ratio, or cellulose acetate particles alone, preparing particle aggregates by using an air fluidized granulation method while adding a binder thereto, and sieving the particle aggregates to obtain a cellulose acetate particle aggregate having a required particle size. The cellulose acetate particle aggregate has a porous structure, an irregular shape, and a rough and uneven surface, which help to improve the efficiency of filtering out particulate matters or one or more harmful ingredients in cigarette smoke.
1. A cellulose acetate particle aggregate, comprising 49-99.5 wt % of cellulose acetate particles, 0-50 wt % of a second kind of particles and 0.5-20 wt % of a binder, wherein the cellulose acetate particles have an average particle size in a range of 5-80 μm.
2. The cellulose acetate particle aggregate of claim 1 , wherein the cellulose acetate particle aggregate comprises 60-99.5 wt % of the cellulose acetate particles, 0-35 wt % of the second kind of particles and 0.5-15 wt % of the binder.
3. The cellulose acetate particle aggregate of claim 1 , wherein the cellulose acetate particle aggregate comprises 64-89 wt % of the cellulose acetate particles, 10-35 wt % of the second kind of particles and 0.5-15 wt % of the binder.
4. The cellulose acetate particle aggregate of claim 1 , wherein the cellulose acetate particle aggregate comprises 85-99.5 wt % of the cellulose acetate particles and 0.5-15 wt % of the binder.
5. The cellulose acetate particle aggregate of claim 1 , wherein the second kind of particles are prepared from one or more of substances selected from cellulose, methylcellulose, ethylcellulose, propylcellulose, methylethylcellulose, and chitosan.
6. The cellulose acetate particle aggregate of claim 1 , wherein the cellulose acetate has an acetyl value in a range of 40-62%.
7. The cellulose acetate particle aggregate of claim 1 , wherein the binder is selected from one or more of starch, hydroxypropylmethylcellulose, hydroxyethylmethylcellulose, hydroxyethylethylcellulose, carboxymethylcellulose, methylcellulose, ethylcellulose, propylcellulose, methylethylcellulose, zein, guar gum, glycerol triacetate, triethyl citrate, triethylene glycol diacetate, alginate, gelatin, and dextrin.
8. The cellulose acetate particle aggregate of claim 1 , wherein the cellulose acetate particle aggregate has an average particle size in a range of 150-850 μm.
9. The cellulose acetate particle aggregate of claim 1 , wherein the cellulose acetate particle aggregate has a pore size in a range of 0.2-25 μm.
10. The cellulose acetate particle aggregate of claim 1 , wherein the cellulose acetate particle aggregate has a specific surface area in a range of 0.5-10 m 2 /g.
11. The cellulose acetate particle aggregate of claim 1 , wherein the cellulose acetate particle aggregate has a bulk density in a range of 0.05-0.22 g/mL.