HIGH ELONGATION PRESS HARDENED STEEL AND MANUFACTURE OF THE SAME
The residual ductility of currently available press hardened steel is approximately six percent. This characteristic of the material is primarily due to the fully martensitic microstructure in the hot stamped condition. The present alloys and processing improve the residual ductility of steels for use in press hardening applications. A series of specialized heat treatments were applied to a variety of new alloys to obtain higher residual ductility and a significant volume fraction of retained austenite in the as-hot stamped microstructure.
1 . A press hardenable steel comprising 0.1-0.5 mass % C, 1.0-10.0 mass % Mn, 0.02-2.0 mass % Si, 0.0-2.0 mass % Al, 0.0-0.045 mass % Ti, 0-4.0 mass % Mo, 0-6.0 mass % Cr, 0.0-1.0 mass % Ni, 0-0.005 mass % B, wherein said steel is intercritically annealed or substantially fully austenitized prior to forming and quenching in a hot stamping die.
2 . The press hardenable steel of claim 1 comprising 0.1-0.35 mass % C.
3 . The press hardenable steel of claim 1 comprising 1.0-6.0 mass % Mn.
4 . The press hardenable steel of claim 1 comprising 0.02-1.0 mass % Si.
5 . The press hardenable steel of claim 1 comprising 0.02-1.0 mass % Al.
6 . The press hardenable steel of claim 1 comprising no more than 0.035 mass % Ti.
7 . The press hardenable steel of claim 1 comprising 0-1.0 mass % Mo.
8 . The press hardenable steel of claim 1 comprising 0-2.0 mass % Cr.
9 . The press hardenable steel of claim 1 comprising 0.02-0.5 mass % Ni.
10 . The press hardenable steel of claim 1 , wherein the press hardenable steel has, after press hardening or hot stamping, an ultimate tensile strength of at least 1100 megapascals and a residual ductility of at least 8%.
11 . The press hardenable steel of claim 1 , wherein the press hardenable steel has, after press hardening or hot stamping, an ultimate tensile strength of at least 1200 megapascals and a residual ductility of at least 12%.
12 . The press hardenable steel of claim 1 , wherein the press hardenable steel includes an aluminum-based coating or a zinc-based coating.