Rubber composition and pneumatic tire using same
View Patent ↗A rubber composition contains a diene rubber including a styrene-butadiene copolymer component including a styrene-butadiene copolymer and a reinforcing filler. (1) The bonded styrene content is from 5 to 50 wt. %. (2) The total amount of styrene of an ozone decomposed component S1 including one styrene-derived unit and an ozone decomposed component S1V1 including one styrene-derived unit and one 1,2-bonded butadiene-derived unit is less than 80 wt. % of the amount of bonded styrene. The total amount of styrene of the decomposed component S1V1 is less than 10 wt. % of the amount of bonded styrene. (3) The integrated intensity of an ozone decomposed component S1V2 including one styrene-derived unit and two 1,2-bonded butadiene-derived units is less than 15% of the integrated intensity of all decomposed components including styrene-derived units. (4) The vinyl content of a butadiene portion is not less than 20% and less than 50%.
1. A rubber composition comprising a diene rubber containing at least one styrene-butadiene copolymer and a reinforcing filler, a styrene-butadiene copolymer component including the at least one styrene-butadiene copolymer having the characteristics of (1) to (4):
(1) a bonded styrene content is from 5 to 50 wt. %;
(2) when a decomposed component S1 including one styrene-derived unit and a decomposed component S1V1 including one styrene-derived unit and one 1,2-bonded butadiene-derived unit are measured by gel permeation chromatography as decomposed components obtained by ozone decomposition, a total amount of styrene of the decomposed component S1 and the decomposed component S1V1 is less than 80 wt. % of the amount of bonded styrene, and a total amount of styrene of the decomposed component S1V1 is less than 10 wt. % of the amount of bonded styrene;
(3) when the decomposed components obtained by ozone decomposition are measured by a liquid chromatography-mass spectrometer, an integrated intensity of a decomposed component S1V2 including one styrene-derived unit and two 1,2-bonded butadiene-derived units is less than 15% of an integrated intensity of all decomposed components including styrene-derived units; and
(4) a vinyl content of a butadiene portion is not less than 20% and less than 50%;
wherein the decomposed component S1 is represented by following general formula (I):
the decomposed component S1V1 is represented by at least one selected from following general formulae (II) and (III):
the decomposed component S1V2 is represented by at least one selected from following general formulae (TV) through (VI):
2. The rubber composition according to claim 1 , wherein the diene rubber further contains at least one selected from natural rubber, polyisoprene, and polybutadiene.
3. The rubber composition according to claim 1 , wherein the reinforcing filler is at least one selected from silica and carbon black.
4. A pneumatic tire using the rubber composition according to claim 1 .
5. The pneumatic tire according to claim 4 , wherein the rubber composition is used in a cap tread.
6. The rubber composition according to claim 2 , wherein the reinforcing filler is at least one selected from silica and carbon black.
7. A pneumatic tire using the rubber composition according to claim 6 .
8. The pneumatic tire according to claim 7 , wherein the rubber composition is used in a cap tread.