Foams and Films Using Specialized Lignin
This disclosure provides polymer and film derivatives of specialized clean lignin with improved properties. This disclosure also provides methods of making polymer and film derivatives of specialized clean lignin with improved properties.
1 . A polyurethane product comprising a polymerization product of an isocyanate and polyols that comprise a lignin product; wherein the polyurethane product has a higher compressive strength than polyurethane made under same conditions except without the lignin product; and wherein the lignin product is a solid residue from a pretreatment and hydrolysis of a biomass, whereby at least 80% of carbohydrates in the biomass are extracted and separated from the solid residue.
2 . A polyurethane product comprising a polymerization product of an isocyanate and polyols that comprise a lignin product, the lignin product being made by:
(a) pretreating a biomass within a pretreatment unit at an elevated temperature and pressure to produce a pretreated biomass;
(b) hydrolyzing the pretreated biomass to produce soluble carbohydrates and lignin residue; and
(c) water washing and drying the lignin residue to produce the lignin product.
3 . The polyurethane product of claim 1 or 2 , wherein the lignin product has a carbohydrate content of at most 5% by weight.
4 . The polyurethane product of any one of claims 1 - 3 , wherein the lignin product has a sulfur content of at most 0.2% by weight.
5 . The polyurethane product of any one of claims 1 - 4 , wherein the lignin product has an ash content of at most 2% by weight.
6 . The polyurethane product of any one of claims 1 - 5 , wherein about 1% to about 30% of the polyurethane product by weight is the lignin product.
7 . The polyurethane product of any one of claims 1 - 6 , wherein the lignin product is at least 15% of the polyols by weight.
8 . The polyurethane product of any one of claim 1 or 3 - 7 , wherein the pretreatment comprises:
(i) pretreating the biomass within a pretreatment unit at an elevated temperature and pressure to produce a pretreated biomass;
(ii) hydrolyzing the pretreated biomass to produce soluble carbohydrates and lignin residue; and
(iii) water washing and drying the lignin residue to produce the lignin product.
9 . The polyurethane product of any one of claims 2 - 8 , wherein the pretreating comprises mechanical processing of the biomass for particle size reduction.
10 . The polyurethane product of claim 9 , wherein the reduced particle size is about 15-25 μm on average.
11 . The polyurethane product of any one of claims 2 - 10 , wherein the pretreating comprises providing a non-pH neutral medium to the biomass in the pretreatment unit, the non-pH neutral medium comprising sulfuric acid.
12 . The polyurethane product of claim 11 , wherein the sulfuric acid has a concentration of 5% or less by biomass weight.
13 . The polyurethane product of any one of claims 2 - 12 , wherein the pretreating comprises steam explosion.
14 . The polyurethane product of any one of claims 2 - 13 , wherein the pretreatment unit comprises:
a. a barrel defining an inner chamber and comprising an inlet port near of first end of the barrel and an end flange plate at a second end of the barrel;
b. one or more rotatable screws configured to move the biomass through the inner chamber of the barrel and containing one or more sections configured to form one or more plugs from the biomass to separate the inner chamber of the barrel into two or more zones, including a feeder zone and a reaction zone; and
c. a pressure actuated discharge valve connected to the end flange plate and configured to open and close in response to pressure within the barrel, thereby allowing for continuous production of a pretreated biomass composition comprising a liquid fraction comprising monosaccharides and solid particles comprising cellulose.
15 . The polyurethane product of any one of claims 1 - 14 , wherein the lignin product has a particle size that is about 15-25 μm on average.
16 . The polyurethane product of any one of claims 1 - 15 , wherein the biomass comprises algae, corn, grass, straw, wood, bark, sawdust, paper, poplars, willows, switchgrass, alfalfa, prairie bluestem, sugar palms, nypa palm, cassava, milo, sorghum, sweet potatoes, molasses, tubers, roots, stems, sago, cassaya, tapioca, rice peas, beans, potatoes, beets, fruits, pits, sorghum, sugar cane, rice, wheat, whole grains, rye, barley, bamboo, seeds, oats, or a combination thereof, or a derivative or byproduct thereof.
17 . The polyurethane product of any one of claims 1 - 16 , wherein the biomass comprises a woody biomass.
18 . The polyurethane product of any one of claims 1 - 17 , wherein the polyurethane product is a polyurethane foam.
19 . The polyurethane product of any one of claims 1 - 18 , wherein the polyurethane product is a polyurethane plastic.
20 . A polyurethane foam comprising a polymerization product of an isocyanate and a lignin-containing solution, the lignin-containing solution formed by dissolving a powdered lignin directly in a solution comprising polyols other than lignin.
21 . The polyurethane foam of claim 20 , wherein the powdered lignin has a carbohydrate content of at most 5% by weight.
22 . The polyurethane foam of any one of claims 20 - 21 , wherein the powdered lignin has a sulfur content of at most 0.2% by weight.
23 . The polyurethane foam of any one of claims 20 - 22 , wherein the powdered lignin has an ash content of at most 2% by weight.
24 . The polyurethane foam of any one of claims 20 - 23 , wherein the powdered lignin has a particle size that is in a range of 15-25 nm on average.
25 . The polyurethane foam of any one of claims 20 - 24 , wherein the solution for the dissolution of the powdered lignin has a pH that is about: 6.5, 6.4, 6.3, 6.2, 6.1, 6, 5.9, 5.8, 5.7, 5.6, 5.5, 5.4, 5.3, 5.2, 5.1, 5, 4.9, 4.8, 4.7, 4.6, 4.5, 4.4, 4.3, 4.2, 4.1, 4, 3.9, 3.8, 3.7, 3.6, 3.5, 3.4, 3.3, 3.2, 3.1, 3, 2.9, 2.8, 2.7, 2.6, 2.5, 2.4, 2.3, 2.2, 2.1, 2, 1.9, 1.8, 1.7, 1.6, 1.5, 1.4, 1.3, 1.2, 1.1, 1, 0.9, 0.8, 0.7, 0.6, 0.5, 0.4, 0.3, 0.2, or 0.1, or in between any two of these values.
26 . The polyurethane foam of any one of claims 20 - 25 , wherein the polyurethane foam has a compressive strength higher than polyurethane foam made under same conditions except without the lignin product.
27 . A method of preparing a polyurethane product comprising: contacting an isocyanate with polyols that comprise a lignin product under conditions sufficient for a polymerization reaction to produce the polyurethane product; wherein the polyurethane product has a higher compressive strength than polyurethane made under same conditions except without the lignin product; and wherein the lignin product is a solid residue from a pretreatment and hydrolysis of a biomass, whereby at least 80% of carbohydrates in the biomass are extracted and separated from the solid residue.
28 . A method of preparing a polyurethane product comprising:
(a) pretreating a biomass within a pretreatment unit at an elevated temperature and pressure to produce a pretreated biomass;
(b) hydrolyzing the pretreated biomass to produce soluble carbohydrates and lignin residue;
(c) water washing and drying the lignin residue to produce a lignin product; and
(d) contacting an isocyanate with polyols that comprise the lignin product under conditions sufficient for a polymerization reaction to produce the polyurethane product.
29 . The method of claim 27 or 28 , wherein about 1% to about 30% of the polyurethane product by weight is the lignin product.
30 . The method of any one of claims 27 - 29 , wherein the lignin product is at least 15% of the polyols by weight.
31 . The method of any one of claim 27 or 29 - 30 , wherein the pretreatment comprises:
(i) pretreating the biomass within a pretreatment unit at an elevated temperature and pressure to produce a pretreated biomass;
(ii) hydrolyzing the pretreated biomass to produce soluble carbohydrates and lignin residue; and
(iii) water washing and drying the lignin residue to produce the lignin product.
32 . The method of any one of claims 27 - 31 , wherein the pretreating comprises mechanical processing of the biomass for particle size reduction.
33 . The method of claim 32 , wherein the reduced particle size is about 15-25 μm on average.
34 . The method of any one of claims 28 - 33 , wherein the pretreating comprises providing a non-pH neutral medium to the biomass in the pretreatment unit, the non-pH neutral medium comprising sulfuric acid.
35 . The method of claim 34 , wherein the sulfuric acid has a concentration of 5% or less by biomass weight.
36 . The method of any one of claims 28 - 35 , wherein the pretreating comprises steam explosion.
37 . The method of any one of claims 27 - 36 , wherein the pretreatment unit comprises:
a. a barrel defining an inner chamber and comprising an inlet port near of first end of the barrel and an end flange plate at a second end of the barrel;
b. one or more rotatable screws configured to move the biomass through the inner chamber of the barrel and containing one or more sections configured to form one or more plugs from the biomass to separate the inner chamber of the barrel into two or more zones, including a feeder zone and a reaction zone; and
c. a pressure actuated discharge valve connected to the end flange plate and configured to open and close in response to pressure within the barrel, thereby allowing for continuous production of a pretreated biomass composition comprising a liquid fraction comprising monosaccharides and solid particles comprising cellulose.
38 . The method of any one of claims 27 - 37 , wherein the lignin residue has a particle size that is about 15-25 μm on average.
39 . The method of any one of claims 27 - 38 , wherein the lignin product has a carbohydrate content of at most 5% by weight.
40 . The method of any one of claims 27 - 39 , wherein the lignin product has a sulfur content of at most 0.2% by weight.
41 . The method of any one of claims 27 - 40 , wherein the lignin product has an ash content of at most 2% by weight.
42 . The method of any one of claims 27 - 41 , the polyols further comprises polyether polyol, polyester polyol, or a combination thereof.
43 . The method of any one of claims 27 - 42 , wherein the isocyanate comprises aliphatic isocyanate, aromatic isocyanate, or a combination thereof.
44 . The method of any one of claims 27 - 43 , wherein the lignin product is combined with one or more other polyols prior to being contacted with the isocyanate.
45 . The method of any one of claims 27 - 44 , wherein the lignin product is liquefied before being contacted with the isocyanate.
46 . The method of any one of claims 27 - 45 , wherein the polyurethane product is a polyurethane foam.
47 . The method of any one of claims 27 - 46 , wherein the polyurethane product is a polyurethane plastic.
48 . The method of any one of claims 27 - 47 , wherein the polyurethane product has a compressive strength higher than polyurethane product made under same conditions except without the lignin product.
49 . The method of any one of claims 27 - 48 , wherein the biomass comprises algae, corn, grass, straw, wood, bark, sawdust, paper, poplars, willows, switchgrass, alfalfa, prairie bluestem, sugar palms, nypa palm, cassava, milo, sorghum, sweet potatoes, molasses, tubers, roots, stems, sago, cassaya, tapioca, rice peas, beans, potatoes, beets, fruits, pits, sorghum, sugar cane, rice, wheat, whole grains, rye, barley, bamboo, seeds, oats, or a combination thereof, or a derivative or byproduct thereof.
50 . The polyurethane product of any one of claims 27 - 49 , wherein the biomass comprises a woody biomass.
51 . The polyurethane product of any one of claims 27 - 50 , wherein the polyurethane product is a polyurethane foam.
52 . The polyurethane product of any one of claims 27 - 51 , wherein the polyurethane product is a polyurethane plastic.
53 . A polyurethane product produced according to the method of any one of claims 27 - 52 .
54 . A method of making a polyurethane foam, comprising:
(a) dissolving a powdered lignin directly in a solution comprising polyols other than lignin; and
(b) contacting the lignin-containing solution with an isocyanate and submitting the mixture for polymerization to produce the polyurethane foam.
55 . The method of claim 54 , wherein the powdered lignin has a carbohydrate content of at most 5% by weight.
56 . The method of claim 54 or 55 , wherein the powdered lignin has a sulfur content of at most 0.2% by weight.
57 . The method of any one of claims 54 - 56 , wherein the powdered lignin has an ash content of at most 2% by weight.
58 . The method of any one of claims 54 - 57 , wherein the powdered lignin has a particle size that is about 15-25 μm on average.
59 . The method of any one of claims 54 - 58 , wherein the solution for the dissolution of the powdered lignin has a pH that is about: 6.5, 6.4, 6.3, 6.2, 6.1, 6, 5.9, 5.8, 5.7, 5.6, 5.5, 5.4, 5.3, 5.2, 5.1, 5, 4.9, 4.8, 4.7, 4.6, 4.5, 4.4, 4.3, 4.2, 4.1, 4, 3.9, 3.8, 3.7, 3.6, 3.5, 3.4, 3.3, 3.2, 3.1, 3, 2.9, 2.8, 2.7, 2.6, 2.5, 2.4, 2.3, 2.2, 2.1, 2, 1.9, 1.8, 1.7, 1.6, 1.5, 1.4, 1.3, 1.2, 1.1, 1, 0.9, 0.8, 0.7, 0.6, 0.5, 0.4, 0.3, 0.2, or 0.1, or in between any two of these values.
60 . The method of any one of claims 54 - 59 , wherein the polyurethane foam has a compressive strength higher than polyurethane foam made under same conditions except without the lignin product.