Systems and methods for making thick gauge aluminum alloy articles
Provided herein are systems and methods for producing thick gauge aluminum alloy articles such as plates, shates, slabs, sheet plates or the like. A method for producing thick gauge aluminum alloy articles can include continuously casting an aluminum alloy article and hot or warm rolling the aluminum alloy article. Also provided herein is a continuous casting system for producing thick gauge aluminum alloy articles. The disclosed thick gauge aluminum alloy articles can be provided in any suitable temper.
1. A method for producing rolled aluminum alloy articles, comprising:
providing a molten aluminum alloy;
continuously casting an aluminum alloy article from the molten aluminum alloy;
reheating the aluminum alloy article after continuously casting, wherein the reheating the aluminum alloy article comprises reheating the aluminum alloy article to a peak metal temperature from 420° C. to 580° C. and maintaining the peak metal temperature for a duration consisting of 1 minute to 5 minutes;
quenching the aluminum alloy article after continuously casting with a quenching device; and
after quenching and reheating, rolling the aluminum alloy article at a rolling temperature from 300° C. to 580° C. to a gauge of 4 millimeters (mm) or greater to produce a rolled aluminum alloy article.
2. The method of claim 1 , wherein the molten aluminum alloy comprises an AA7xxx series aluminum alloy, and wherein reheating the aluminum alloy article comprises reheating the aluminum alloy article to a peak metal temperature of at least 480° C.
3. The method of claim 1 , wherein the molten aluminum alloy comprises an AA6xxx series aluminum alloy, and wherein reheating the aluminum alloy article comprises reheating the aluminum alloy article to a peak metal temperature of at least 560° C.
4. The method of claim 1 , further comprising quenching the rolled aluminum alloy article at a rate of at least 100° C./second after rolling.
5. The method of claim 1 , further comprising cutting the rolled aluminum alloy article after rolling to produce cut and rolled aluminum alloy articles.
6. The method of claim 5 , further comprising stacking the cut and rolled aluminum alloy articles after cutting.
7. The method of claim 6 , wherein stacking the cut and rolled aluminum alloy articles after cutting is performed at a cut and rolled aluminum alloy article temperature of from 100° C. to 250° C.
8. The method of claim 7 , wherein stacking the cut and rolled aluminum alloy articles controls a temper.
9. The method of claim 7 , wherein stacking the cut and rolled aluminum alloy articles controls a temper without cold rolling.
10. The method of claim 1 , further comprising artificially aging the rolled aluminum alloy article.
11. The method of claim 1 , wherein a continuous casting exit temperature of the aluminum alloy article is from 350° C. to 500° C.
12. The method of claim 1 , wherein rolling the aluminum alloy article comprises warm rolling the aluminum alloy article at a warm rolling temperature of from 300° C. to 400° C.