Method of making an insulation material and an insulated mailer
A method and system for producing an insulated mailer and an insulated box having an insulative paper fiber pad substructure with a density of less than about 10 pounds per cubic foot. The insulative paper fiber pad has entangled reinforcement fibers. A method of forming an insulative paper fiber pad using recycling-compatible or water soluble adhesive and paper layers is provided.
1. A repulpable insulation material comprising:
a batt formed of a mixture of cellulose fiber and between about 0.5% and about 25% thermoplastic binder fiber distributed substantially randomly within the cellulose fiber, said thermoplastic binder fiber being adhered to the cellulose fiber, wherein the thermoplastic binder fiber has a length of between about 0.5 mm to about 16 mm, and wherein subjecting the repulpable insulation material to a repulpability test produces greater than 85% fiber yield.
2. The repulpable insulation material according to claim 1 wherein the thermoplastic binder fiber is a meltable PE/PP bi-component thermoplastic binder fiber distributed substantially randomly.
3. The repulpable insulation material according to claim 2 wherein the thermoplastic binder fiber has about a 65/35 percent PE/PP mixture.
4. The repulpable insulation material according to claim 1 having a compression resistance of between about 0.3 psi and about 1.4 psi at thickness compressions of between about 25% and about 50%.
5. The repulpable insulation material according to claim 1 having a compression set at about 25% of between about 5% and about 18%.
6. The repulpable insulation material according to claim 1 wherein the batt is formed of a mixture of the cellulose fiber and about 10% by weight of said thermoplastic binder fiber.
7. The repulpable insulation material according to claim 1 wherein the cellulose fiber includes at least one of paper fiber and cardboard fiber.
8. The repulpable insulation material according to claim 1 wherein the cellulose fiber includes both paper fiber and cardboard fiber.
9. The repulpable insulation material according to claim 1 wherein the repulpable insulation material has a weight of between 1000 and 1600 GSM.
10. A method for producing an insulation material comprising:
mixing cellulose reinforcement fibers with about 0.5% to about 25% by weight of a meltable PE/PP bi-component thermoplastic binder fiber having a length less than about 16 mm to distribute the PE/PP bi-component thermoplastic binder fiber substantially randomly within the cellulose reinforcement fibers to form a mixture; and
applying heat to the mixture to melt the PE/PP bi-component thermoplastic binder fiber to bind the PE/PP bi-component thermoplastic binder fiber to the cellulose reinforcement fibers to from a batt, wherein subjecting the insulation material to a repulpability test produces a fiber yield of greater than 85%.
11. The method for producing an insulation material according to claim 10 further comprising coupling a first repulpable paper layer to the batt to form an insulative batt assembly.
12. The method for producing an insulation material according to claim 11 further comprising disposing a water soluble adhesive layer between the batt and the first repulpable paper layer.
13. The method for producing an insulation material according to claim 10 wherein the batt has a compression resistance of between about 0.3 psi and about 1.4 psi at compressions of between about 25% and about 50%.
14. The method for producing an insulation material according to claim 10 wherein the batt has a compression set at about 25% thickness compression of between about 5% and about 18%.
15. A repulpable insulation liner for a shipping container, the repulpable insulation liner comprising:
a first paper layer; and
a cellulose fiber pad coupled to the first paper layer, the cellulose fiber pad having cellulose reinforcement fibers interlocked with about 2% to about 25% by weight meltable PE/PP bi-component thermoplastic binder fiber distributed substantially randomly, wherein subjecting the repulpable insulation liner to a repulpability test produces greater than 85% fiber yield.
16. The repulpable insulation liner according to claim 15 wherein the meltable PE/PP bi-component thermoplastic binder fiber is a chopped fiber having a length less than about 24 mm.
17. The repulpable insulation liner according to claim 15 wherein the meltable PE/PP bi-component thermoplastic binder fiber has a length less between 0.5 to about 16 mm.
18. The repulpable insulation liner according to claim 15 further comprising one of a recycling-compatible or water soluble adhesive layer disposed between the first paper layer and the cellulose fiber pad.
19. The repulpable insulation liner according to claim 15 wherein the insulation liner has a weight of between 1000 and 1600 GSM.
20. The repulpable insulation liner according to claim 15 wherein the meltable PE/PP bi-component thermoplastic binder fiber has a plurality of different lengths.
21. The repulpable insulation liner according to claim 20 wherein the meltable PE/PP bi-component thermoplastic binder fiber has a length distribution of about 50% 1 mm length bi-component fiber and about 50% 6 mm length bi-component fiber.
22. The repulpable insulation liner according to claim 15 further comprising a second paper layer coupled to at least one of the cellulose fiber pad and the first paper layer.
23. The repulpable insulation liner according to claim 22 wherein:
the second paper layer is coupled to the first paper layer; and
the cellulose fiber pad is encapsulated between the first and second paper layers.
24. The repulpable insulation liner according to claim 1 wherein the cellulose reinforcement fibers include at least one of paper fibers and cardboard fibers.
25. The repulpable insulation liner according to claim 15 wherein the cellulose reinforcement fibers include both paper fibers and cardboard fibers.
26. The repulpable insulation liner according to claim 15 wherein the meltable PE/PP bi-component thermoplastic binder fiber makes up about 5% to about 10% by weight of the cellulose fiber pad.
27. The repulpable insulation liner according to claim 15 wherein the meltable PE/PP bi-component thermoplastic binder fiber makes up about 10% by weight of the cellulose fiber pad.
28. An insulation liner for a shipping container, the insulation liner comprising:
a first paper layer;
a second paper layer coupled to the first paper layer to form an envelope; and
a cellulose fiber batt encapsulated between the first and second paper layers with edges of the first and second paper layers being joined together on all four sides of the cellulose fiber batt, the cellulose fiber batt including cellulose fibers bound together by thermoplastic binder fibers, wherein subjecting the cellulose fiber batt to a repulpability test produces greater than 85% fiber yield.
29. The insulation liner according to claim 28 wherein the thermoplastic binder fibers makeup between about 5% and about 10% by weight of the cellulose fiber batt.
30. The insulation liner according to claim 29 wherein the thermoplastic binder fibers makeup about 10% by weight of the cellulose fiber batt.
31. The insulation liner according to claim 29 wherein the thermoplastic binder fibers are meltable PE/PP bi-component thermoplastic binder fibers.
32. The insulation liner according to claim 28 wherein the cellulose fibers include at least one of paper fibers and cardboard fibers.
33. The insulation liner according to claim 28 wherein the cellulose fibers include both paper fibers and cardboard fibers.
34. The insulation liner according to claim 28 wherein the cellulose fiber batt has a weight of between 1000 and 1600 GSM.