Golf club grip and golf club
An object of the present invention is to provide a golf club grip having excellent grip performance under a wet condition. The present invention provides a golf club grip having an outermost surface layer, wherein the outermost surface layer contains (A) a crosslinked rubber and (B) a silica, and has, at at least a part thereof, a region where a spherical silica secondary particle with a particle size of 3 μm or more exists in an amount of at least two particles/mm 2 . If a spherical silica secondary particle with a particle size of 3 μm or more exists in a given amount at at least a part of the outermost surface layer, the golf club grip has an improved grip performance under a wet condition.
1. A golf club grip having an outermost surface layer, wherein the outermost surface layer contains (A) a crosslinked rubber and (B) a silica, and has a region where a spherical silica secondary particle with a particle size of 3 μm or more exists in an amount of at least two particles/mm 2 at least in part of the outermost surface layer,
wherein a base rubber constituting (A) the crosslinked rubber contains at least one member selected from the group consisting of a carboxyl-modified acrylonitrile-butadiene rubber, a hydrogenated acrylonitrile-butadiene rubber and a carboxyl-modified hydrogenated acrylonitrile-butadiene rubber.
2. The golf club grip according to claim 1 , wherein the outermost surface layer contains (B) the silica in an amount of 1 part by mass or more and 30 parts by mass or less with respect to 100 parts by mass of a base rubber constituting (A) the crosslinked rubber.
3. A golf club grip having an outermost surface layer, wherein the outermost surface layer contains (A) a crosslinked rubber and (B) a silica, and has a region where a spherical silica secondary particle with a particle size of 3 μm or more exists in an amount of at least two particles/mm 2 at least in part of the outermost surface layer,
wherein the outermost surface layer has tan δ ranging from 1.15 to 3.0.
4. A golf club grip having an outermost surface layer, wherein the outermost surface layer contains (A) a crosslinked rubber and (B) a silica, and has a region where a spherical silica secondary particle with a particle size of 3 μm or more exists in an amount of at least two particles/mm 2 at least in part of the outermost surface layer,
wherein the outermost surface layer is formed from a surface layer rubber composition containing (a) a base rubber, (b) spherical silica secondary particles and (c) a silane coupling agent.
5. The golf club grip according to claim 4 , wherein (b) the spherical silica secondary particles have an average sphericity of 0.90 or more.
6. The golf club grip according to claim 4 , wherein (b) the spherical silica secondary particles have a number average particle size of 1 μm or more and less than 63 μm.
7. The golf club grip according to claim 4 , wherein (b) the spherical silica secondary particles are porous and have a pore volume of more than 0.05 ml/g and 2.5 ml/g or less.
8. The golf club grip according to claim 4 , wherein the surface layer rubber composition contains (c) the silane coupling agent in an amount of 0.1 part by mass or more and 2.5 parts by mass or less with respect to 100 parts by mass of (a) the base rubber, and in an amount of 0.1 part by mass or more and 30 parts by mass or less with respect to 100 parts by mass of (b) the spherical silica secondary particles.
9. A golf club comprising a shaft, a head provided on one end of the shaft, and a grip provided on another end of the shaft, wherein the grip has an outermost surface layer containing (A) a crosslinked rubber and (B) a silica, and having a region where a spherical silica secondary particle with a particle size of 3 μm or more exists in an amount of at least two particles/mm 2 at least in part of the outermost surface layer,
wherein a base rubber constituting (A) the crosslinked rubber contains at least one member selected from the group consisting of a carboxyl-modified acrylonitrile-butadiene rubber, a hydrogenated acrylonitrile-butadiene rubber and a carboxyl-modified hydrogenated acrylonitrile-butadiene rubber.
10. The golf club according to claim 9 , wherein the outermost surface layer contains (B) the silica in an amount of 1 part by mass or more and 30 parts by mass or less with respect to 100 parts by mass of a base rubber constituting (A) the crosslinked rubber.
11. A golf club comprising a shaft, a head provided on one end of the shaft, and a grip provided on another end of the shaft,
wherein the grip has an outermost surface layer containing (A) a crosslinked rubber and (B) a silica, and having a region where a spherical silica secondary particle with a particle size of 3 μm or more exists in an amount of at least two particles/mm 2 at least in part of the outermost surface layer, and
wherein the outermost surface layer has tan δ ranging from 1.15 to 3.0.
12. A golf club comprising a shaft, a head provided on one end of the shaft, and a grip provided on another end of the shaft,
wherein the grip has an outermost surface layer containing (A) a crosslinked rubber and (B) a silica, and having a region where a spherical silica secondary particle with a particle size of 3 μm or more exists in an amount of at least two particles/mm 2 at least in part of the outermost surface layer, and
wherein the outermost surface layer is formed from a surface layer rubber composition containing (a) a base rubber, (b) spherical silica secondary particles and (c) a silane coupling agent.
13. The golf club according to claim 12 , wherein (b) the spherical silica secondary particles have an average sphericity of 0.90 or more.
14. The golf club according to claim 12 , wherein (b) the spherical silica secondary particles have a number average particle size of 1 μm or more and less than 63 μm.
15. The golf club according to claim 12 , wherein (b) the spherical silica secondary particles are porous and have a pore volume of more than 0.05 ml/g and 2.5 ml/g or less.
16. The golf club according to claim 12 , wherein the surface layer rubber composition contains (c) the silane coupling agent in an amount of 0.1 part by mass or more and 2.5 parts by mass or less with respect to 100 parts by mass of (a) the base rubber, and in an amount of 0.1 part by mass or more and 30 parts by mass or less with respect to 100 parts by mass of (b) the spherical silica secondary particles.
17. The golf club grip according to claim 4 , wherein (c) the silane coupling agent is a compound represented by the formula (1) and/or a compound represented by the formula (2):
in the formulae (1) and (2), X 1 and X 2 independently represent a methoxy group, an ethoxy group or a 2-methoxy ethoxy group, R 1 and R 2 independently represent an ethylene group or a propylene group, Y represents an amino group, a vinyl group, a methacryloxy group, an acryloxy group, a mercapto group, an isocyanate group, a ureido group, an epoxy group or a glycidoxy group, n represents 0 or 1, and m represents 2, 3 or 4.
18. The golf club according to claim 12 , wherein (c) the silane coupling agent is a compound represented by the formula (1) and/or a compound represented by the formula (2):
in the formulae (1) and (2), X 1 and X 2 independently represent a methoxy group, an ethoxy group or a 2-methoxy ethoxy group, R 1 and R 2 independently represent an ethylene group or a propylene group, Y represents an amino group, a vinyl group, a methacryloxy group, an acryloxy group, a mercapto group, an isocyanate group, a ureido group, an epoxy group or a glycidoxy group, n represents 0 or 1, and m represents 2, 3 or 4.
19. The golf club grip according to claim 3 , wherein the outermost surface layer contains (B) the silica in an amount of 1 part by mass or more and 30 parts by mass or less with respect to 100 parts by mass of a base rubber constituting (A) the crosslinked rubber.
20. The golf club according to claim 11 , wherein the outermost surface layer contains (B) the silica in an amount of 1 part by mass or more and 30 parts by mass or less with respect to 100 parts by mass of a base rubber constituting (A) the crosslinked rubber.