System for forming floor underlayment
A process for making a fibrous panel member and a flooring structure is disclosed. The flooring structure has a subfloor, a surface layer, and an insulative pad disposed between the subfloor and the surface layer. The insulative pad has an MDI binder and reinforcement fibers distributed uniformly and randomly within a first plane. The process includes mixing a porous fiber material with a MDI adhesive. The fiber batt is compressed between a pair of porous belts. Steam and heat are applied to the compressed batt to form a bound flexible batting material.
1. A method for producing a textile fiber matt comprising:
a) providing fibers into a blowline;
b) providing an adhesive having, a content of less than about 20% by weight of the fibers into the blowline to treat the fibers;
c) pressing the fibers to form a flexible fiber matt having a predetermined compression resistance.
2. The method of claim 1 , wherein providing an adhesive having a content of less than about 20% by weight to the blowline comprises providing a polymeric adhesive into the blowline.
3. The method of claim 2 , wherein the polymeric adhesive has a polymer content of about 8% by weight or less.
4. The method of claim 2 , wherein the polymeric adhesive is of about 6% by weight or less.
5. The method of claim 2 , wherein the polymeric adhesive contains and emulsifiable adhesive.
6. The method of claim 5 , wherein the emulsifiable adhesive is emulsified.
7. The method of claim 1 , wherein the flexible fiber matt is water repellent.
8. A method for producing a textile fiber matt comprising:
a) providing fibers selected into a blowline;
b) providing binder into the blowline to form a mixture of fibers and binder; and
c) pressing the fibers in the presence of heat to form a flexible textile fiber matt to a predetermined density and mixture having less than 8% by weight binder and more than 85% by weight textile fibers.
9. The method of claim 8 , further comprising providing an adhesive binder of about 10% by weight or less into the blowline.
10. The method of claim 9 , further comprising mixing an adhesive binder in the blowline to treat the fibers to form a mixture having less than 8% by weight adhesive and more than 85% by weight fibers.