Adhesive composition and production method therefor
The present technology provides: a one-part moisture-curable adhesive composition including: a preliminary composition obtained by mixing a urethane prepolymer, an aliphatic isocyanate A, and an aminosilane compound B, and a dimethyl tin catalyst represented by Formula (1) below; and a production method thereof. In Formula (1), X 1 and X 2 each independently represent a divalent heteroatom, and R 1 and R 2 each independently represent a hydrocarbon group that may have a heteroatom.
1. A one-part moisture-curable adhesive composition comprising:
a preliminary composition obtained by mixing a urethane prepolymer, an aliphatic isocyanate A, and an aminosilane compound B; and
a dimethyl tin catalyst represented by Formula (1):
where, X 1 and X 2 each independently represent a divalent heteroatom, and R 1 and R 2 each independently represent a hydrocarbon group that may have a heteroatom.
2. The adhesive composition according to claim 1 , wherein the divalent heteroatom is at least one type selected from the group consisting of an oxygen atom and a sulfur atom.
3. The adhesive composition according to claim 1 , wherein the X 1 moiety and the X 2 moiety are sulfur atoms, and the R 1 moiety and the R 2 moiety are unsubstituted or ester bond-containing alkyl groups.
4. The adhesive composition according to claim 1 , wherein the X 1 moiety and the X 2 moiety are oxygen atoms, and the R 1 moiety and the R 2 moiety are carbonyl group-containing alkyl groups.
5. The adhesive composition according to claim 1 , wherein a content of the dimethyl tin catalyst is from 0.001 to 0.3 parts by mass per 100 parts by mass of the urethane prepolymer.
6. The adhesive composition according to claim 1 , wherein the aliphatic isocyanate A is at least one type of hexamethylene diisocyanate-modified product selected from the group consisting of reaction products of hexamethylene diisocyanate and a polyol having tri- or higher functionality, allophanates of hexamethylene diisocyanate, isocyanurates of hexamethylene diisocyanate, and biurets of hexamethylene diisocyanate.
7. The adhesive composition according to claim 1 , wherein the aminosilane compound B contains an imino group, and the imino group bonds to at least one aromatic hydrocarbon group.
8. The adhesive composition according to claim 1 , further comprising a tertiary amine.
9. The adhesive composition according to claim 1 , wherein the preliminary composition further contains a filler.
10. The adhesive composition according to claim 1 , wherein the preliminary composition further contains a plasticizer.
11. A method of producing an adhesive composition, the method comprising:
a mixing step 1 of mixing the urethane prepolymer, the aliphatic isocyanate A, and the aminosilane compound B to obtain a preliminary composition; and
a mixing step 2 of mixing the preliminary composition and the dimethyl tin catalyst to produce the adhesive composition described in claim 1 .
12. The method of producing the adhesive composition according to claim 11 , wherein, in the mixing step 1, at least one type selected from the group consisting of fillers and plasticizers is further mixed.
13. The method of producing the adhesive composition according to claim 11 , wherein, in the mixing step 2, a tertiary amine is further mixed.