Method for producing bent glass article, and bent glass article
A method for producing a bent glass article includes a heat treatment step of heat-treating a bent glass. The bent glass includes a first main stir-face, a second main surface and an end face. In the heat treatment step, the bent glass is supported by a support jig with one of the main surfaces facing downward. The support jig supports at least a part of one of the main surfaces or the end face in a higher position than the lowest position of one of the main surfaces.
1. A bent glass article comprising:
a first main surface;
a second main surface;
an end face; and
a curvature part provided at least partially,
wherein a main stress difference near the end face in one of the main surfaces is 5 MPa or less.
2. The bent glass article according to claim 1 , wherein a main stress difference in the curvature part in one of the main surfaces is 5 MPa or less.
3. The bent glass article according to claim 1 , comprising a chemically strengthened glass.
4. The bent glass article according to claim 1 , which has a Young's modulus of 45 GPa or more.
5. The bent glass article according to claim 1 , which has a Young's modulus of 90 GPa or less.
6. The bent glass article according to claim 1 , wherein the curvature part has a curvature radius of 5,000 mm or less.
7. A method for producing the bent glass article of claim 1 , comprising:
heat-treating a bent glass including a first main surface, a second main surface and an end face,
while the bent glass is supported by a support jig with one of the main surfaces facing downward such that
the support jig supports at least a part of the one of the main surfaces or the end face in a higher position than the lowest position of the one of the main surfaces.
8. The method according to claim 7 , wherein the heat treatment is an annealing.
9. The method according to claim 7 , further comprising:
contacting a sheet glass with a mold to form the bent glass,
wherein in the heat treatment, the surface of the bent glass which was in contact with the mold is supported by the support jig.
10. The method according to claim 9 , wherein the heat treatment is performed after the bent glass is cooled at a cooling rate of 5° C./min or more in a region where equilibrium viscosity of the bent glass is from 10 12.5 Pa·s to 10 20 Pa·s.
11. The method according to claim 7 , wherein in the heat treatment, the bent glass is heated until equilibrium viscosity of the bent glass reaches a range of from 10 12.5 Pa·s to 10 17 Pa·s.
12. The method according to claim 7 , wherein the heat treatment comprises heating the bent glass to a predetermined temperature, and slowly cooling.
13. The method according to claim 12 , further comprising:
chamfering at least a part of the bent glass after the slowly cooling.
14. The method according to claim 13 , wherein in the chamfering, the end face of the bent glass is chamfered.
15. The method according to claim 12 , further comprising:
cutting at least a part of the bent glass after the slowly cooling.
16. The method according to claim 15 , wherein in the cutting, a peripheral part including the end face in the bent glass is cut off.
17. The bent glass article according to claim 1 , wherein the curvature part includes a twisted structure.