Transport vehicle glazing with water repellent and anti-dust coating associated with a detection device

1. A transport vehicle glazing comprising a first side to face an interior of a transport vehicle and a second side to face an exterior atmosphere, the second side being opposite the first side, at least one zone of the second side not wiped by windscreen wipers and facing the exterior atmosphere, and said at least one zone being located to face a detecting device placed in the interior of the transport vehicle,

wherein the transport vehicle glazing comprises a substrate and a mineral oxide layer provided on the substrate,

the mineral oxide layer being of 0.1 to 20 μm thickness, wherein 30% to 90% of the volume of the mineral oxide layer consists of 20 to 300 nm open pores that are distributed uniformly throughout the thickness of the mineral oxide layer, and a majority of the open pores are connected to one another, an internal surface and an external surface of the mineral oxide layer being functionalized with a compound containing a perfluoroalkyl or alkyl functional group, saturated with a hydrophobic oil that impregnates the functionalized porous layer and forms a film on the surface thereof, and

wherein the mineral oxide layer is made of silica and formed at least in the zone of the second side not wiped by windscreen wipers and facing the exterior atmosphere.

2. The glazing as claimed in claim 1 , wherein 40% to 90% of the volume of the mineral oxide layer consists of open pores.

3. The glazing as claimed in claim 2 , wherein from 50% to 90% of the volume of the mineral oxide layer consists of open pores.

4. The glazing as claimed in claim 1 , wherein 30% to 80% of the volume of the layer consists of open pores.

5. The glazing as claimed in claim 1 , wherein the open pores are from 30 nm to 300 nm in size.

6. The glazing as claimed in claim 5 , wherein the open pores are from 50 nm to 300 nm in size.

7. The glazing as claimed in claim 1 , wherein the open pores are from 20 nm to 200 nm in size.

8. The glazing as claimed in claim 1 , wherein the hydrophobic oil comprises at least one compound selected from the group consisting perfluorinated hydrocarbons or organic silicones; perfluoropolyethers, perfluoroalkylethers and perfluorocycloethers; tertiary perfluoroalkylamines; perfluoroalkylsulfides and perfluoroalkylsulfoxides; perfluoroalkylphosphines and oxidation products thereof; perfluorinated carboxylic acids; fluorinated phosphonic and sulfonic acids; fluorinated silanes; and any combinations thereof.

9. The glazing as claimed in claim 1 , wherein the detecting device is an anti-collision/obstacle-detecting/security video camera.

10. The glazing as claimed in claim 1 , wherein the detecting device is placed on the first side of the glazing.

11. A process for manufacturing a transport vehicle glazing that comprises a first side to face an interior of a transport vehicle and a second side to face an exterior atmosphere, the second side being opposite the first side, the process comprising in succession:

depositing on a substrate a liquid pore-forming agent composition and one or more mineral oxide precursors;

calcinating the obtained assembly of the substrate coated with the liquid pore-forming agent composition and the one or more mineral oxide precursors to remove the pore-forming agent and form a condensed porous mineral oxide layer of 0.1 to 20 μm thickness on the substrate, wherein 30 to 90% of the volume of the mineral oxide layer consists of 20 to 300 nm open pores that are distributed uniformly throughout the thickness of the mineral oxide layer, and a majority of the open pores are connected to one another;

grafting onto an external surface and an internal surface of the porous mineral oxide layer said compound containing a perfluoroalkyl or alkyl functional group to functionalize the internal and the external surfaces of the porous mineral oxide layer, then

pouring an excess of hydrophobic oil onto the functionalized mineral oxide layer of the substrate, the hydrophobic oil impregnating the functionalized mineral oxide layer and forming a film on the surface thereof, the substrate being held inclined in order to remove excess oil from the substrate,

wherein the mineral oxide layer is made of silica and formed at least in a zone of the second side not wiped by windscreen wipers and facing the exterior atmosphere, and said at least one zone being located to face a detecting device placed in the interior of the transport vehicle.

12. The process as claimed in claim 11 , wherein the mineral oxide is formed from silica precursors comprising glycidoxypropyltrimethoxysilane and tetraethoxysilane.

13. The process as claimed in claim 11 , wherein the pore-forming agent is selected from the group consisting of a latex of acrylic particles and a meth(acrylic) polymer emulsion.

14. The process as claimed in claim 13 , wherein the pore-forming agent is formed from a latex of particles of polymethyl methacrylate.

15. The process as claimed in claim 11 , wherein the liquid pore-forming agent composition and the one or more mineral oxide precursors are deposited on the substrate by roller, spraying, dip-coating, screen printing with adjustment of the rheology or inkjet printing.

16. The process as claimed in claim 11 , wherein the compound containing a perfluoroalyl functional group has the formula:

in which

m=0 to 15;

n=1 to 5;

p=0, 1 or 2;

R is an alkyl group or a hydrogen atom; and

X represents a hydrolysable group;

or consists of a perfluoropolyethersilane represented by the formula (II)

or by the formula

in which:

m=2 to 30;

n=1 to 3;

p=0, 1 or 2;

R is an alkyl group or a hydrogen atom; and

X is a hydrolysable group;

or consists of a perfluoropolyether bearing an alkoxysilane group at two ends having the following formula

R 1 OSiR 2 R 3 R 4 [(CF 2 ) n O]R 5 R 6 R 7 SiOR 8

wherein R 1 O and OR 8 are alkoxy groups,

R 2-7 are alkyl groups optionally comprising one or more heteroatoms,

n and m being integers of 1 or more.

17. The process as claimed in claim 16 , wherein, in formula I, m=5 to 11.

18. The process as claimed in claim 11 , wherein, before the compound containing a perfluoroalkyl or alkyl functional group is grafted, the internal and external surfaces of the porous mineral oxide layer are hydrophilic, and wherein a graft precursor containing a perfluoroalkyl or alkyl functional group is hydrolyzed to condense with the surface of the porous mineral oxide layer to obtain the graft.