WATER-SOLUBLE FILM, CHEMICAL AGENT PACKAGE AND WATER-SOLUBLE FILM PRODUCTION METHOD
A water-soluble film comprises a polyvinyl alcohol resin (A), wherein a difference (ΔR) between a phase retardation (Rα) of one of opposite surfaces (α surface) of the water-soluble film and a phase retardation (Rβ) of the other surface (β surface) of the water-soluble film is not greater than 8 nm as measured on a middle portion of the water-soluble film with respect to a transverse direction (TD) of the water-soluble film. Therefore, the water-soluble film has a reduced difference in crystallinity between the front and back surfaces thereof and, hence, is less liable to be curled to thereby ensure a higher productivity.
1 . A water-soluble film comprising a polyvinyl alcohol resin (A), wherein a difference ΔR between a phase retardation Rα of an α surface of the water-soluble film and a phase retardation Rβ of a β surface of the water-soluble film opposite from the α surface is not greater than 8 nm as measured on a middle portion of the water-soluble film with respect to a transverse direction TD of the water-soluble film.
2 . The water-soluble film according to claim 1 , further comprising a plasticizer (B).
3 . The water-soluble film according to claim 2 , wherein the plasticizer (B) is present in a proportion of at least 20 parts by weight based on 100 parts by weight of the polyvinyl alcohol resin (A).
4 . The water-soluble film according to claim 1 , wherein the polyvinyl alcohol resin (A) includes an anionic group-modified polyvinyl alcohol resin.
5 . The water-soluble film according to claim 1 , which has a water content of 3 to 15 wt. % as a whole.
6 . The water-soluble film according to claim 1 , which is usable for a chemical agent package.
7 . A chemical agent package comprising:
a package bag formed from the water-soluble film according to claim 1 ; and
a liquid detergent packaged in the package bag.
8 . The chemical agent package according to claim 7 ,
wherein the liquid detergent has a pH of 6 to 12 when being dissolved or dispersed in water, and
wherein the liquid detergent has a water content of not higher than 15 wt. %.
9 . A water-soluble film production method for producing the water-soluble film according to claim 1 , the method comprising the steps of:
forming a film from a film forming material containing a polyvinyl alcohol resin (A), and drying the film; and
heat-treating the film at 90° C. to 135° C.