Alcohol-resistant, chemically-strippable floor coating and composition for making same
A chemically-strippable, alcohol-resistant floor coating contains a crosslinked polymer, an alkali soluble resin, and an amine functional compound. The coating exhibits a Strippability Level of at least 40% after 300 cycles in a solvent on an abrasion machine, and an Ethanol Resistance of at least 60 percent, as measured by a 60° Gloss Retention Test. A floor coating composition comprising an aqueous dispersion of a crosslinkable polymer, an alkali soluble resin, an amine functional compound, and a crosslinker can be applied to a floor to make the coating.
1. A coated floor comprising:
(A) a flooring substrate, and
(B) a chemically-strippable, alcohol-resistant coating on the flooring substrate, the coating comprising:
(i) at least one crosslinked polymer selected from the group consisting of crosslinked polyurethane, crosslinked acrylic polymer, and crosslinked polyurea;
(ii) alkali soluble resin; and
(iii) an amine functional compound;
wherein the coating exhibits:
(a) a Strippability Level of at least 40% as measured by percent coating stripped from a tile after 300 cycles using a Modified ASTM D1792-82 Strippability Test Procedure with a stripping solution consisting of 4 wt % monoethanolamine, 1 wt % diethyleneglycol butylether, 0.1% ethylenediamine tetracetic acid, 0.25 wt % C 9-11 alcohol ethoxylate, 2.6 wt % benzyl alcohol, and 92.05 wt % water, and
(b) an Ethanol Resistance (R Et ) of at least 60 percent, as measured by a 60° Gloss Retention Test re upon exposure to 0.33 milliliter/in2 of a blend of 67.5 wt % ethanol and 32.5 wt % water for a period of 60 minutes at 72° F. and relative humidity of 50%, wherein:
R E1 =%60° Gloss Retention E1 =100%−[(60° GU@ T o −60° GU@ T E1 )/60° GU@ T o ]×100%.
2. The coated floor according to claim 1 , wherein the crosslinked polymer is present in the coating in an amount of from 30 to 98 wt % based on coating weight, the alkali soluble resin is present in the coating in an amount of from 1 to 15 wt %, based on coating weight, and the amine functional compound is present in the coating in an amount of from 0.1 to 10 wt %, based on coating weight.
3. The coated floor according to claim 1 , wherein the crosslinked polymer is formed by crosslinking an polyurethane with a carbodiimide, and the crosslinked polymer is present in an amount of from 60 to 95 wt % based on coating weight, the alkali soluble resin is present in the coating in an amount of from 2 wt % to 10 wt %, based on coating weight, and the amine functional compound is present in the coating in an amount of from 1 to 5 wt %, based on coating weight, or wherein the crosslinked polymer is formed by crosslinking a polyol with polysocyanate, and the crosslinked poymer is present in an amount of from 60 wt % to 95 wt % based on coating weight, the alkali soluble resin is present in the coating in an amount of from 4 wt % to 12 wt %, based on coating weight, and the amine functional compound is present in the coating in an amount of from 1 to 8 wt %, based on coating weight.
4. The coated floor according to claim 1 , wherein the coating comprises a wax in an amount of from 5 wt % to 15 wt %, based on coating weight.
5. The coated floor according to claim 1 , wherein the alkali soluble resin has a weight average molecular weight of from 500 to 10,000.
6. The coated floor according to claim 1 , wherein the alkali soluble resin comprises at least one member selected from the group consisting of acrylic-acrylic acid resin, styrene-acrylic acid resin, styrene-α-methyl styrene-acrylic acid resin, styrene-acrylic-acrylic acid resin, styrene-α-methyl styrene-acrylic-acrylic acid resin, acrylic-methacrylic acid resin, styrene-methacrylic acid resin, styrene-methyl styrene-methacrylic acid resin, styrene-acrylic-methacrylic acid resin, styrene-α-methyl styrene-acrylic-methacrylic acid resin, styrene-maleic anhydride resin, and polycarboxypolyamide resin.
7. The coated floor according to claim 1 , wherein the alkali soluble resin has an acid number of at least 100.
8. The coated floor according to claim 1 , wherein the amine functional compound comprises at least one member selected from the group consisting of amine-containing polyester, amine-containing polyacrylate, amine-containing polycarbonate, amine-containing polyurea, amine-containing polybutadiene, amine-containing polyether, amine-containing polyamide, and amine-containing polysiloxane.
9. The coated floor according to claim 1 , wherein the amine functional compound comprises 3-aminopropyl terminated polydimethylsiloxane.
10. The coated floor according to claim 1 , wherein the crosslinked polymer comprises at least one member selected from the group consisting of crosslinked urethane-acrylic polymer, a crosslinked reaction product of a diol with an aliphatic diisocyanate, and a crosslinked reaction product of a diol with an aromatic diisocyanate.
11. The coated floor according to claim 1 , wherein the crosslinked polymer comprises a crosslinked polyurethane comprising a reaction product of a diisocyanate with a dial, wherein the diisocyanate comprises at least one member selected from the group consisting of isophorone diisocyanate, hexamethylene diisocyanate, toluene diisocyanate, and diphenylmethane diisocyanate, and the dial comprises at least one member selected from the group consisting of a dial-containing a polyester, a dial-containing a polyacrylate, a dial-containing polycarbonate, a dial-containing a polyurea, a dial-containing a polybutadiene, a dial-containing a polyether, and a dial-containing a polyamide, and a dial containing polyurethane.
12. A floor coating composition for making a chemically-strippable, ethanol-resistant floor coating, the composition comprising:
(A) an aqueous dispersion of at least one crosslinkable polymer selected from the group consisting of crosslinkable polyurethane, crosslinkable acrylic polymer, and crosslinkable polyurea; and
(B) alkali soluble resin;
(C) an amine functional compound
(D) a crosslinker for the crosslinkable polymer; and
wherein the floor coating composition, when applied to a flooring substrate as four 0.1 mil thick coats, exhibits:
(i) a Strippability Level of at least 40% as measured by percent coating stripped from a tile after 300 cycles using a Modified ASTM D1792-82 Strippability Test Procedure with a stripping solution consisting of 4 wt % monoethanolamine, 1 wt % diethyleneglycol butylether, 0.1% ethylenediamine tetracetic acid, 0.25 wt % Cg-11 alcohol ethoxylate, 2.6 wt % benzyl alcohol, and 92.05 wt % water, and
(ii) an Ethanol Resistance of at least 60 percent, as measured by a 60° Gloss Retention Test re upon exposure to 0.33 milliliter/in2 of a blend of 67.5 wt % ethanol and 32.5 wt % water for a period of 60 minutes at 72° F. and relative humidity of 50%, wherein:
R E1 =%60° Gloss Retention E1 =100%−[(60° GU@T o −60° GU@ T E1 )/60° GU@ T o ]×100%.
13. The floor coating composition according to claim 12 , wherein the alkali soluble resin comprises at least one member selected from the group consisting of acrylic-acrylic acid resin, styrene-acrylic acid resin, styrene-α-methyl styrene-acrylic acid resin, styrene-acrylic-acrylic acid resin, styrene-α-methyl styrene-acrylic-acrylic acid resin, acrylic-methacrylic acid resin, styrene-methacrylic acid resin, styrene-methyl styrene-methacrylic acid resin, styrene-acrylic-methacrylic acid resin, styrene-α-methyl styrene-acrylic-methacrylic acid resin, styrene-maleic anhydride resin, and polycarboxypolyamide resin.
14. The floor coating composition according to claim 12 , wherein the amine functional compound comprises at least one member selected from the group consisting of amine-containing polyester, amine-containing polyacrylate, amine-containing polycarbonate, amine-containing polyurea, amine-containing polybutadiene, amine-containing polyether, amine-containing polyamide, and amine-containing polysiloxane.
15. The floor coating composition according to claim 12 , wherein the coating composition comprises a wax in an amount of from 5 wt % to 15 wt %, based on coating weight.
16. The floor coating composition according to claim 12 , further comprising a coalescing agent comprising at least one member selected from the group consisting of an organic solvent and a plasticizer.
17. The floor coating composition according to claim 16 , wherein the organic solvent comprises at least one member selected from the group consisting of ethylene glycol, propylene glycol, ethylene glycol ether, pyrrolidone, and the plasticizer comprises at least one member selected from the group consisting of phosphate ester solvent, dibenzoate solvent, monobenzoate solvent, and phthalate solvent.
18. The floor coating composition according to claim 16 , wherein the coalescing agent is present in the coating composition in an amount of from 2 wt % to 15 wt %, based on coating composition weight.
19. The floor coating composition according to claim 12 , wherein, based on the weight of the coating composition:
(i) the crosslinkable polymer is present in an amount of from 1 wt % to 50 wt %,
(ii) the crosslinker is present in an amount of from 1 wt % to 10 wt %,
(iii) the alkali soluble resin is present in an amount of from 0.1 wt % to 3 wt %, and
(iv) the amine functional compound is present in an amount of from 0.02 wt % to 1.6 wt %.
20. The floor coating composition according to claim 19 , wherein the aqueous dispersion comprises a crosslinkable polyurethane, the alkali soluble resin has a weight average molecular weight of from 500 to 10,000 and an acid number of at least 100.