Antiglare film-coated substrate, antiglare film forming liquid composition, and method of producing antiglare film-coated substrate
To provide an antiglare film-coated substrate that has an excellent antiglare property and reduced haze and through which cloudiness is not easily recognized visually on a black printed layer when the black printed layer is seen therethrough, for example, an antiglare film forming liquid composition for forming the antiglare film, and a method of producing an antiglare film-coated substrate. An antiglare film-coated substrate 1 includes a transparent substrate 2 ; and an antiglare film 3 provided on the transparent substrate 2 , in which the antiglare film 3 contains silica as its main component and a CF 3 (CH 2 ) n -group where n is an integer of 1 to 6, and the antiglare film 3 has surface roughness curve skewness Rsk of 1.3 or less and has arithmetic mean roughness Ra of 0.01 μm or more.
1. An antiglare film-coated substrate, comprising:
a transparent substrate; and
an antiglare film provided on the transparent substrate,
wherein the antiglare film comprises silica as its main component and a CF 3 (CH 2 ) n -group where n is an integer of 1 to 6,
wherein the antiglare film has surface roughness curve skewness Rsk of 1.3 or less and has arithmetic mean roughness Ra of 0.01 μm or more,
wherein the antiglare-film-coated substrate has a 60° specular gloss of from 82% to 128%,
wherein the antiglare film has a surface roughness curve element average length RSm of 10 μm to 20.2 μm, and
wherein a value obtained by dividing a measured value of a fluorine content of the antiglare film by a measured value of the fluorine of a standard sample (F content) is 0.23 to 2.5, where the standard sample is a glass containing 1.0 mass % of fluorine and having a specific gravity of 2.48.
2. The antiglare film-coated substrate according to claim 1 , wherein the antiglare film has an average film thickness of 15 to 1500 nm.
3. The antiglare film-coated substrate according to claim 2 , wherein the antiglare film has the average film thickness of 50 to 1500 nm.
4. The antiglare film-coated substrate according to claim 1 , wherein a part of the surface of the transparent substrate is exposed without the antiglare film formed thereon.
5. The antiglare film-coated substrate according to claim 1 , wherein the antiglare film has a surface roughness curve element average length RSm of 10 μm to 18 μm.
6. The antiglare film-coated substrate according to claim 1 , wherein the antiglare film has the surface roughness curve skewness Rsk of 1.05 or less.
7. The antiglare film-coated substrate according to claim 1 , wherein the antiglare film has the surface arithmetic mean roughness Ra of 0.1 μm or less.
8. The antiglare film-coated substrate according to claim 1 , wherein the CF 3 (CH 2 ) n -group is a CF 3 CH 2 CH 2 -group.
9. The antiglare film-coated substrate according to claim 1 , wherein the antiglare film has 60° specular gloss of the surface of 135% or less.
10. The antiglare film-coated substrate according to claim 1 , wherein the transparent substrate is made of a glass substrate.
11. The antiglare film-coated substrate according to claim 1 , wherein the transparent substrate is made of a chemically tempered glass substrate.
12. The antiglare film-coated substrate according to claim 1 , wherein the transparent substrate has a curved surface.
13. The antiglare film-coated substrate according to claim 1 , wherein the transparent substrate has a thickness of 0.1 to 5 mm.
14. A method of producing an antiglare film-coated substrate according to claim 1 , comprising:
applying an antiglare film forming liquid composition containing trifluoropropyltrimethoxysilane, scaly silica particles and liquid medium on a transparent substrate by a spray coating method to form an applied film, and
burning the applied film to obtain an antiglare film-coated substrate,
wherein the antiglare film comprises silica as its main component and a CF 3 (CH 2 ) n -group where n is an integer of 1 to 6, and
wherein the antiglare film has surface roughness curve skewness Rsk of 1.3 or less and has arithmetic mean roughness Ra of 0.01 μm or more.
15. The method of producing the antiglare film-coated substrate according to claim 14 , wherein the antiglare film forming liquid composition is applied on the transparent substrate by an electrostatic spray coating method.