Polypropylene composition with improved hot-tack force

1. A polypropylene composition comprising:

a) 55.0 to 90.0 wt % of a crystalline propylene random copolymer (C-PP) comprising propylene monomers and 1.0 to 6.5 wt % of at least one comonomer selected from ethylene and a C 4 -C 12 alpha olefin, having a melting temperature in the range of 135 to 155° C. as measured according to ISO 11357-3 and a melt flow rate (MFR 2 ) in the range of 0.1 to 15 g/10 min as measured according to ISO 1133 at a temperature of 230° C. and under a load of 2.16 kg; and

b) 10.0 to 45.0 wt % of an amorphous propylene copolymer (AM-PP) comprising propylene monomers and 30.0 to 50.0 wt % of at least one comonomer selected from ethylene and a C 4 -C 12 alpha olefin and having a glass transition temperature Tg(b) in the range of −60 to −40° C., the wt % of the C-PP and AM-PP copolymers being relative to the total weight of the C-PP and AM-PP copolymers,

said polypropylene composition having a melt flow rate (MFR 2 ) in the range of 0.3 to 90 g/10 min as measured according to ISO 1133 at a temperature of 230° C. and under a load of 2.16 kg and also having a relative content of isolated to block comonomer sequences I(E) in the range of 20 to 50%, which is calculated according to the equation:

I ( E )= fPEP /(( fEEE+fPEE+fPEP ))×100  (1)

wherein:

I(E) is the relative content of isolated to block comonomer sequences [in %];

fPEP is the mol fraction of propylene/comonomer/propylene sequences (PEP) in the sample;

fPEE is the mol fraction of propylene/comonomer/comonomer sequences (PEE) and of comonomer/comonomer/propylene sequences (EEP) in the sample;

fEEE is the mol fraction of comonomer/comonomer/comonomer sequences (EEE) in the sample; and

all sequence concentrations being based on a statistical triad analysis of 13 C-NMR data.

2. The polypropylene composition according to claim 1 wherein at least 50 wt % of the comonomers in the crystalline propylene random copolymer (C-PP) and in the amorphous propylene copolymer (AM-PP) are ethylene comonomers, and wherein the comonomers are only ethylene and butylene.

3. The polypropylene composition according to claim 1 having a matrix (M) of the crystalline propylene random copolymer (C-PP) and dispersed therein an amorphous phase of the amorphous propylene copolymer (AM-PP).

4. The polypropylene composition according to claim 1 having a xylene cold soluble (XCS) content, determined according ISO 16152 at 25° C., in the range of 15.0 to 50.0 wt %, wherein the XCS fraction has a comonomer content between 25 and 50 wt %, the XCS fraction further has an intrinsic viscosity between 1.2 and 4 dl/g, and wherein the XCS fraction further has a I(E) between 15 and 45%.

5. The polypropylene composition according to claim 1 having a total comonomer content in the range of 7.0 to 25.0 wt %, the total comonomer content being calculated based on the total amount of monomers comprised in the crystalline propylene random copolymer (C-PP) and the amorphous propylene copolymer (AM-PP) comprised in the polypropylene composition.

6. The polypropylene composition according to claim 1 wherein the polypropylene composition has at least two glass transition temperatures:

a) a glass transition temperature Tg(a) in the range of −10.0 to 1.0° C., and

b) a glass transition temperature Tg(b) in the range of −60 to −40° C.,

wherein Tg(a) relates to the crystalline propylene random copolymer (C-PP) and Tg(b) relates to the amorphous propylene copolymer (AM-PP).

7. The polypropylene composition according to claim 1 having:

a) Vicat-A temperature of more than 80° C., as measured according to ISO 306, and

b) storage modulus (G′23) in the range of 150 to 450 MPa as measured at 23° C. according to ISO 6721-07.

8. The polypropylene composition according to claim 1 having a tensile modulus (E) in the range of 300 to 700 MPa, as measured at 23° C. according to ISO 527 on injection molded specimens.

9. The polypropylene composition according to claim 1 having a Flexibility of more than 0.8 which is calculated according to the equation:

Flexibility= EAY* 100000/( TSY*E )

wherein:

EAY is the elongation at yield value,

TSY is the tensile strength at yield value, in MPa,

E is the tensile modulus value, in MPa, and

EAY, TSY, and E are determined at 23° C. according to ISO 527.

10. The polypropylene composition according to claim 1 having a hot tack force in the range of 1.8 to 6.0 N.

11. A process for the manufacture of the polypropylene composition according to claim 1 comprising the steps of:

a) in a pre-polymerisation reactor propylene is pre-polymerised in the presence of a Ziegler-Natta catalyst, a co-catalyst and an external donor, obtaining a reaction mixture (RM-1) comprising a polypropylene (Pre-PP),

b) transferring the reaction mixture (RM-1) to a loop reactor,

c) in the loop reactor propylene and at least one comonomer selected from ethylene and a C 4 -C 12 alpha-olefin are polymerised in the presence of the reaction mixture (RM-1), obtaining a reaction mixture (RM-2),

d) transferring the reaction mixture (RM-2) to a gas-phase reactor-1,

e) in the gas-phase reactor-1 propylene and at least one comonomer selected from ethylene and a C 4 -C 12 alpha olefin are polymerised, obtaining a reaction mixture (RM-3) comprising the crystalline propylene random copolymer (C-PP),

f) transferring the reaction mixture (RM-3) to a gas-phase reactor-2,

g) in the gas-phase reactor-2 propylene and at least one comonomer selected from ethylene and a C 4 -C 12 alpha olefin are polymerised, obtaining a reaction mixture (RM-4) comprising the crystalline propylene random copolymer (C-PP) and the amorphous propylene copolymer (AM-PP), and

h) recovering the polypropylene composition.

12. A process according to claim 11 having:

a) a Ziegler Natta based catalyst comprising a group 2 metal and a group 6 metal containing catalyst which comprises an internal electron donor, triethylaluminium (TEAL) as co-catalyst and di-cyclopentyldimethoxy silane as external donor (donor D),

b) a hydrogen/propylene (H 2 /C 3 ) ratio in the loop reactor in the range of 0.1 to 0.4 mol/kmol,

c) a hydrogen/propylene (H 2 /C 3 ) ratio in the gas-phase reactor-1 in the range of 2.5 to 27.0 mol/kmol,

d) a hydrogen/propylene (H 2 /C 3 ) ratio in the gas-phase reactor-2 in the range of 60 to 270 mol/kmol,

e) an ethylene/propylene (C 2 /C 3 ) ratio in the loop reactor in the range of 0.0 to 25 mol/kmol,

f) an ethylene/propylene (C 2 /C 3 ) ratio in the gas-phase reactor-1 in the range of 25.0 to 50.0 mol/kmol, and

g) an ethylene/propylene (C 2 /C 3 ) ratio in the gas-phase reactor-2 in the range of 500 to 600 mol/kmol.

13. The polypropylene composition according to claim 1 further comprising at least one of: a polymer other than the crystalline propylene random copolymer (C-PP) and the amorphous propylene copolymer (AM-PP), a tackifying resin, a plasticizer, an additive or a filler, wherein the other polymer is chosen from the group consisting of high pressure polyethylene and co-polymers thereof, ethylene vinyl acetate (EVA) and ethylene acrylate co-polymers, low pressure polyethylene, styrene butadiene copolymer (SBC), styrene ethylene/butylene styrene (SEBS), polyolefin based plastomer (POP) and elastomers (POE), amorphous poly alpha olefin (APAO) and wax.

14. The polypropylene composition according to claim 13 comprising one or more of:

a) at least 10.0 wt % of the polypropylene composition according to claim 1 ,

b) a polymer other than the crystalline propylene random copolymer (C-PP) and the amorphous propylene copolymer (AM-PP) in the range of 0.0 to 50.0 wt %,

c) a tackifying resin in a range of 0.0 to 70.0 wt %,

d) a plasticizer in a range of 0.0 to 60.0 wt %,

e) an additive in a range of 0.1 to 4.0 wt %,

or

f) a filler in a range of 0.0 to 50.0 wt %,

said weight percentages being calculated based on the total amount of the polypropylene composition components (a) to (f).

15. An article comprising the polypropylene composition according to claim 1 .

16. The article according to claim 15 , wherein the hot-tack film comprises at least one surface layer, the at least one surface layer comprising the polypropylene composition, the polypropylene composition exhibiting a hot tack force of at least 1.8 N.

17. The article according to claim 16 wherein the hot-tack film is a multilayer film having an overall thickness in the range of 30 to 500 μm, wherein the at least one surface layer has a thickness in the range of 3 to 50 μm, and wherein said multilayer film exhibits a hot tack force in the range of 1.8 to 6.0 N.

18. The article according to claim 15 , wherein the article comprises an adhesive composition, and wherein the adhesive composition comprises one or more of:

a) at least 10.0 wt % of the polypropylene composition,

b) a polymer other than the crystalline propylene random copolymer (C-PP) and the amorphous propylene copolymer (AM-PP) in the range of 3.0 to 40.0 wt %,

c) a tackifying resin in a range of 10.0 to 60.0 wt %,

d) a plasticizer in a range of 3.0 to 55.0 wt %,

e) an additive in a range of 0.15 to 3.0 wt %,

or

f) a filler in a range of 0.5 to 40.0 wt %,

said percentages being calculated based on the total amount of polypropylene composition components (a) to (f).

19. The article according to claim 15 , wherein the article comprises a hot-tack film, and wherein the hot-tack film comprises:

a) at least 90 wt % of a polypropylene composition consisting of crystalline propylene random copolymer (C-PP) and of amorphous propylene copolymer (AM-PP),

and

b) at least 0.1 wt % of additives, the additives comprising one or more of: antioxidants, slip agents, antiblocking agents or nucleating agents,

said percentages being calculated based on the total amount of polypropylene composition components including components (a) to (b).

20. The article according to claim 16 , further comprising at least one substrate.