Process for efficient cross-linking of hyaluronic acid
A process for manufacturing a cross-linked hyaluronic acid (HA) gel product is comprising the steps of: (a) preparing an aqueous mixture of HA and a cross-linking agent selected from multiepoxides and diepoxides; wherein the HA is dissolved in an aqueous solution containing 1-10% (w/w) inorganic hydroxide; and wherein the dissolved HA constitutes more than 10% (w/w) of the final mixture; and (b) subjecting the aqueous mixture to cross-linking conditions to allow the dissolved HA to react with the cross-linking agent so as to obtain a cross-linked HA gel product.
1. A process for manufacturing a cross-linked hyaluronic acid (HA) gel product, the process comprising:
(a) obtaining an aqueous mixture of HA and a diepoxide cross-linking agent selected from the group consisting of 1,4-butanediol diglycidyl ether (BDDE), 1,2-ethanediol diglycidyl ether (EDDE) and diepoxyoctane, wherein the HA is dissolved in an aqueous solution comprising 6-8% (w/w) inorganic hydroxide, and wherein the dissolved HA constitutes 33-35% (w/w) of the aqueous mixture; and
(b) cross-linking the aqueous mixture at 10-75° C. to obtain the cross-linked HA gel product, wherein the HA is cross-linked in a single step.
2. The process according to claim 1 , wherein the aqueous solution of (a) comprises 6% (w/w) inorganic hydroxide.
3. The process according to claim 1 , wherein the aqueous solution of (a) comprises 8% (w/w) inorganic hydroxide.
4. The process according to claim 1 , wherein the aqueous mixture of (a) comprises 33% (w/w) HA.
5. The process according to claim 1 , wherein the aqueous mixture of (a) comprises 35% (w/w) HA.
6. The process according to claim 1 , wherein the cross-linking occurs at room temperature.
7. The process according to claim 1 , wherein the cross-linking is performed for 4-36 h.
8. The process according to claim 1 , wherein the cross-linking agent is 1,4-butanediol diglycidyl ether (BDDE).
9. The process according to claim 1 , further comprising (c) isolating the cross-linked HA product.
10. The process according to claim 9 , wherein the isolating comprises precipitating the HA gel product.
11. The process according to claim 1 , wherein the cross-linking is performed at 15-35° C. for 2-40 h so as to obtain the cross-linked HA gel product.
12. The process according to claim 1 , wherein the cross-linking is performed at 15-35° C.
13. The process according to claim 1 , wherein the cross-linked HA gel product exhibits an elastic modulus of at least 450 Pa.