Light selective transmission type glass and laminated substrate

1. A laminated substrate, comprising:

a solid-state imaging element provided on a silicon substrate; and a light selective transmission type glass, the light selective transmission type glass, comprising:

a glass substrate; and

a light selective transmission layer that is provided on at least one main surface of the glass substrate and selectively transmits at least one selected from the group consisting of near infrared rays, visible light rays, visible light rays of a blue wavelength region, visible light rays of a red wavelength region, and visible light rays of a green wavelength region, among near infrared rays and visible light rays,

wherein:

the glass substrate has a composition satisfying the following conditions, as expressed in terms of a molar percentage based on oxides:

a content of MgO is 3.6% to 15%, and

a content of CaO is 6.8% or less;

the glass substrate has:

an average thermal expansion coefficient α 50/100 at 50° C. to 100° C. of 2.70 ppm/° C. to 3.20 ppm/° C.;

an average thermal expansion coefficient α 200/300 at 200° C. to 300° C. of 3.45 ppm/° C. to 3.95 ppm/° C.;

a value α 200/300 /α 50/100 obtained by dividing the average thermal expansion coefficient α 200/300 at 200° C. to 300° C. by the average thermal expansion coefficient α 50/100 at 50° C. to 100° C. of 1.20 to 1.30; and

a content of an alkali metal oxide being 0% to 0.1% as expressed in terms of a molar percentage based on oxides; and

the light selective transmission layer is an absorption layer containing a transparent resin and a near ultraviolet ray absorption dye and does not include a near infrared ray absorption dye.

2. The light selective transmission type glass according to claim 1 , wherein the average thermal expansion coefficient α 200/300 at 200° C. to 300° C. of the glass substrate is 3.55 ppm/° C. to 3.85 ppm/° C.

3. The light selective transmission type glass according to claim 1 , wherein the glass substrate has a composition comprising, as expressed in terms of a molar percentage based on oxides:

SiO 2 : 50% to 75%;

Al 2 O 3 : 6% to 16%;

B 2 O 3 : 0% to 15%;

MgO: 3.6% to 15%;

CaO: 6.8% or less;

SrO: 0% to 11%; and

BaO: 0% to 9.5%.

4. The light selective transmission type glass according to claim 1 , wherein:

in the composition of the glass substrate, a total content of CaO, SrO, and BaO is 7% or more as expressed in terms of a molar percentage based on oxides and a relation of {(content of Al 2 O 3 )≥(content of MgO)}; and

the glass substrate has a devitrification viscosity of 10 3.8 dPa·sec or more.

5. The light selective transmission type glass according to claim 1 , wherein the glass substrate has an average thermal expansion coefficient α 100/200 at 100° C. to 200° C. of 3.13 ppm/° C. to 3.63 ppm/° C.

6. The light selective transmission type glass according to claim 1 , wherein the glass substrate has a content of Fe 2 O 3 being 200 ppm or less as expressed in terms of parts per million mass based on oxides.

7. The light selective transmission type glass according to claim 1 , wherein the glass substrate has a Young's modulus of 80 GPa or more.

8. The light selective transmission type glass according to claim 1 , wherein the glass substrate has a thickness of 1.0 mm or less.

9. The light selective transmission type glass according to claim 1 , wherein the glass substrate has an area of 0.03 m 2 or more.

10. The light selective transmission type glass according to claim 1 , wherein a density of defect having a size of 0.5 μm or more and 1 mm or less contained in the glass substrate is one or less per cm 2 .

11. The light selective transmission type glass according to claim 1 , wherein the glass substrate has a fictive viscosity of 10 11.0 dPa·sec to 10 14.1 dPa·sec.

12. The light selective transmission type glass according to claim 1 , wherein the glass substrate satisfies the following:

{0.0177×(content of SiO 2 )−0.0173×(content of Al 2 O 3 )+0.0377×(content of B 2 O 3 )+0.0771×(content of MgO)+0.1543×(content of CaO)+0.1808×(content of SrO)+0.2082×(content of BaO)+0.0344×(12.3+log 10 60−log 10 η)} is 2.70 to 3.20;

{0.0181×(content of SiO 2 )+0.0004×(content of Al 2 O 3 )+0.0387×(content of B 2 O 3 )+0.0913×(content of MgO)+0.1621×(content of CaO)+0.1900×(content of SrO)+0.2180×(content of BaO)+0.0391×(12.3+log 10 60−log 10 η)} is 3.13 to 3.63;

{0.0177×(content of SiO 2 )+0.0195×(content of Al 2 O 3 )+0.0323×(content of B 2 O 3 )+0.1015×(content of MgO)+0.1686×(content of CaO)+0.1990×(content of SrO)+0.2179×(content of BaO)+0.0312×(12.3+log 10 60−log 10 η)} is 3.45 to 3.95; and

{0.0111×(content of SiO 2 )+0.0250×(content of Al 2 O 3 )+0.0078×(content of B 2 O 3 )+0.0144×(content of MgO)+0.0053×(content of CaO)+0.0052×(content of SrO)+0.0013×(content of BaO)−0.0041×(12.3+log 10 60−log 10 η)} is 1.20 to 1.30,

in which:

the content of SiO 2 , the content of Al 2 O 3 , the content of B 2 O 3 , the content of MgO, the content of CaO, the content of SrO, and the content of BaO are respectively a content of each of the components contained in the resulting glass as expressed in terms of a molar percentage based on oxides; and

η is a fictive viscosity (unit: dPa·sec).

13. The light selective transmission type glass according to claim 1 , wherein the glass substrate has a weight loss value relative to a 5 mass % hydrofluoric aqueous solution at 25° C. of 0.05 (mg/cm 2 )/min or more and 0.20 (mg/cm 2 )/min or less.

14. The light selective transmission type glass according to claim 1 , wherein the glass substrate has a photoelastic constant of 31 nm/(MPa·cm) or less.

15. The light selective transmission type glass according to claim 1 , wherein a reflection layer having a dielectric multilayer film is provided on at least one main surface of the glass substrate.