Foamed polypropylene composition comprising polymeric fibers

1. A polypropylene composition (C), comprising

a) 68.0 to 77.0 wt % of a heterophasic propylene copolymer (HECO) having a melt flow rate MFR 2 (230° C., 2.16 kg) determined according to ISO 1133 in the range of 0.1 to 30 g/10 min and having a xylene soluble fraction (XCS) in the range of 28.0 to 35.0 wt %, based on the overall weight of the heterophasic propylene copolymer (HECO) comprising

i) a matrix being a propylene polymer (PP1), and

ii) an elastomeric propylene copolymer (EPR) being dispersed in said matrix, wherein the elastomeric propylene copolymer (EPR) has an ethylene content of 40.0 to 55.0 mol %,

b) 6.5 to 8.5 wt % of a crystalline propylene homopolymer (PP2) having a melt flow rate MFR 2 (230° C., 2.16 kg) determined according to ISO 1133 in the range of 100 to 800 g/10 min, and

c) 15.0 to 25.0 wt % of polymeric fibers (PF), wherein the polymeric fibers (PF) are polyethylene terephthalate fibers (PET-F) having a melting temperature Tm equal or above 210° C.,

based on the overall weight of the polypropylene composition (C),

wherein said polypropylene composition (C) is a foamable polypropylene composition.

2. The polypropylene composition (C) according to claim 1 , wherein the propylene polymer (PP1) is a propylene homopolymer (H-PP1).

3. The polypropylene composition (C) according to claim 1 , wherein the xylene soluble fraction (XCS) of the heterophasic propylene copolymer (HECO) has

i) a comonomer content in the range of 40.0 to 55.0 mol %, and

ii) an intrinsic viscosity IV determined according to DIN ISO 1628/1, October 1999 (in Decalin at 135° C.) in the range of 2.0 to 3.0 dl/g.

4. The polypropylene composition (C) according to claim 1 , wherein the polymeric fibers (PF) have

i) an average fiber length in the range of 0.1 to 20.0 mm, and

ii) an average fiber diameter in the range of 5.0 to 30.0 μm, and

iii) a density in the range of 1100 to 1400 kg/m 3 .

5. The polypropylene composition (C) according to claim 1 , wherein the polymeric fibers (PF) have

i) a tenacity in the range of 3.0 to 17 cN/dtex, and

ii) a Young Modulus determined according to ISO 5079 in the range of 3.0 to 35.0 N/tex.

6. The polypropylene composition (C) according to claim 1 , wherein said polypropylene composition (C) is free of glass fibers and carbon fibers.

7. The polypropylene composition (C) according to claim 1 , wherein the polymeric fibers (PF) are configured as an impact modifier for the heterophasic propylene copolymer (HECO).

8. A process comprising producing a foamed article comprising the polypropylene composition (C) according to claim 1 .

9. A foamed article comprising the polypropylene composition (C) according to claim 1 .

10. The foamed article according to claim 9 , wherein said foamed article comprises at least 90 wt.-% of the polypropylene composition (C).